A kind of melt spinning device and process

A melt spinning and process technology, applied in the field of spinning, can solve problems such as disadvantages, and achieve the effects of easy operation, high spinning efficiency and simple equipment structure

Active Publication Date: 2020-06-19
QINGDAO ST MEER FIBER TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after the magnetic material is mixed into the slurry, the magnetic material in the stirred and mixed slurry shows anisotropic characteristics, which is not conducive to the use in some occasions that require magnetic materials to show obvious orientation.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of melt spinning device and process
  • A kind of melt spinning device and process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A melt-spinning process is a melt-spinning process, and the melt is obtained as follows:

[0048] Step 1, at 50°C, a-Al 2 o 3 The nanoparticles are placed in the aluminum sulfate solution with a concentration of 0.5mol / L to obtain a dispersion, and the pH of the solution is adjusted to 6~7; add magnetic material particles (Fe particles, average particle size 2 microns) to the dispersion, and after the addition is completed, Add ammonium bicarbonate solution with a concentration of 1.5mol / L dropwise into it, the volume of the aluminum salt solution and the ammonium bicarbonate solution is 1:1; then the resulting mixture is spray-dried, and the dried particles are roasted, The calcination temperature is 450°C to obtain a-Al 2 o 3 coated magnetic material particles, wherein, a-Al 2 o 3 The ratio of nanoparticles to inorganic aluminum salt solution is 1g:500mL;

[0049] Step 2, polyphenylene sulfide powder, step 1 obtained a-Al 2 o 3 The coated magnetic material par...

Embodiment 2

[0052] A melt-spinning process is a melt-spinning process, and the melt is obtained as follows:

[0053] Step 1, at 50°C, a-Al 2 o 3 The nanoparticles are placed in the aluminum sulfate solution with a concentration of 0.5mol / L to obtain a dispersion, and the pH of the solution is adjusted to 6~7; add magnetic material particles (Fe particles, average particle size 2 microns) to the dispersion, and after the addition is completed, Add ammonium bicarbonate solution with a concentration of 1.5mol / L dropwise into it, the volume of the aluminum salt solution and the ammonium bicarbonate solution is 1:1; then the resulting mixture is spray-dried, and the dried particles are roasted, The calcination temperature is 450°C to obtain a-Al 2 o 3 coated magnetic material particles, wherein, a-Al 2 o 3 The ratio of nanoparticles to inorganic aluminum salt solution is 1g:500mL;

[0054] Step 2, polyphenylene sulfide powder, step 1 obtained a-Al 2 o 3 The coated magnetic material par...

Embodiment 3

[0057] A melt-spinning process is a melt-spinning process, and the melt is obtained as follows:

[0058] Step 1, at 80°C, the a-Al 2 o 3 The nanoparticles are placed in the inorganic aluminum salt solution with a concentration of 1mol / L to obtain a dispersion, and the pH of the solution is adjusted to 6~7; the magnetic material particles are added to the dispersion, and the concentration of 2mol / L is added dropwise to the dispersion. L of ammonium bicarbonate solution, the volume of the aluminum salt solution and the ammonium bicarbonate solution is 1:1; then the resulting mixture is spray-dried, and the dried particles are roasted at a roasting temperature of 500°C to obtain a-Al 2 o 3 coated magnetic material particles, wherein, a-Al 2 o 3 The ratio of nanoparticles to inorganic aluminum salt solution is 1g:700mL;

[0059] Step two, the a-Al obtained in step one 2 o 3 The coated magnetic material particles are mixed with other fiber raw materials and obtained by melti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a melt spinning device and technology and belongs to the field of spinning. According to the melt spinning technology, magnetic force parallel to the direction of the ground is applied to a melt in a wire drawing process, and the melt is prepared with a method comprising steps as follows: step 1, a-Al2O3 coated magnetic material particles are prepared; step 2, the a-Al2O3coated magnetic material particles obtained in step 1 are mixed with other fiber raw materials, and a mixture is molten. With adoption of the technology and the device, magnetic fibers with consistentmagnetic orientation can be obtained.

Description

technical field [0001] The invention relates to a melt spinning device and process, belonging to the spinning field. Background technique [0002] Magnetic fibers are chemical fibers that contain magnetic substances and are magnetic. Currently, fiber preparation methods mainly include melt spinning and solution spinning. Fiber-forming polymers that generally do not decompose significantly in the molten state are melt-spun, such as polyester fibers, polyamide fibers, and the like. The melt spinning process is simple, the spinning speed is high, and it is the most widely used spinning method. At present, there are many methods for preparing magnetic fibers by melt spinning, such as wrapping or attaching a layer of magnetic material on the existing fibers, so that the obtained fibers can obtain certain magnetic properties. It is also possible to mix the magnetic material into the slurry for preparing the fiber when the fiber is prepared, so that the magnetic material is inco...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/94D01F9/08D01F1/10D01D5/08D01D13/02D01D1/09
CPCD01D1/09D01D5/08D01D13/02D01F1/10D01F6/94D01F9/08
Inventor 孙亮蒋秋菊
Owner QINGDAO ST MEER FIBER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap