Composite alloy plate and preparation method thereof

A composite alloy and composite material technology, applied in the field of composite alloy plate and its preparation, can solve the problems of low bonding strength, unsatisfactory, unstable, etc., and achieve the effect of high metallurgical bonding rate and good peel strength performance

Inactive Publication Date: 2018-06-05
JIANGSU CHUANGTAITE STEEL PROD CO LTD
View PDF13 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the cold rolling composite method has been used in industrial production as early as the 1950s, it has not achieved ideal results when used in the production of copper / steel composite materials. The reason is that the matrix and oxides of copper and its alloys have good properties. When the plastic cold rolling is compounded, although the billet is cleaned by a wire brush and the first-pass deformation reaches 70%, there is no crack on the surface. The result is that the billet is squeezed into the crack of the steel with a thin oxide film on the original surface and compounded with the steel (further increasing the amount of deformation in the first pass is limited by the capacity of the rolling mill), so the bond is very fragile, the bond strength is low and unstable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The invention provides a composite alloy plate and a preparation method of the composite alloy plate, wherein the preparation method of the composite alloy plate comprises the following steps:

[0035] (1) Raw material inspection: inspect the raw materials, and select stainless steel plates with a thickness of 1.0-2.5mm and copper plates with a thickness of 0.3-1.0mm that pass the inspection and are suitable for the processing area;

[0036] (2) Surface cleaning and roughening treatment: Clean the surface of stainless steel plates and copper plates, soak them with 8-12% NaOH aqueous solution at 70-80°C for 20 minutes, pickle them with 10% HCl aqueous solution for about 10 minutes, and finally clean them with a wire brush The oxide skin on the composite surface should be washed with alkali before use; and the surface of the cleaned stainless steel plate and copper plate should be polished longitudinally to make the surface roughness of the stainless steel plate 80-100 mic...

Embodiment 1

[0051] A composite alloy plate prepared by the following method:

[0052] (1) Raw material inspection: inspect the raw materials, select the stainless steel plate with a thickness of 1.0mm and the copper plate with a thickness of 0.3mm that pass the inspection and are suitable for the processing area;

[0053] (2) Surface cleaning and roughening treatment: Clean the surface of the stainless steel plate and copper plate, soak in 8% NaOH aqueous solution at 80°C for 20 minutes, then pickle with 10% HCl aqueous solution for about 10 minutes, and finally clean the surface to be composited with a wire brush Oxide skin, wire brushes are washed with alkali before use; and the surface of the cleaned stainless steel plate and copper plate is longitudinally polished, so that the surface roughness of the stainless steel plate is 80 microns, and the surface roughness of the copper plate is 83 microns;

[0054] (3) Continuous temperature compounding: Send the stainless steel plate and copp...

Embodiment 2

[0067] A composite alloy plate prepared by the following method:

[0068] (1) Raw material inspection: inspect the raw materials, select the stainless steel plate with a thickness of 2.5mm and the copper plate with a thickness of 1.0mm that pass the inspection and are suitable for the processing area;

[0069] (2) Surface cleaning and roughening treatment: Clean the surface of stainless steel plate and copper plate, soak in 12% NaOH aqueous solution at 80°C for 20 minutes, then pickle with 10% HCl aqueous solution for about 10 minutes, and finally clean the surface to be compounded with a wire brush Scale, steel wire brushes are washed with alkali before use; and the surface of the cleaned stainless steel plate and copper plate is longitudinally polished, so that the surface roughness of the stainless steel plate is 100 microns, and the surface roughness of the copper plate is 104 microns;

[0070] (3) Continuous temperature compounding: the stainless steel plate and copper pl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to view more

Abstract

The invention provides a composite alloy plate and a preparation method thereof. The preparation method comprises the following steps of raw material inspection, surface cleaning, roughening treatment, continuous temperature compounding, diffusion annealing, scale cinder cleaning, cogging rolling, middle annealing, fine rolling, straightening and flattening, oil removal and degreasing, shearing and online whole inspection, and packaging and warehouse entering. The composite alloy plate formed by the preparation method has the advantages of high tensile intensity, high peeling intensity and thelike.

Description

technical field [0001] The invention relates to the technical field of composite rolling, in particular to a composite alloy plate and a preparation method thereof. Background technique [0002] In the prior art, copper-steel composite materials are usually prepared by hot-rolling and cold-rolling composite methods. [0003] The hot-rolling composite method is a process method in which the composite metal billet is rolled and deformed under high temperature and high pressure, and different metals are combined under the combined action of heat and force. It has the advantages of simple process and high production efficiency. Hot-rolling cladding is a commonly used cladding method of solid-phase bonding, and its process generally includes 3 steps: firstly, cleaning of the bonded surface, including degreasing and deoxidizing film. Keep the surface to be bonded clean; then carry out initial bonding, and make the component metals undergo plastic deformation together through high...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21C37/02C21D1/26C21D1/74C22F1/08C22F1/02
CPCB21C37/02C21D1/26C21D1/74C22F1/02C22F1/08
Inventor 华以恒陈显卿马远国蒉忠芳郭阳刘云飞
Owner JIANGSU CHUANGTAITE STEEL PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap