Hydrophobic graphene solvent-free epoxy underwater curing coating and preparation method thereof

An underwater curing and graphene technology, applied in epoxy resin coatings, coatings, etc., can solve problems such as poor adhesion, poor flexibility of paint films, and difficulties in underwater construction

Inactive Publication Date: 2018-06-22
燕园众欣纳米科技(北京)有限公司
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a hydrophobic graphene solvent-free epoxy underwater curing coating and it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrophobic graphene solvent-free epoxy underwater curing coating and preparation method thereof
  • Hydrophobic graphene solvent-free epoxy underwater curing coating and preparation method thereof
  • Hydrophobic graphene solvent-free epoxy underwater curing coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The preparation method of a kind of hydrophobic type graphene solvent-free epoxy underwater curing coating described in the present embodiment is made from the raw material of following percentage by weight:

[0019] Component A

[0020]

[0021] Component B

[0022]

[0023] Preparation method: (1) Put each raw material in component A into the tank one by one, stir rapidly to disperse, and grind to 50 μm to obtain component A. (2) Put each raw material in component B into the tank one by one, stir rapidly to disperse, and grind to 50 μm to obtain component B. (3) Mix component A and component B uniformly according to the weight ratio of 100:38 to obtain a hydrophobic graphene solvent-free epoxy underwater curing coating.

[0024] How to use: Remove floating rust on steel surface, remove dirt on concrete surface, and then brush, roll or scrape the mixed paint on the surface of the substrate.

Embodiment 2

[0026] The preparation method of a kind of hydrophobic type graphene solvent-free epoxy underwater curing coating described in the present embodiment is made from the raw material of following percentage by weight:

[0027] Component A

[0028]

[0029] Component B

[0030]

[0031] Preparation process and method of use are the same as in Example 1

Embodiment 3

[0033] The preparation method of a kind of hydrophobic type graphene solvent-free epoxy underwater curing coating described in the present embodiment is made from the raw material of following percentage by weight:

[0034] Component A

[0035]

[0036] Component B

[0037]

[0038]

[0039] Preparation process and method of use are the same as in Example 1

[0040] Table 1 performance test results

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a hydrophobic graphene solvent-free epoxy underwater curing coating and a preparation method thereof. The hydrophobic graphene solvent-free epoxy underwater curing coating is prepared from a component A and a component B in the weight ratio being 100:(30-55), wherein the component A comprises raw materials as follows: 35%-50% of epoxy resin, 6%-10% of polysulfide rubber, 2%-8% of petroleum resin, 7%-10% of a reactive diluent, 1%-5% of organic silicon resin, 20%-40% of antirust pigments, 0.2%-6% of an aid and 0.5%-5% of hydrophobic graphene; the component B comprises rawmaterials as follows: 40%-50% of modified phenolic amine, 15%-20% of modified aliphatic amine, 0.5%-15% of an aid and 18%-30% of pigment and filler. The invention provides the hydrophobic graphene solvent-free epoxy underwater curing coating and the preparation method thereof, and the hydrophobic graphene solvent-free epoxy underwater curing coating can be constructed on surfaces of underwater substrates, can be cured quickly and has excellent adhesive force and corrosion resistance.

Description

technical field [0001] The invention relates to a hydrophobic graphene solvent-free epoxy underwater curing coating, in particular to a preparation method of a hydrophobic graphene solvent-free epoxy underwater curing coating. technical background [0002] my country has a long coastline and a vast sea area under its jurisdiction. With the vigorous development of ocean development, marine corrosion and protection has become one of the main problems to be solved in the process of my country's economic development. At present, some special engineering components of marine heavy-duty anti-corrosion, such as offshore oil drilling platforms, trestles, various oil pipelines, wharf steel piles and other large-scale facilities, as well as marine concrete structures, use anti-corrosion coatings for anti-corrosion. If coating anti-corrosion failure occurs, these The components have been soaked in seawater environment for a long time, so that they cannot reach the service life. Moreov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D163/00C09D181/04C09D157/02C09D183/04C09D7/61
CPCC09D163/00C08K2003/327C08L2205/035C08L81/04C08L57/02C08L83/04C08K13/06C08K3/04C08K3/32
Inventor 田幼华侯胜华
Owner 燕园众欣纳米科技(北京)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap