Colorful multi-element nylon yarn and preparation method thereof

A multi-element, nylon filament technology, applied in the field of textiles, can solve the problems of lack of nylon filament preparation methods with different colors, colorful and multi-element, and achieve the effects of increasing durability, solving insufficient cohesion, and having good anti-pilling performance.

Inactive Publication Date: 2018-07-03
YIWU MASHANGSHENG KNIT GOODS CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there is a lack of a colorful and multi-element nylon filament with different colors per meter and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A colorful and multi-element nylon filament of the present invention, said colorful and multi-element nylon filament is composed of the following components according to the mass percentage:

[0035] Infrared heating fiber silk 80%,

[0036] Antibacterial Fiber 2%,

[0037] The balance is nylon filaments.

[0038] The infrared heating fiber filaments include the following components by mass percentage:

[0039] Nano zinc oxide poly and urethane microcapsules 30%

[0040] Nano Zirconia Composite Particles 18%,

[0041] The balance is nylon filaments.

[0042] The nano zinc oxide polyurethane microcapsules are nano zinc oxide polyurethane microcapsules formed by dispersing nano zinc oxide particles in polyurethane raw materials.

[0043] The nano-zirconia composite particles are prepared by the following method: dispersing the nano-zirconia powder in the aqueous solution of hydroxypropyl methylcellulose to form a nano-zirconia dispersion; adjusting the pH value of th...

Embodiment 2

[0055] The difference between Example 2 and Example 1 is: a colorful multi-element nylon yarn of the present invention, said colorful multi-element nylon yarn is composed of the following components according to mass percentage:

[0056] Infrared heating fiber silk 55%,

[0057] Antibacterial Fiber 15%,

[0058] The balance is nylon filaments.

[0059] The infrared heating fiber filaments include the following components by mass percentage:

[0060] Nano zinc oxide poly and urethane microcapsules 10%

[0061] Nano Zirconia Composite Particles 2%,

[0062] The balance is nylon filaments.

[0063] The nano zinc oxide polyurethane microcapsules are nano zinc oxide polyurethane microcapsules formed by dispersing nano zinc oxide particles in polyurethane raw materials.

[0064] The nano-zirconia composite particles are prepared by the following method: dispersing the nano-zirconia powder in the aqueous solution of hydroxypropyl methylcellulose to form a nano-zirconia dispersio...

Embodiment 3

[0069] The difference between Example 3 and Example 1 is: a colorful multi-element nylon yarn of the present invention, said colorful multi-element nylon yarn is composed of the following components according to the mass percentage:

[0070] Infrared heating fiber silk 70%,

[0071] Antibacterial Fiber 8%,

[0072] The balance is nylon filaments.

[0073] The infrared heating fiber filaments include the following components by mass percentage:

[0074] Nano zinc oxide poly and urethane microcapsules 20%

[0075] Nano Zirconia Composite Particles 20%,

[0076] The balance is nylon filaments.

[0077] The nano zinc oxide polyurethane microcapsules are nano zinc oxide polyurethane microcapsules formed by dispersing nano zinc oxide particles in polyurethane raw materials.

[0078] The nano-zirconia composite particles are prepared by the following method: dispersing the nano-zirconia powder in an aqueous solution of hydroxypropyl methylcellulose to form a nano-zirconia disper...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a colorful multi-element nylon yarn and a preparation method thereof. The colorful multi-element nylon yarn consists of the following components in percentage by mass: 55-80% of infrared heating fiber yarn, 2-15% of antibacterial fiber and the balance of nylon fiber yarn. The textile provided by the invention has the advantage of high comfort and tinting strength, differentcolors in different meters, high quality, high brightness and softness, perfect uniformity, low content of impurities, low strength loss and stable structure and proper tightness of double-twisted composite yarn; and moreover, the textile has good anti-pilling performance, and can absorb the infrared rays reflected by the sun and a human body so as to convert the infrared rays into heat energy while the stereoscopic impression is strong.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a colorful and multi-element nylon filament and a preparation method thereof. Background technique [0002] In the field of textile technology, yarn is the key to ensuring the quality of textile products. Scientifically and effectively selecting and blending various yarns and appropriate blending ratios is not only related to the cost of the product, but also related to the quality of the product. At present, in the linen textile industry, flax fibers are blended with other fibers to produce linen blended yarns, such as blending linen with special fibers, so as to improve the roughness and poor hand feeling of linen fabrics while maintaining the advantages of linen. When people sleep in bed in winter, they are often affected by the coldness of the bedding, and it is easy to have a bad rest, which seriously affects people's sleep quality. At present, the traditional ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/04D02G3/34D02G3/44D06C27/00D06B21/00D06M16/00D06L1/02D06M101/34
CPCD02G3/045D02G3/34D02G3/44D02G3/449D06B21/00D06C27/00D06L1/02D06M16/00D06M16/003D06M2101/34D10B2331/02
Inventor 王铀锝
Owner YIWU MASHANGSHENG KNIT GOODS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com