Pt/MoS2 nano catalyst and preparation method and application thereof

A nano-catalyst and nano-sheet technology, which can be used in catalyst activation/preparation, physical/chemical process catalysts, chemical instruments and methods, etc., can solve the problem of high price, and achieve the effect of less special equipment, easy separation, and high catalytic activity.

Active Publication Date: 2018-07-06
INST OF ADVANCED TECH UNIV OF SCI & TECH OF CHINA
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional noble metal catalysts have

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pt/MoS2 nano catalyst and preparation method and application thereof
  • Pt/MoS2 nano catalyst and preparation method and application thereof
  • Pt/MoS2 nano catalyst and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0040] Example 1

[0041] Pt / MoS 2 Preparation of nanocatalyst

[0042] (1) Mix (NH 4 ) 6 Mo 7 O 24 ·4H 2 O and thiourea dissolved in deionized water, (NH 4 ) 6 Mo 7 O 24 ·4H 2 The mass of O is 1.22g, the mass of thiourea is 1.07g, and the volume of deionized water is 34mL. After stirring for 40 minutes, the hydrothermal reaction is carried out. The temperature of the hydrothermal reaction is 218℃, and the time of the hydrothermal reaction is 17.5h. Cool to room temperature, centrifuge the solid material cooled to room temperature, the speed of centrifugation is 7600 rpm, the time of centrifugation is 5 minutes, the product obtained by centrifugation is ultrasonically washed with a polar solvent for 2 minutes, and then the centrifugal separation is continued , The speed of centrifugation is 7600 rpm, the time of centrifugation is 7 minutes, and then the product obtained by centrifugation is ultrasonically washed with a polar solvent for 1 min, and dried under vacuum at 61°C overnig...

Example Embodiment

[0045] Example 2

[0046] Pt / MoS 2 Preparation of nanocatalyst

[0047] (1) Under stirring at room temperature, (NH 4 ) 6 Mo 7 O 24 ·4H 2 O and thiourea dissolved in deionized water, (NH 4 ) 6 Mo 7 O 24 ·4H 2 The mass of O is 1.21g, the mass of thiourea is 1.05g, the volume of deionized water is 34mL, and the hydrothermal reaction is carried out after stirring for 40min. The temperature of the hydrothermal reaction is 215℃, the time of the hydrothermal reaction is 17h, and then cooling To room temperature, centrifuge the solid material cooled to room temperature at 7000 rpm, and the time of centrifugation is 5 minutes. The product obtained by centrifugation is ultrasonically washed with a polar solvent for 2 minutes, and then the centrifugal separation is continued. The speed of centrifugation was 7000 rpm, the time of centrifugation was 5 min, and the product obtained by centrifugation was ultrasonically washed with a polar solvent for 1 min, and dried under vacuum at 58°C overnig...

Example Embodiment

[0050] Example 3

[0051] Pt / MoS 2 Preparation of nanocatalyst

[0052] (1) Mix (NH 4 ) 6 Mo 7 O 24 ·4H 2 O and thiourea dissolved in deionized water, (NH 4 ) 6 Mo 7 O 24 ·4H 2 The mass of O is 1.25g, the mass of thiourea is 1.08g, the volume of deionized water is 36mL, the hydrothermal reaction is carried out after stirring for 50min, the temperature of the hydrothermal reaction is 225℃, the time of the hydrothermal reaction is 19h, and then cooling To room temperature, the solid material cooled to room temperature is centrifuged, the rotation speed of the centrifugal separation is 8000 rpm, and the time of the centrifugal separation is 7 minutes. The product obtained by centrifugation is ultrasonically washed with a polar solvent for 2 minutes, and then the centrifugal separation is continued. The speed of centrifugation is 8000 rpm, the time of centrifugation is 5 minutes, and the product obtained by centrifugation is ultrasonically washed with a polar solvent for 2 minutes, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Concentrationaaaaaaaaaa
Concentrationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a Pt/MoS2 nano catalyst and a preparation method and application thereof. The Pt/MoS2 nano catalyst is prepared from MoS2 nano sheets and Pt atoms independently loaded on the surfaces of the MoS2 nano sheets. The Pt/MoS2 nano catalyst is built up by loading the platinum single atoms lonely on the substrates of the molybdenum sulfide nano sheets, not only a heterogeneous structure is achieved so that the catalyst can be easily separated, collected and recycled from a reaction system, but also the Pt/MoS2 nano catalyst can have very high catalysis activity in catalyzing hydrogenation of carbon dioxide based on the high-efficiency atom utilization rate of the single atoms, the high metal substrate mutual action and the synergistic effects of adjacent single atoms.

Description

technical field [0001] The invention relates to the technical field of energy catalysis, in particular to a Pt / MoS 2 Nanocatalyst and its preparation method and application. Background technique [0002] In recent years, with the intensification of energy crisis and environmental pollution, the technology of using carbon-containing inorganic substances to prepare small molecular organic substances through thermochemical reactions has received extensive attention. How to conduct safe and efficient reactions is the focus of research in this field. Both carbon dioxide and hydrogen are stable at room temperature and are ideal starting materials for the reaction. The temperature required for the hydrogenation of carbon dioxide is low, and the products are valuable substances such as alkanes, alcohols, ethers, aldehydes, and carboxylic acids. The main products can be controlled by using different catalysts or changing the ratio of reaction gases. Meet different needs. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J27/051B01J37/10B01J37/16C07C31/04C07C29/157
CPCB01J27/0515B01J35/0006B01J35/0013B01J37/10B01J37/16C07C29/157C07C31/04Y02P20/52
Inventor 李洪良蒲正天王梦琳曾杰
Owner INST OF ADVANCED TECH UNIV OF SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products