Preparation method of waterborne rainbow aluminum paste

A rainbow, water-based technology, applied in chemical instruments and methods, pigment slurry, dyeing organosilicon compound treatment, etc., can solve the problems of single color, water-based metal pigments and other problems, and achieve the effect of easy dispersion.

Inactive Publication Date: 2018-07-06
HEFEI SUNRISE PIGMENTS
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, due to the requirements of environmental protection, the development of oil-based products is more and more constrained, so the water-based of metallic pigments is urgent
Traditional water-based metallic pigments generally use spherical aluminum powder as raw material, are produced by wet ball milling, and are produced by water-based surface modification methods. The color is single, and usually only shows silver-gray effects. In view of this, We propose a preparation method of water-based rainbow aluminum paste

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] This embodiment provides a kind of preparation method of water-based rainbow aluminum paste, comprising the following steps:

[0023] Step 1. Coating a layer of water-based release coating with a dry film thickness of not less than 1um on a PET film of a certain thickness;

[0024] Step 2. Coating a layer of aluminum with a purity of 99.99% on the film coating by PVD method to form an aluminized film with a film thickness of between;

[0025] Step 3. Carve the surface of the aluminized film by laser engraving or embossing to give a flat surface microstructure of the aluminized layer, and obtain an aluminum layer that can interfere and diffract light;

[0026] Step 4. Immerse the aluminized film in a certain quality solvent. After the release coating is dissolved, the aluminized layer will fall off from the film and disperse in the solvent;

[0027] Step 5, concentrating the aluminum film suspension to obtain an aluminum paste with a solid content of not less than 60%...

Embodiment 2

[0036] This embodiment provides a kind of preparation method of water-based rainbow aluminum paste, it is characterized in that, comprises the following steps:

[0037] Step 1. Coating a layer of water-based release coating with a dry film thickness of not less than 1um on a PET film of a certain thickness;

[0038] Step 2. Coating a layer of aluminum with a purity of 99.99% on the film coating by PVD method to form an aluminized film with a film thickness of between;

[0039] Step 3. Carve the surface of the aluminized film by laser engraving or embossing to give a flat surface microstructure of the aluminized layer, and obtain an aluminum layer that can interfere and diffract light;

[0040] Step 4. Immerse the aluminized film in a certain quality solvent. After the release coating is dissolved, the aluminized layer will fall off from the film and disperse in the solvent;

[0041] Step 5, concentrating the aluminum film suspension to obtain an aluminum paste with a solid ...

Embodiment 3

[0050] A preparation method of water-based rainbow aluminum paste, comprising the following steps:

[0051] Step 1. Coating a layer of water-based release coating with a dry film thickness of not less than 1um on a PET film of a certain thickness;

[0052] Step 2. Coating a layer of aluminum with a purity of 99.99% on the film coating by PVD method to form an aluminized film with a film thickness of between;

[0053] Step 3. Carve the surface of the aluminized film by laser engraving or embossing to give a flat surface microstructure of the aluminized layer, and obtain an aluminum layer that can interfere and diffract light;

[0054] Step 4. Immerse the aluminized film in a certain quality solvent. After the release coating is dissolved, the aluminized layer will fall off from the film and disperse in the solvent;

[0055] Step 5, concentrating the aluminum film suspension to obtain an aluminum paste with a solid content of not less than 60%;

[0056]Step 6. Add the above-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of chemical industry, in particular to a preparation method of waterborne rainbow aluminum paste. The preparation method comprises the following steps: step one, coating a PET thin film with certain thickness with a layer of waterborne release coating of which the thickness of a dry film is not smaller than 1mu m; step two, plating a film coating with alayer of aluminum with the purity of 99.99 percent by using a PVD method, thus forming an aluminum-plated film, wherein the film thickness is seen in the description; step three, carrying out surfacecarving on the aluminum-plated film by laser engraving or molding, endowing the surface of a flat aluminum-plating layer with a micro-structure to obtain an aluminum layer which can generate interference and diffraction to light. According to the preparation method of the waterborne rainbow aluminum paste, disclosed by the invention, a waterborne aluminum pigment with rainbow effects selects a high-purity aluminum wire as a raw material; the high-purity aluminum wire is subjected to vapor deposition on the PET thin film by adopting a vacuum evaporation method; the high-purity aluminum wire isendowed with great diameter-thickness ratio and excellent rainbow effects by mould pressing, and is subjected to waterborne surface treatment at later stage to obtain a product. The waterborne rainbow aluminum paste is subjected to surface waterborne treatment based on oily rainbow aluminum paste; meanwhile, the rainbow effects of the waterborne rainbow aluminum paste are not affected.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to a preparation method of water-based rainbow aluminum paste. Background technique [0002] With the development of the times, people's pursuit of color has gradually changed from a single color to a colorful color. Metallic pigments with rainbow effects have also emerged as the times require, and are widely used in anti-counterfeiting, home appliances, automobiles and other fields. At the same time, due to the requirements of environmental protection, the development of oil-based products is increasingly constrained, so the water-based transformation of metallic pigments is urgent. Traditional water-based metallic pigments generally use spherical aluminum powder as raw material, are produced by wet ball milling, and are produced by water-based surface modification methods. The color is single, and usually only shows silver-gray effects. In view of this, We propose a pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D17/00C09D11/037C09C1/40C09C3/08C09C3/10C09C3/12
CPCC09C1/0015C09C3/006C09C3/08C09C3/10C09C3/12C09D11/037C09D17/006
Inventor 朱胜利董前年王蓓蓓沈志平张泽锋朱双单
Owner HEFEI SUNRISE PIGMENTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com