Solid electrolyte used for horizontal battery production

A solid-state electrolyte and horizontal battery technology, applied in electrolyte immobilization/gelation, lead-acid batteries, etc., can solve problems such as poor conductivity of solid-state electrolytes

Inactive Publication Date: 2018-07-06
GUANGZHOU ZHUOYUE POWER NEW ENERGY CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a solid electrolyte for horizontal battery production, to solve the problem of poor conductivity of the solid electrolyte

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid electrolyte used for horizontal battery production
  • Solid electrolyte used for horizontal battery production
  • Solid electrolyte used for horizontal battery production

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The solid electrolyte for horizontal battery production is mainly composed of the following raw materials by mass: 80 parts by mass of polyphenylene sulfide, 9 parts by mass of Li2CO3, 1.5 parts by mass of colloidal graphite powder, 8 parts by mass of expanded body 6 and 50 parts by mass The infiltration layer 2 of the swelling body 6 contains 2 parts by mass of sodium 10 and 4 parts by mass of water 12. The mass parts of the grease 3 in the infiltration layer 2 is 30, and the grease 3 is conductive grease; the mass parts of the lead acetate solution 4 is 20, and the concentration of the lead acetate solution 4 is 0.2 mol / L.

[0027] After the above raw materials are made into solid electrolyte 1, it is detected with a testing tool that the conductivity of solid electrolyte 1 at room temperature is 2.4×10 -4 S / cm, where the detection tool is a conductivity detector.

Embodiment 2

[0029] The solid electrolyte for horizontal battery production is mainly composed of the following raw materials by mass: 91 parts by mass of polyphenylene sulfide, 16 parts by mass of Li2CO3, 4 parts by mass of colloidal graphite powder, 8 parts by mass of expanded body 6 and 50 parts by mass The infiltration layer 2 of the swelling body 6 contains 2 parts by mass of sodium 10 and 4 parts by mass of water 12. The mass parts of grease in the infiltration layer 2 is 30, and the grease is conductive grease; the mass parts of the lead acetate solution 4 is 20, and the concentration of the lead acetate solution 4 is 0.2 mol / L.

[0030] After the above raw materials are made into solid electrolyte 1, it is detected with a testing tool that the conductivity of solid electrolyte 1 at room temperature is 1.9×10 -4 S / cm, where the detection tool is a conductivity detector.

Embodiment 3

[0032] The solid electrolyte for horizontal battery production mainly consists of the following raw materials by mass: 86 parts by mass of polyphenylene sulfide, 12 parts by mass of Li2CO3, 2.5 parts by mass of colloidal graphite powder, 8 parts by mass of expanded body 6 and 50 parts by mass The infiltration layer 2 of the swelling body 6 contains 2 parts by mass of sodium 10 and 4 parts by mass of water 12. The mass parts of grease in the infiltration layer 2 is 30, and the grease is conductive grease; the mass parts of the lead acetate solution 4 is 20, and the concentration of the lead acetate solution 4 is 0.2 mol / L.

[0033] After the above raw materials are made into solid electrolyte 1, it is detected with a testing tool that the conductivity of solid electrolyte 1 at room temperature is 2.6×10 -4 S / cm, where the detection tool is a conductivity detector.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
electrical conductivityaaaaaaaaaa
electrical conductivityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of battery production, and discloses a solid electrolyte used for horizontal battery production. The solid electrolyte comprises the following components in parts bymass: 80 to 91 parts of a polyhenylene high-molecular organic polymer, 9 to 16 parts of a lithium salt and 1.5 to 4 parts of graphite powder. The graphite powder in the scheme has high electrical conductivity, abrasion resistance and lubricating property, the electrical conductivity of the solid electrolyte can be improved, and then the electrical conductivity of each part of the solid electrolyte is relatively balanced, so that the electrical conductivity is promoted. Through the scheme, the space structure is adjusted by selecting appropriate lithium salt, and through the combined action ofthe polyhenylene high-molecular organic polymer and the lithium salt, the electrical conductivity activation energy is reduced, so that an ion channel of a one-dimensional structure is realized, theleakage probability of the solid electrolyte is reduced, and guarantee is provided for the electrical conductivity of the solid electrolyte.

Description

Technical field [0001] The invention belongs to the field of battery manufacturing. Background technique [0002] In traditional lead-acid batteries, the plates are assembled perpendicular to the ground, and when in use, they are also installed perpendicular to the ground. The plate lugs of the positive and negative plates are placed on the upper part of the battery, and the conductive component busbars and end poles are connected from above. Lead out. [0003] The grid of the horizontal lead-acid battery pole plate is woven with glass fiber and lead composite material, and the pole plate is a quasi-bipolar structure, that is, half of the grid is coated with a positive electrode active material, and the other half is coated with a negative electrode active material It is the negative plate, in which the positive electrode active material and the negative electrode active material are solid electrolytes. After laminating, pickling acid, surface drying, curing and other processes, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/10
CPCH01M10/10H01M2300/0085Y02E60/10
Inventor 何幸华李政文黎少伟何可立马俊
Owner GUANGZHOU ZHUOYUE POWER NEW ENERGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap