Acidic-corrosion-resistant X65MS pipeline steel and preparation method thereof

A pipeline steel, acid-resistant technology, applied in the direction of manufacturing tools, metal rolling, heat treatment equipment, etc., can solve the problems of high Mn content in pipeline steel, affecting the HIC performance of pipeline steel, and high cost

Inactive Publication Date: 2018-07-10
BAOTOU IRON & STEEL GRP
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the above-mentioned defects of the prior art, the technical problem to be solved by the present invention is that the X65MS pipeline steel has a high Mn content in the prior art, which affects the HIC performance of the pipeline steel, uses expensive Mo element, makes the cost higher, and is not easy to be popularized and applied on a large scale

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acidic-corrosion-resistant X65MS pipeline steel and preparation method thereof
  • Acidic-corrosion-resistant X65MS pipeline steel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0081] Embodiment 1, preparation of acid corrosion resistant X65MS pipeline steel

[0082] Adopt KR method to desulfurize molten iron and high-quality steel scrap, LF refining and RH vacuum treatment to ensure the cleanliness of molten steel, LF refining uses a large amount of slag to make slag, RH vacuum treatment ensures the deep vacuum cycle time of molten steel, calcium treatment after vacuum treatment, Ar gas softening The blowing time is longer than 12 minutes, the slab is continuously cast with full protection pouring, and the dynamic soft reduction technology is adopted to reduce the center segregation of the continuous casting slab to obtain the slab;

[0083] The slab is heated to a heating temperature of 1173°C, and the total time in the furnace is 189 minutes, and then the first-stage rolling is carried out, that is, the rolling in the austenite recrystallization zone, the starting rolling temperature is 1160°C, and the reduction ratio of the first pass is > 10%, t...

Embodiment 2

[0084] Embodiment 2, preparation of acid corrosion resistant X65MS pipeline steel

[0085] Adopt KR method to desulfurize molten iron and high-quality steel scrap, LF refining and RH vacuum treatment to ensure the cleanliness of molten steel, LF refining uses a large amount of slag to make slag, RH vacuum treatment ensures the deep vacuum cycle time of molten steel, calcium treatment after vacuum treatment, Ar gas softening The blowing time is longer than 12 minutes, the slab is continuously cast with full protection pouring, and the dynamic soft reduction technology is adopted to reduce the center segregation of the continuous casting slab to obtain the slab;

[0086] The slab is heated to a heating temperature of 1172°C, and the total time in the furnace is 192 minutes, and then the first-stage rolling is carried out, that is, the rolling in the austenite recrystallization zone, the starting rolling temperature is 1158°C, and the reduction rate of the first pass is > 10%, th...

Embodiment 3

[0087] Embodiment 3, preparation of acid corrosion resistant X65MS pipeline steel

[0088] Adopt KR method to desulfurize molten iron and high-quality steel scrap, LF refining and RH vacuum treatment to ensure the cleanliness of molten steel, LF refining uses a large amount of slag to make slag, RH vacuum treatment ensures the deep vacuum cycle time of molten steel, calcium treatment after vacuum treatment, Ar gas softening The blowing time is longer than 12 minutes, the slab is continuously cast with full protection pouring, and the dynamic soft reduction technology is adopted to reduce the center segregation of the continuous casting slab to obtain the slab;

[0089] The slab is heated to a heating temperature of 1177°C, and the total time in the furnace is 183 minutes, and then the first-stage rolling is carried out, that is, the rolling in the austenite recrystallization zone, the starting rolling temperature is 1165°C, and the reduction rate of the first pass is > 10%, th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses acidic-corrosion-resistant X65MS pipeline steel which comprises the following components in percentage by weight: 0.04-0.06% of C, 0.10-0.20% of Si, 1.20-1.40% of Mn, no more than 0.010% of P, no more than 0.002% of S, 0.030-0.040% of Nb, 0.010-0.020% of Ti, 0.020-0.040% of Al, 0.20-0.30% of Cr, 0.10-0.20% of Cu and 0.10-0.20% of Ni. The invention further discloses a preparation method of the acidic-corrosion-resistant X65MS pipeline steel. According to the acidic-corrosion-resistant X65MS pipeline steel and the preparation method, the Mn content is lowered, no expensive Mo element is added, and the alloy cost is relatively low, thereby being beneficial to wide popularization and application.

Description

technical field [0001] The invention relates to the technical field of iron and steel metallurgy, in particular to an acid corrosion-resistant X65MS pipeline steel and a preparation method thereof. Background technique [0002] Oil and natural gas is an important strategy and reserve material of the national economy. With the rapid development of the national economy, the demand for energy such as oil and natural gas is increasing. The continuous growth of energy demand, structural adjustment and optimization have driven the oil and gas industry. comprehensive development. Pipeline transportation is an economical, safe and uninterrupted transportation method, which has the advantages of large transportation volume, low cost, high safety, convenience and high efficiency. In order to meet future oil and gas demand, H 2 Compared with the past, the development quantity of S oil and gas fields has increased greatly, and at the same time, the demand for pipeline steel for sour s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/42C22C38/48C22C38/50C22C33/04B21B1/22C21D8/02C21D9/00
CPCC22C38/02B21B1/22B21B2001/225C21D8/0226C21D9/0081C21D2211/005C21D2211/009C22C33/04C22C38/001C22C38/04C22C38/06C22C38/42C22C38/48C22C38/50
Inventor 王少炳王雪莲袁晓鸣卢晓禹魏慧慧
Owner BAOTOU IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com