Macromolecular synthetic adhesive and preparation method thereof

A synthetic rubber and polymer technology, applied in the field of polymer synthetic rubber and its preparation, can solve problems such as air leakage, failure to ensure driving safety, degumming, etc.

Inactive Publication Date: 2018-07-13
上运车物联网科技(深圳)有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there is no high-efficiency, applicable, long-term use and non-degumming anti-puncture and leak-proof special safety upgraded polymer synthetic rubber for car tires. Most of the rubber used in tire upgrade services is improved by hot-melt adhesives for shoes or packaging. Although this kind of hot melt adhesive for shoes or packaging can achieve the function of quickly filling the air leak after the car tire is pierced by a sharp object in a short period of time, it may be degummed during the high-speed driving of the car. risk, so that long-term driving safety cannot be guaranteed, and there will still be air leakage after nailing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Macromolecular synthetic adhesive and preparation method thereof
  • Macromolecular synthetic adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Raw materials and weight percentages thereof required for preparing polymer synthetic glue are as follows:

[0027] Elastomer 39.6%, said elastomer includes SBS thermoplastic elastomer, SEPS thermoplastic elastomer and polybutadiene rubber, wherein: SBS thermoplastic elastomer 29.6%, SEPS thermoplastic elastomer 7%, polybutadiene rubber 3%;

[0028] Tackifier 42.5%, said tackifier includes rosin pentaerythritol ester, petroleum resin and terpene resin, wherein: rosin pentaerythritol ester 8%, petroleum resin 6.5%, terpene resin 28%;

[0029] Softener 5.1%, said softener includes diethyl phthalate, naphthenic oil and pine tar, wherein: diethyl phthalate 3.1%, naphthenic oil 1%, pine tar 1%;

[0030] Anti-aging agent 3.2%, said anti-aging agent includes N,N'-diphenyl-p-phenylenediamine, N-phenyl-N'-isopropyl-p-phenylenediamine and 2,6-di-tert-butyl-4- Methylphenol, of which: N,N'-diphenyl-p-phenylenediamine 1.2%, N-phenyl-N'-isopropyl-p-phenylenediamine 1%, 2,6-di-tert-b...

Embodiment 2

[0041] Raw materials and weight percentages thereof required for preparing polymer synthetic glue are as follows:,

[0042] Elastomer 41.4%, said elastomer includes SIS thermoplastic elastomer, SBS thermoplastic elastomer and natural rubber, wherein: SIS thermoplastic elastomer 30.4%, SBS thermoplastic elastomer 8%, natural rubber 3%;

[0043] Tackifier 41.9%, said tackifier includes rosin pentaerythritol ester, hydrogenated petroleum resin and rosin, wherein: rosin pentaerythritol ester 7.9%, hydrogenated petroleum resin 6%, rosin 28%;

[0044] Softener 5.4%, said softener includes diethyl phthalate, pine tar and aromatic oil, wherein: diethyl phthalate 1%, pine tar 1.4%, aromatic oil 3%;

[0045] Anti-aging agent 2.2%, said anti-aging agent includes N,N'-diphenyl-p-phenylenediamine and N-phenyl-N'-isopropyl-p-phenylenediamine, wherein: N,N'-diphenyl-p-phenylenediamine 0.5% of phenylenediamine, 1.7% of N-phenyl-N'-isopropyl-p-phenylenediamine;

[0046] Filler 7.7%, described ...

Embodiment 3

[0056] Raw materials and weight percentages thereof required for preparing polymer synthetic glue are as follows:,

[0057] Elastomer 43.1%, said elastomer includes SEPS thermoplastic elastomer, SIS thermoplastic elastomer and polyisoprene rubber, of which: SEPS thermoplastic elastomer 32%, SIS thermoplastic elastomer 8.1%, polyisoprene rubber 3 %;

[0058] Tackifier 41.2%, said tackifier includes hydrogenated petroleum resin, hydrogenated rosin and petroleum resin, wherein: petroleum resin 6%, hydrogenated rosin 5.2%, hydrogenated petroleum resin 30%;

[0059] Softener 5.9%, said softener includes diethyl phthalate, aromatic oil and liquid polybutadiene, wherein: diethyl phthalate 1.9%, aromatic oil 1%, liquid polybutadiene 3 %;

[0060] Anti-aging agent 2%, said anti-aging agent includes N-phenyl-N'-isopropyl-p-phenylenediamine and 2,6-di-tert-butyl-4-methylphenol, wherein: N-phenyl-N' - Isopropyl-p-phenylenediamine 1%, 2,6-di-tert-butyl-4-methylphenol 1%;

[0061] Fille...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention discloses macromolecular synthetic adhesive. The macromolecular synthetic adhesive comprises the following components in percentage by weight: 40 to 48 percent of elastomer, 41.5 to 43 percent of tackifier, 4 to 6 percent of softening agent, 1.5 to 3.2 percent of anti-aging agent and 4.5 to 9 percent of filling agent. The invention further discloses a preparation method of the macromolecular synthetic adhesive. The macromolecular synthetic adhesive has high toughness, high viscosity, high stability, high durability, high tensile strength and special memory performance, a prickedand deformed part of the inner wall of a tyre can automatically recover the memory position when the tyre whose the inner wall is spray-coated with the macromolecular synthetic adhesive is inserted bya sharp object, and the macromolecular synthetic adhesive can rapidly fill a gap formed after the sharp object is pulled out of the tyre, so that the full-sealed space of the tyre still can be maintained and the air leakage condition of the tyre is avoided.

Description

technical field [0001] The invention relates to the field of polymer synthetic glue, in particular to a polymer synthetic glue and a preparation method thereof. Background technique [0002] According to authoritative department statistics, 70% of accidental traffic accidents on domestic highways are caused by automobile tire blowouts, and when automobiles have traffic accidents at a speed of more than 150 km / h, the death rate is close to 100%. Especially small cars are also likely to cause major traffic accidents such as secondary collisions after a high-speed tire blowout. Therefore tire is very important to guaranteeing the driving safety of automobile, and various automobile manufacturers have also released various "explosion-proof tires", but the explosion-proof principle of the current "explosion-proof tire" mainly prevents the tire from being crushed and prevents the tire from being crushed after the tire leaks and loses pressure. The tire comes off the rim, not to p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L53/02C08L7/00C08L9/00C08L93/04C08L57/02C08L45/00C08K13/02C08K5/18C08K3/36C08K3/34C08K3/26C08K5/13
Inventor 吴华龙郭丽丽
Owner 上运车物联网科技(深圳)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap