Light incontinence pad for adult
An incontinence pad, light technology, applied in the direction of absorbent pads, personal care, synthetic resin layered products, etc., can solve the problems of poor antibacterial and deodorizing effects, poor water absorption of incontinence pads, and can not be reused to improve the anti-side Leakage effect, good liquid absorption, long service life effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0037] Example 1
[0038] The woven fabric, needle-punched fabric, and film are stitched to form an adult mild incontinence pad. The specific process is:
[0039] (1) Preparation of the guide layer: using spinning technology to spin 40mm 5D polyester fibers into yarns, using weaving technology to make warp yarns with a fineness of 75D and weft yarns with a fineness of 60D into a warp density of 100 A woven fabric with a root / 10cm and a weft density of 90 roots / 10cm, forming a diversion layer, with an areal density of 37g / m 2 ;
[0040] (2) Preparation of the absorbent layer: use 40mm 3D viscose fiber and 40mm 2D polypropylene fiber with a ratio of 95% viscose: 5% polypropylene, and they are carded into a net, needle punched reinforcement, and mechanically beaten. The holes are made into needle-punched non-woven fabrics to form an absorbent layer. This layer is composed of upper and lower sheets. After needle punching, the upper sheet undergoes a subsequent punching process. The open...
Example Embodiment
[0044] Example 2
[0045] The woven fabric, needle-punched fabric, and film are stitched to form an adult mild incontinence pad. The specific process is:
[0046] (1) Preparation of the guide layer: using spinning technology to spin 40mm 5D polyester fibers into yarns, using weaving technology to make warp yarns with a fineness of 75D and weft yarns with a fineness of 60D into a warp density of 100 A woven fabric with a root / 10cm and a weft density of 90 roots / 10cm, forming a diversion layer, with an areal density of 37g / m 2 ;
[0047] (2) Preparation of the absorbent layer: use 40mm 3D viscose fiber and 40mm 2D polypropylene fiber with a ratio of 95% viscose: 5% polypropylene, and they are carded into a net, needle punched reinforcement, and mechanically beaten. The holes are made into needle-punched non-woven fabrics to form an absorbent layer. This layer is composed of upper and lower sheets. After needle punching, the upper sheet undergoes a subsequent punching process. The open...
Example Embodiment
[0051] Example 3
[0052] The woven fabric, needle-punched fabric, and film are stitched to form an adult mild incontinence pad. The specific process is:
[0053] (1) Preparation of the guide layer: using spinning technology to spin 40mm 5D polyester fibers into yarns, using weaving technology to make warp yarns with a fineness of 75D and weft yarns with a fineness of 60D into a warp density of 100 A woven fabric with a root / 10cm and a weft density of 90 roots / 10cm, forming a diversion layer, with an areal density of 37g / m 2 ;
[0054] (2) Preparation of the absorbent layer: use 40mm 3D viscose fiber and 40mm 2D polypropylene fiber with a ratio of 95% viscose: 5% polypropylene, and they are carded into a net, needle punched reinforcement, and mechanically beaten. The holes are made into needle-punched non-woven fabrics to form an absorbent layer. This layer is composed of upper and lower sheets. After needle punching, the upper sheet undergoes a subsequent punching process. The open...
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Areal density | aaaaa | aaaaa |
Areal density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap