Manufacturing method of sponge water permeable brick with graphic marble

A technology of permeable bricks and marbles, applied in the field of building materials, can solve the problems of restricting the application range of sponge permeable bricks, low hardness of sponge permeable bricks, and cannot be used in high-end places, etc. Effect

Inactive Publication Date: 2018-07-20
佛山生态海绵城市科技发展有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the existing sponge permeable bricks only pay attention to the water permeability and do not pay attention to their appearance, so they can only be applied to street pavements, and cannot be applied to high-end places with specific water permeability requirements, which restricts the scope of application of sponge permeable bricks
On the other hand, the hardness of existing sponge permeable bricks is not high, not wear-resistant, not durable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] A preparation method of a sponge permeable brick with marble texture, comprising,

[0031] Steps of raw material pretreatment: the sponge permeable brick is processed from waste ceramic tiles, binders, and fluxes, and the waste ceramic tiles in the formula are crushed into spherical or olive-shaped particles; in the prior art, machine shearing is used to The raw materials are processed and pulverized to prepare raw materials. The processed raw materials are microscopically shaped like flakes. When microscopically piled together, the gap between the raw materials is large, the number of particles is small, and the surface is shaped like a plate. When inkjet, the glaze Lacks a point of attachment so is more difficult to stay and difficult to color. To change the raw material processing method in the existing technology, the raw material is now placed in the grinding container, driven by a motor to rotate at a high speed, and the raw material collides with the container wa...

Embodiment 1

[0047] A method for preparing a marble-textured sponge permeable brick. The sponge permeable brick is processed from the following components in parts by weight: 92 parts of waste tiles, 5 parts of binder, and 3 parts of flux.

[0048] The preparation method is as follows:

[0049] The steps of raw material pretreatment: crush the waste tiles of the formula into spherical or olive-shaped particles; the sponge permeable brick embryo is composed of the bottom layer and the surface layer covering the upper surface of the bottom layer; the mesh number of the bottom layer waste tile powder is as follows: 10- 65 parts of 16-mesh waste tile powder, 25 parts of 16-30 mesh waste tile powder; the mesh numbers of surface layer waste tile powder are as follows: 45 parts of 4-10 mesh waste tile powder, 25 parts of 10-16 mesh waste tile powder, 10- 15 parts of 30 purpose waste tile powder.

[0050] The step of pressing and forming: the crushed waste tile powder is mixed with binder and flu...

Embodiment 2

[0058] A method for preparing a marble-textured sponge permeable brick. The sponge permeable brick is processed from the following components in parts by weight: 92 parts of waste tiles, 5 parts of binder, and 3 parts of flux.

[0059] The preparation method is as follows:

[0060] The steps of raw material pretreatment: crush the waste tiles of the formula into spherical or olive-shaped particles; the sponge permeable brick is composed of the bottom layer and the surface layer covering the upper surface of the bottom layer; the mesh number of the bottom layer waste tile powder is as follows: 10-16 70 parts of waste tile powder for purpose, 30 parts of waste tile powder for 16-30 mesh; the mesh numbers of waste tile powder for the surface layer are as follows: 50 parts of waste tile powder for Purpose 20 parts of waste tile powder.

[0061] The step of pressing and forming: the crushed waste tile powder is mixed with binder and flux, placed in a press, and pressed under the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a manufacturing method of a sponge water permeable brick with graphic marble. The method comprises the steps of preprocessing raw materials, pressing and forming, drying, coating a blank and dedusting, coating with protecting glaze, and sintering and forming to obtain the sponge water permeable brick with the graphic marble. According to the method, a layer of protecting glaze is coated on the surface of the sponge water permeable brick, so that the glaze effect of the graphic marble is obtained by improving the glaze coating manner, the appearance of an existing spongewater permeable brick is improved, and the sponge water permeable brick with the graphic marble is obtained, and moreover, the protecting glaze on the surface of the sponge water permeable brick is high in hardness, high in corrosion durability relative to the blank.

Description

technical field [0001] The invention relates to a building material technology, in particular to a method for preparing a marble-textured sponge permeable brick. Background technique [0002] Sponge permeable brick is a kind of porous permeable brick made by mixing aggregate, admixture, water, etc. through a specific process. Its surface forms a honeycomb structure with uniform distribution of holes, and its interior contains a large proportion of through-holes. It is breathable, water permeable and light in weight. Sponge permeable bricks play a huge role in the protection of groundwater resources, sound absorption and noise reduction, improvement of urban thermal environment, improvement of urban surface soil ecological environment, water purification and surface runoff relief. [0003] However, the existing sponge permeable bricks only pay attention to the water permeability and do not pay attention to their appearance, so they can only be applied to street pavements, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/132C04B41/89C03C8/14
CPCC03C8/14C04B33/1324C04B33/1328C04B41/009C04B41/52C04B41/89C04B2235/963C04B41/4572C04B41/5022C04B41/4543Y02P40/60
Inventor 范国雄周伟军
Owner 佛山生态海绵城市科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products