A kind of slow and controlled oxygen release microsphere and its preparation method and application

A technology of microspheres and oxygen release, applied in microcapsules, pharmaceutical formulations, prostheses, etc., can solve the problems of large volume of oxygen release materials, complicated preparation process, and uncontrollable oxygen release, achieving great application prospects and simple preparation process , the effect of long oxygen release time

Active Publication Date: 2020-06-02
SOUTHERN MEDICAL UNIVERSITY
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This problem has attracted the attention of some scholars. At present, it has been reported to add oxygen-releasing agents to tissue engineering materials, but the oxygen-releasing time period is short (most reports are several hours to several days).
Oxygen release in such a short time is very likely to cause high concentration of oxygen and cause cellular oxygen poisoning
Although there are currently reports of oxygen-releasing materials used in tissue engineering; however, they all have certain defects, such as short oxygen release time, high burst release rate, uncontrollable oxygen release, complicated preparation process, and large volume of oxygen-releasing materials.
At present, there is still no effective solution for the above shortcomings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of slow and controlled oxygen release microsphere and its preparation method and application
  • A kind of slow and controlled oxygen release microsphere and its preparation method and application
  • A kind of slow and controlled oxygen release microsphere and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0083] Example 1 Preparation of oxygen-releasing microspheres

[0084] 1) Preparation of gelatin solution: prepare a gelatin solution with a concentration of 0.8g / ml, the specific method is as follows:

[0085] ①Weigh 8g of gelatin into a beaker, then add 10ml of PBS, place on a magnetic stirrer and stir at 500rpm for about 5min;

[0086] ②Seal ① with a disposable sterile sealing film, place at 54°C to fully dissolve the gelatin in PBS (50min), and set aside;

[0087] Preparation of nanofiber film: prepare a hexafluoroisopropanol solution of collagen powder, and make the solution into a nanofiber film for in vivo experiments;

[0088] 2) Preparation of liquid paraffin dispersed phase: the specific method is as follows:

[0089] ①Preheat the liquid paraffin at 54°C for 1 hour;

[0090] ② Take 100ml into a 250ml beaker, put it on a heating magnetic stirrer (54°C), stir at 1500rpm, add 1ml of emulsifier Span80 at the same time, keep stirring, and fully emulsify for 20min;

[...

Embodiment 2

[0101] Example 2 Preparation of oxygen-releasing microspheres

[0102] 1) Preparation of gelatin solution: prepare a gelatin solution with a concentration of 0.8g / ml, the specific method is as follows:

[0103] ①Weigh 8g of gelatin into a beaker, then add 10ml of PBS, place on a magnetic stirrer and stir at 500rpm for about 5min;

[0104] ②Seal ① with a disposable sterile sealing film, place at 54°C to fully dissolve the gelatin in PBS (50min), and set aside;

[0105] Preparation of nanofiber film: prepare a hexafluoroisopropanol solution of collagen powder, and make the solution into a nanofiber film for in vivo experiments;

[0106] 2) Preparation of liquid paraffin dispersed phase: the specific method is as follows:

[0107] ①Preheat the liquid paraffin at 54°C for 1 hour;

[0108] ② Take 100ml into a 250ml beaker, place it on a heating magnetic stirrer (54°C), stir at 1000rpm, add 1ml emulsifier Span80 at the same time, keep stirring, and fully emulsify for 20min;

[0...

Embodiment 3

[0119] Example 3 Preparation of oxygen-releasing microspheres

[0120] 1) Preparation of gelatin solution: prepare a gelatin solution with a concentration of 0.8g / ml, the specific method is as follows:

[0121] ①Weigh 8g of gelatin into a beaker, then add 10ml of PBS, place on a magnetic stirrer and stir at 500rpm for about 5min;

[0122] ②Seal ① with a disposable sterile sealing film, place at 54°C to fully dissolve the gelatin in PBS (50min), and set aside;

[0123] Preparation of nanofiber film: prepare a hexafluoroisopropanol solution of collagen powder, and make the solution into a nanofiber film for in vivo experiments;

[0124] 2) Preparation of liquid paraffin dispersed phase: the specific method is as follows:

[0125] ①Preheat the liquid paraffin at 54°C for 1 hour;

[0126] ② Take 100ml into a 250ml beaker, place it on a heating magnetic stirrer (54°C), stir at 500rpm, add 1ml of emulsifier Span80 at the same time, keep stirring, and fully emulsify for 20min;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sustained-release oxygen microsphere as well as a preparation method and application thereof. The sustained-release oxygen microsphere is a microsphere using gelatin as a matrix; the interior of the microsphere contains peroxidated inorganic particles, and preferably, the peroxidated inorganic particles are selected from one or multiple of CaO2 (calcium peroxide), MgO2 (magnesium peroxide), NaCO3 (sodium carbonate), SrO2 (strontium peroxide), BaO2 (barium peroxide), K2O2 (potassium peroxide), and Na2O2 (sodium peroxide). The sustained-release oxygen microsphere has the advantages that the size is controllable, the oxygen release time is long and controllable, the sudden release rate is low, the cell toxicity is low, the immunogenicity is low, the preparation process is relatively simple, the industrialized production is easily realized, and the like; the larger application prospect is realized in clinical application of bone defect repair.

Description

technical field [0001] The invention belongs to the field of preparation of bone engineering artificial slow-release materials, in particular to a gelatin composite CaO 2 The preparation method of the constructed controllable oxygen release type tissue engineering material. Background technique [0002] As we all know, some small bone defects in the human body can be repaired by themselves, but large bone defects caused by bone tumor resection, traumatic massive bone loss, osteonecrosis, bone metabolic diseases, etc. cannot be repaired by themselves and require human intervention. At present, large bone defects can be repaired by bone tissue engineering and bone grafting. Among them, bone transplantation includes autograft, allograft, and xenograft, but they all have their own obvious disadvantages, such as the possibility of disease transmission, lack of tissue that can be used for autologous transplantation, and donors with high disease risk. risk etc. In recent years, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/44A61L27/58A61L27/50
CPCA61L27/446A61L27/50A61L27/58A61L2300/622A61L2430/02C08L89/00
Inventor 朱立新张志明王一涵郭家松
Owner SOUTHERN MEDICAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com