Inert glass bead explosion-proof heat-insulation paint

A technology of vitrified microbeads and thermal insulation coatings, which is applied in fire-resistant coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problem of heavy weight of foamed cement composite panels, unsatisfactory structural strength, and restrictions on prefabricated houses. Application and other issues, to achieve the effect of good flame retardant and anti-knock performance, good fire resistance and freeze-thaw cycle resistance, and excellent combustion growth rate index

Inactive Publication Date: 2018-08-21
GRAND FACADE DECORATION ENG CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if the prefabricated house is applied to outdoor camping, the foamed cement composite board is heavy and inconvenient to carry, which limits the application of the prefabricated house outdoors.
If insulation boards (such as polyurethane insulation boards, phenolic insulation boards, etc.) are used to assemble outdoor houses, their structural strength cannot meet the requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inert glass bead explosion-proof heat-insulation paint
  • Inert glass bead explosion-proof heat-insulation paint
  • Inert glass bead explosion-proof heat-insulation paint

Examples

Experimental program
Comparison scheme
Effect test

preparation example 1

[0024] After stirring 100g of isophorone diisocyanate and 30g of polypropylene glycol at 30°C for 1 hour, add 15g of amino-terminated polyether D2000 and 0.1g of isopropanol, and react at 30°C for 0.75 hours to obtain polyurea prepolymer.

preparation example 2

[0026] After stirring 100g of isophorone diisocyanate and 35g of polypropylene glycol at 35°C for 0.5 hours, add 12g of amino-terminated polyether D3500 and 0.5g of isopropanol, and keep warm at 35°C for 0.5 hours to obtain polyurea prepolymer.

preparation example 3

[0028] After stirring 100g of isophorone diisocyanate and 40g of polypropylene glycol at 32°C for 0.75 hours, add 10g of amino-terminated polyether D5000 and 0.3g of isopropanol, and keep warm at 32°C for 1 hour to obtain polyurea prepolymer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an inert glass bead explosion-proof heat-insulation paint. The inert glass bead explosion-proof heat-insulation paint comprises a component A and a component B at a weight ratio of 50-60:10-15; the component A comprises, by weight, 50 to 60 parts of a polyurea performed polymer, 5 to 10 parts of polyurethane gel, 8 to 15 parts of hollow glass bead, and 10 to 15 parts of afire retardant; and the component B comprises, by weight, 20 to 30 parts of a diamine chain extender, and 25 to 35 parts of a solvent. The inert glass bead explosion-proof heat-insulation paint possesses excellent fire resistance and freezing and thawing resistance, is capable of providing thermal insulation boards coated with the inert glass bead explosion-proof heat-insulation paint with relatively high compressive strength, and relatively excellent heat insulation performance, flame resistance, and explosion resistance.

Description

technical field [0001] The invention relates to the technical field of architectural coatings, in particular to an explosion-proof and heat-insulating coating of inert vitrified microbeads. Background technique [0002] Prefabricated buildings refer to buildings assembled on site with prefabricated components. The prefabricated concrete components of this type of building are mainly composed of post-cast concrete, grout anchors or superimposed methods at the joints. The assembled integral concrete structure has reliability. The force transmission structure and meet the bearing requirements. In urban construction, there are more and more prefabricated buildings. Assembled structural components are industrially produced, and the quality of components is easy to guarantee. The on-site construction is simple and fast, and there is less construction waste, which greatly improves the efficiency of housing construction. In the process of urbanization, prefabricated structures adva...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/02C09D133/24C09D5/18C09D7/61C09D7/65C08G18/50C08G18/48C08G18/12C08G18/32C08F220/54C08F222/38
CPCC08F220/54C08G18/12C08G18/482C08G18/5021C08L2201/02C09D5/18C09D175/02C09D7/65C09D7/70C08F222/385C08G18/3234C08G18/3857C08L33/24C08K7/28C08K5/5477
Inventor 冯华国
Owner GRAND FACADE DECORATION ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products