Plastic formula with high rate of finished products

A high-yield, plastic technology, applied in the field of plastic materials, can solve the problems of low yield and achieve the effects of high yield, excellent performance and low price

Inactive Publication Date: 2018-08-28
XUZHOU CURRENCY MAGNETOELECTRICITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a plastic formula with high yield in view of the above problems, so as to overcome the defects of low yield in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: A plastic formulation with high yield, comprising the following components by weight: 88 parts of polypropylene, 1.5 parts of stannous octoate, 1 part of monomer resin, 6.2 parts of calcium carbonate, 1.5 parts of preservative, plasticizer 1 part, 1.1 parts of aluminum oxide powder, and 1.3 parts of magnesium stearate; the above-mentioned raw materials are fully mixed, and then put into an injection molding machine for die-casting.

Embodiment 2

[0013] Embodiment 2: A kind of plastic formulation with high yield, comprising the following ingredients in parts by weight: 69 parts of polypropylene, 1.3 parts of stannous octoate, 0.2 parts of monomer resin, 5 parts of calcium carbonate, 1.3 parts of preservative, plasticizer 0.2 parts, 1.1 parts of aluminum oxide powder, and 1.3 parts of magnesium stearate; the above-mentioned raw materials are fully mixed, and then put into an injection molding machine for die-casting.

Embodiment 3

[0014] Embodiment 3: A kind of plastic formulation with high yield, including the following ingredients in parts by weight: 77 parts of polypropylene, 1.4 parts of stannous octoate, 0.75 parts of monomer resin, 5.8 parts of calcium carbonate, 1.4 parts of preservative, plasticizer 0.7 parts, 1.1 parts of aluminum oxide powder, and 1.3 parts of magnesium stearate; the above-mentioned raw materials are fully mixed, and then put into an injection molding machine for die-casting.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a plastic formula with high rate of finished products. The plastic formula comprises the following components in parts by weight: 69-88 parts of polypropylene, 1.3-1.5 parts ofstannous octoate, 0.2-1 part of monomer resin, 5-6.2 parts of calcium carbonate, 1.3-1.5 parts of a preservative, 0.2-1 part of a plasticizer, 1.1 parts of an alumina powder and 1.3 parts of magnesium stearate; the raw materials are fully mixed and then put in an injection molding machine for die-cast molding. Compared with the prior art, the plastic formula disclosed by the invention has the advantages of being low in price, high in rate of finished products and excellent in performance.

Description

technical field [0001] The invention relates to the field of plastic materials, in particular to a plastic formula with high yield. Background technique [0002] Plastic is a high molecular compound polymerized by addition polymerization or polycondensation reaction with monomer as raw material. It is commonly known as plastic or resin. It can freely change its composition and shape. , Colorants and other additives. The main component of plastic is resin. The term resin was originally named after the lipids secreted by animals and plants, such as rosin, shellac, etc. Resin refers to a polymer compound that has not been mixed with various additives. Resin accounts for about 40% to 100% of the total weight of the plastic. The existing plastic yield is low. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a plastic formula with high yield in order to overcome the defect of low yield in the prior art. [0004] In...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08K13/02C08K5/098C08K3/26C08K3/22
CPCC08K13/02C08K3/22C08K3/26C08K5/098C08K2003/2227C08K2003/265C08K2201/014C08L23/12
Inventor 高坤
Owner XUZHOU CURRENCY MAGNETOELECTRICITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products