Silicone protective cover with good thermal conductivity

A protective cover and thermal conductivity technology, applied in the field of electronic product accessories, can solve the problems of easy aging, high production cost, poor thermal conductivity of silicone material, etc., to achieve improved heat resistance and thermal conductivity, improved electrical conductivity, and improved protection. Effect

Inactive Publication Date: 2018-08-31
HEFEI ZEJUN ELECTRICAL EQUIP CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] These fall-proof protective covers are mainly made of metal, silicone and plastic. Among them, the metal material has a good protective effect, but the texture is poor and the production cost is also high.
The degree of plastic material is low and the protection is good, but it is easy to age
Silicone material has good elasticity, the best anti-dr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A silica gel protective cover with good thermal conductivity. According to the mass parts, the silica gel used for the protective cover is prepared from the following raw materials: 100 parts of silicone rubber, 10 parts of vinyl silicone oil, 5 parts of hydroxyl silicone oil, 0.4 parts of catalyst, polydimethyl 2 parts of siloxane, 3 parts of zinc stearate, 16 parts of aluminum oxide powder, 4 parts of copper powder, and 1 part of coupling agent.

[0022] The silicone rubber is dimethyl silicone rubber; the catalyst is a platinum complex catalyst; the mesh number of the copper powder is 200 mesh.

[0023] The alumina powder has been modified. The modification process is as follows: dissolve the silane coupling agent in the ethanol solvent, then add the alumina powder into the solution and mix evenly. Stir at a rotating speed for 15 minutes, and then dry to obtain the desired modified alumina powder, the mesh number of which is 250 mesh.

[0024] The preparation method...

Embodiment 2

[0029] A silicone protective cover with good thermal conductivity. According to the mass parts, the silicone rubber used for the protective cover is prepared from the following raw materials: 120 parts of silicone rubber, 13 parts of vinyl silicone oil, 8 parts of hydroxyl silicone oil, 0.7 parts of catalyst, polydimethyl 4 parts of siloxane, 4 parts of zinc stearate, 19 parts of aluminum oxide powder, 8 parts of copper powder, and 2 parts of coupling agent.

[0030] Fluorosilicone rubber is used as the silicone rubber; the catalyst is a platinum complex catalyst; the mesh number of the copper powder is 250 mesh.

[0031] The alumina powder has been modified. The modification process is: dissolve the silane coupling agent in the ethanol solvent, then add the alumina powder into the solution and mix evenly. Stir at a rotating speed for 20 minutes, and then dry to obtain the desired modified alumina powder, the mesh number of which is 300 mesh.

[0032] The preparation method o...

Embodiment 3

[0037] A silica gel protective cover with good thermal conductivity. According to the mass parts, the silica gel used for the protective cover is prepared from the following raw materials: 110 parts of silicone rubber, 12 parts of vinyl silicone oil, 7 parts of hydroxyl silicone oil, 0.6 parts of catalyst, polydimethyl 3 parts of siloxane, 3.5 parts of zinc stearate, 17 parts of alumina powder, 6 parts of copper powder, and 1.5 parts of coupling agent.

[0038] The silicone rubber is methyl phenyl vinyl silicone rubber; the catalyst is platinum complex catalyst; the mesh number of copper powder is 230 mesh.

[0039] The alumina powder has been modified. The modification process is as follows: dissolve the silane coupling agent in the ethanol solvent, then add the alumina powder into the solution and mix evenly. Stir at a rotating speed for 18 minutes, and then dry to obtain the desired modified alumina powder. The mesh number of the alumina powder is 280 mesh.

[0040] The pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Meshaaaaaaaaaa
Meshaaaaaaaaaa
Meshaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of electronic product accessories, and particularly relates to a silicone protective cover with good thermal conductivity. The silicone protective cover isprepared from silicone rubber, vinyl silicone oil, hydroxyl silicone oil, catalyst, polydimethylsiloxane, zinc stearate, alumina powder, copper powder and coupling agent. The silicone rubber is selected from one of dimethyl silicone rubber, fluorosilicone rubber and methyl phenyl vinyl silicone rubber; the catalyst is a platinum complex catalyst; alumina is modified by an ethanol solution of a silane coupling agent. The silicone protective cover has better impact resistance, excellent protection performance, comfortable touch feeling and improved thermal conductivity.

Description

technical field [0001] The invention belongs to the technical field of electronic product accessories, and in particular relates to a silica gel protective cover with good thermal conductivity. Background technique [0002] Today's electronic products such as mobile phones, tablet computers, and notebook computers are getting better and better in performance and have more and more functions. We can handle various problems such as office, entertainment, and shopping on these products. However, with the improvement of product performance, the precision of equipment parts is also increasing geometrically, so the protection requirements of these electronic products are also getting higher and higher. In order to improve the anti-drop and impact resistance, most users will equip these electronic products with protective cases or cases. [0003] These fall-proof protective covers are mainly made of metal, silicone and plastic. Among them, the metal material has a good protective ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/04C08L83/08C08L83/07C08K13/06C08K9/06C08K3/22C08K5/098C08K3/08
CPCC08K2003/085C08K2003/2227C08K2201/001C08K2201/005C08L83/04C08L83/08C08L2201/04C08L2205/02C08L2205/025C08L2205/035C08K13/06C08K9/06C08K3/22C08K5/098C08K3/08
Inventor 徐仙峰
Owner HEFEI ZEJUN ELECTRICAL EQUIP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap