A kind of incense ash mixed material and incense ash product

A technology of mixed materials and incense ash, which is applied in the field of incense ash mixed materials and incense ash products, which can solve problems such as unsanitary, stability of incense ash products, and poor oxidation resistance, and achieve strong oxidation resistance, stable physical and chemical properties, and improved dispersibility Effect

Active Publication Date: 2020-07-10
衡阳市南岳区圣土文化发展有限责任公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The incense ash products prepared by the above method have poor stability and oxidation resistance, and carry a large number of bacteria from incense ash, which is extremely unhygienic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of incense ash mixed material, calculated by weight percentage, is prepared from the following raw materials:

[0025] Ash 40wt%;

[0026] Bamboo charcoal granules 15wt %;

[0027] Adhesive composition 45wt%.

[0028] The particle size of the bamboo charcoal particles is 80 meshes, and the preparation method of the incense ash mixed material comprises the following steps: washing the incense ash with water, drying, mixing with the bamboo charcoal particles, adding an adhesive composition, stirring evenly, and drying in the shade.

[0029] In parts by weight, the raw materials for preparing the adhesive composition are as follows: 35 parts of polyamide resin, 30 parts of butanol, 5 parts of xanthan gum, 2 parts of titanium dioxide, 10 parts of 10wt% zinc sulfate solution, 10 parts of bentonite, paraffin wax 10 parts, 50 parts cement, 100 parts water.

[0030] The method for preparing adhesive composition comprises the following steps:

[0031] a. Dissolve the ...

Embodiment 2

[0035] A kind of incense ash mixed material, calculated by weight percentage, is prepared from the following raw materials:

[0036] Incense ash 55wt%;

[0037] Bamboo charcoal granules 10wt %;

[0038] Adhesive composition 35wt%.

[0039] The particle size of the bamboo charcoal particles is 200 mesh, and the preparation method of the incense ash mixed material comprises the following steps: washing the incense ash with water, drying, mixing with the bamboo charcoal particles, adding an adhesive composition, stirring evenly, and drying in the shade.

[0040] In parts by weight, the raw materials for preparing the adhesive composition are as follows: 50 parts of polyamide resin, 45 parts of butanol, 7 parts of xanthan gum, 5 parts of titanium dioxide, 15 parts of 10wt% zinc sulfate solution, 20 parts of bentonite, paraffin wax 20 parts, 60 parts of cement, 150 parts of water.

[0041] The method for preparing adhesive composition comprises the following steps:

[0042] a. ...

Embodiment 3

[0046] A kind of incense ash mixed material, calculated by weight percentage, is prepared from the following raw materials:

[0047] Incense ash 50wt%;

[0048] Bamboo charcoal granules 12wt %;

[0049] Adhesive composition 38wt%.

[0050] The particle size of the bamboo charcoal granule is 140 meshes. The preparation method of the incense ash mixed material comprises the following steps: washing the incense ash with water, drying, mixing with the bamboo charcoal granules, adding an adhesive composition, stirring evenly and drying in the shade.

[0051] In parts by weight, the raw materials for preparing the adhesive composition are as follows: 42 parts of polyamide resin, 37 parts of butanol, 6 parts of xanthan gum, 3 parts of titanium dioxide, 12 parts of 10wt% zinc sulfate solution, 15 parts of bentonite, paraffin wax 15 parts, 55 parts cement, 125 parts water.

[0052] The method for preparing adhesive composition comprises the following steps:

[0053] a. Dissolve the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to an incense ash mixed material. The incense ash mixed material is prepared from, by weight, 40-55% of incense ash, 10-15% of bamboo charcoal granules and 30-45% of adhesive composition, wherein the particle size of the bamboo charcoal particles is 80-200 mesh. A preparation method of the incense ash mixed material comprises the following steps that the incense ash is washedwith water, dried and mixed with the bamboo charcoal granules, then the adhesive composition is added and evenly stirred, the mixture is dried in the shade, and the incense ash mixed material is obtained. A preparation method of the adhesive composition includes the following steps that a, polyamide resin is dissolved in butanol, and then the mixture is heated to 50-60 DEG C to obtain a solutionA; b, xanthan gum and titanium dioxide powder are added into a zinc sulfate solution in sequence, and the pH value is adjusted to be 8.5-9.2 to obtain a solution B; c, bentonite, paraffin and cement are mixed, water is added for uniform mixing, then the solution A and the solution B continue to be added and stirred for 1-1.5 h, and the adhesive composition is obtained. The incense ash mixed material is relatively stable in physical and chemical property and relatively high in antioxidant capacity, the number of bacteria carried by the incense ash is small, and the incense ash mixed material isclean and sanitary and is suitable for making various Buddha-related products to promote and develop broad and profound Buddhist culture.

Description

technical field [0001] The invention relates to an incense ash mixture material, in particular to an incense ash mixture material and an incense ash product. Background technique [0002] As an extremely important part of the five thousand years of Chinese culture, Buddhist culture has been integrated into the lives of Chinese people, subtly affecting people's lives, and the incense burner culture is an important part of Buddhist culture. Take Nanyue, which has a high Buddhist cultural background, as an example. During major religious festivals, the amount of incense ash in the temple of Nanyue increases sharply, sometimes as much as 240 tons a day. [0003] In general, incense ash is usually mixed with household garbage and dumped to the garbage dump, which not only pollutes the environment, but also easily deposits at the bottom of household garbage, thereby blocking the underground water pipes of the garbage dump and causing poor drainage. [0004] In order to deal with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/00
CPCC04B28/00C04B24/287C04B24/026C04B24/38C04B14/305C04B22/142C04B14/104C04B24/36C04B18/10C04B14/022
Inventor 旷新文
Owner 衡阳市南岳区圣土文化发展有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products