Emulsion for preparing facial mask and preparation method thereof

A technology of emulsion and facial mask, applied in the field of preparation of facial mask emulsion and its preparation, can solve the problems of complex formula, graphene facial mask cannot meet the needs of customers with different face shapes, complicated operation, etc., and achieves the promotion of cell proliferation, good biocompatibility, The effect of good film formation

Inactive Publication Date: 2018-09-25
SICHUAN UNIV
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is: in order to solve the problem that the existing graphene facial mask cannot meet the needs of customers with different face shapes, and the formula is complex and complicated to operate, the present invention provides an emulsion for preparing a facial mask and a preparation method thereof , by compounding graphene with a polymer emulsion with good biocompatibility, the mask emulsion not only has good biocompatibility, but also has antibacterial properties and excellent functions of promoting cell proliferation and anti-aging

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] A preparation method for the emulsion of facial mask, comprises the following steps:

[0027] a. Dispersion of graphene, graphene is added to deionized water, and a uniform graphene dispersion is obtained by ultrasonic dispersion;

[0028] b. Mixing of the graphene dispersion and the polymer emulsion, adding the graphene dispersion into the polymer emulsion for ultrasonic stirring to obtain a uniformly dispersed graphene and polymer emulsion.

[0029] Specifically, the ultrasonic time of the graphene in deionized water is 30-60 min, and the temperature is 10-35°C. The ultrasonic stirring time of the graphene dispersion liquid and the polymer emulsion is 30min, and the temperature is 20-30°C.

Embodiment 1

[0031] A kind of parts by weight of raw materials in the emulsion for preparing facial mask: 0.01 part of graphene, 50 parts of polymer emulsion, 0.01 part of perfume.

[0032] The spice is honey.

[0033] The preparation method of the emulsion used to prepare the facial mask comprises the following steps: (1) homogenization of the polymer emulsion; weighing a certain quality of the polymer emulsion, and emulsifying it for 30 minutes under an emulsifier to make the emulsion more uniform. (2) Purification of graphene: Weigh a certain mass of graphene and ultrasonically disperse it in water, and centrifuge and wash it three times to obtain purified graphene. (3) Dispersion of graphene / polymer emulsion: add a certain quality of purified graphene into the polymer emulsion, and disperse for 60 minutes under ultrasonic, so that the graphene is uniformly dispersed in the emulsion. (4) At room temperature, add the remaining components and stir evenly with a mixer.

Embodiment 2

[0035] A kind of parts by weight of raw materials in the emulsion for preparing facial mask: 0.1 part of graphene, 45 parts of aqueous polymer emulsion, 0.05 part of perfume.

[0036] The spice is peppermint.

[0037] The preparation method of the emulsion used to prepare the facial mask comprises the following steps: (1) homogenization of the polymer emulsion; weighing a certain quality of the water-based polymer emulsion, and stirring it for 30 minutes under a mixer to make the emulsion more uniform. (2) Purification of graphene: Weigh a certain mass of graphene and ultrasonically disperse it in water, and centrifuge and wash it three times to obtain purified graphene. (3) Dispersion of graphene / polymer emulsion: add a certain quality of purified graphene oxide into the polymer emulsion, and disperse in ultrasonic for 60 minutes, so that the graphene is uniformly dispersed in the emulsion. (4) At room temperature, add the remaining components and disperse evenly with an emu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of a facial mask, in particular to emulsion for preparing a facial mask and a preparation method thereof. The emulsion for preparing the facial mask is prepared fromthe following raw materials in parts by weight: 0.01 part of graphene, 50 parts of macromolecule emulsion and 0.01 part of spice. The graphene and the macromolecule emulsion with good biocompatibility are compounded; the facial mask emulsion has good biocompatibility and antibacterial performance, and also has the excellent functions of promoting cell multiplication and resisting the senility. The macromolecule emulsion uses water as a solvent and can be directly coated and applied on the skin; good film formation performance is realized; the excellent characteristics of conciseness, convenience and safety are realized; meanwhile, due to the characteristic that the emulsion can be directly coated and applied on the skin for film formation, the shape can be designed by self according to user requirements; the user requirements are met.

Description

technical field [0001] The invention relates to the field of facial masks, in particular to an emulsion for preparing facial masks and a preparation method thereof. Background technique [0002] Macromolecules are a class of macromolecules composed of a series of different structural units. Different structures determine different properties of polymer materials. Among them, polymer materials such as polyurethane and polydimethylsiloxane have been widely used in the field of biomedical materials due to their good mechanical properties and biocompatibility. . [0003] Graphene is a honeycomb-like two-dimensional (2D) material that is densely packed with single-atom-thick carbon atoms. It has good mechanical, thermal, and electrical properties, making it widely used. Graphene, as a kind of derivative of graphene, has a large number of carboxyl groups, hydroxyl groups and other hydrophilic groups on its surface, so that it can be stably dispersed in water and form a stable an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61K8/19A61K8/06A61Q19/00A61Q19/08
CPCA61K8/19A61K8/06A61Q19/00A61Q19/08
Inventor 夏和生蹇志文
Owner SICHUAN UNIV