Heat treatment method for solid electrolyte thin film and lithium core structure

A technology of solid electrolyte and heat treatment method, applied in non-aqueous electrolyte battery, electrolyte battery manufacturing, electrolyte and other directions, can solve the problems of electrode material capacity retention rate and structural stability reduction, etc., to reduce the influence of stability, high ratio Effect of capacity and high charge-discharge cycle performance

Active Publication Date: 2018-09-25
成都大超科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the current problem that the capacity retention rate and structural stability of the electrode material are reduced when the solid electrolyte film is heated, the present invention provides a lithium battery that can realize rapid heat treatment of the solid electrolyte film and maintain the conductivity of the electrode material well. Heat treatment method for battery solid electrolyte film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat treatment method for solid electrolyte thin film and lithium core structure
  • Heat treatment method for solid electrolyte thin film and lithium core structure
  • Heat treatment method for solid electrolyte thin film and lithium core structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0046] In order to make the purpose, technical solutions and advantages of the present invention more clear, the present invention will be further described in detail below in conjunction with the accompanying drawings and implementation examples. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0047] see figure 1 , the first embodiment of the present invention provides a heat treatment method of a solid electrolyte film, the heat treatment method of the solid electrolyte film includes the following steps:

[0048] S1: providing a solid electrolyte film to be processed with a certain thickness, the solid electrolyte film to be processed is formed on the electrode structure;

[0049] S2: using a pulse light source with specific pulse parameters to heat-treat the solid electrolyte film for a predetermined time;

[0050] S3: cooling the heat-treated solid electrolyte film....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical conductivityaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of lithium batteries, and provides a heat treatment method for a solid electrolyte thin film and a lithium core structure. The heat treatment method for the solid electrolyte thin film comprises the following steps: providing a to-be-treated solid electrolyte thin film with a certain thickness, wherein the to-be-treated solid electrolyte thin film is formed on an electrode structure; carrying out heat treatment on the to-be-treated solid electrolyte thin film by using a pulse light source with specific pulse parameters for a preset time; and coolingthe solid electrolyte thin film after the solid electrolyte thin film is subjected to heat treatment. The to-be-treated solid electrolyte thin film is subjected to heat treatment by the pulse light source with the specific pulse parameter, the to-be-treated solid electrolyte thin film has good absorption performance on photons transmitted from the pulse light source, the temperature of the to-be-treated solid electrolyte thin film is increased, therefore, the crystalline phase structure of the to-be-treated solid electrolyte thin film is changed, then the bulk phase and the grain boundary resistance of the solid electrolyte thin film are changed to improve the conduction property of conductive ions on the solid electrolyte thin film after the solid electrolyte thin film is subjected to heat treatment, and the electric conduction property is improved.

Description

【Technical field】 [0001] The invention relates to the technical field of lithium batteries, in particular to a heat treatment method for a solid electrolyte film and a lithium battery core structure. 【Background technique】 [0002] In the process of preparing lithium batteries, it is necessary to treat the solid electrolyte film according to actual needs. Among them, the heat treatment technology can change the characteristics of the solid electrolyte film, reduce the grain boundary impedance of the solid electrolyte film, thereby improving the conduction of conductive lithium ions; secondly, the heat treatment technology can also improve the interface contact performance between the solid electrolyte film and the electrode. Improve and reduce interface impedance, thereby improving battery performance. [0003] The existing technology mainly uses a heater to heat the solid electrolyte film. Due to the uncontrollability of the heating process, it is easy to have a great impa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/0562H01M10/058
CPCH01M10/0562H01M10/058H01M2300/0071Y02E60/10Y02P70/50
Inventor 张晓琨
Owner 成都大超科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products