Glass of novel thermometer for livestock

A thermometer, a new type of technology, applied in thermometers, thermometers based on the expansion/contraction of materials, measuring devices, etc., can solve problems such as imperfect glass performance, achieve enhanced rheology and surface activity, improve corrosion resistance, enhance resistance The effect of abrasiveness and corrosion resistance

Inactive Publication Date: 2018-09-28
董子强
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, veterinary thermometers have very high requirements on the performance of glass. The glass used must have good toughness and corrosion resistance, but the performance of existing glass is not perfect enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass of novel thermometer for livestock

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A glass used for a new type of veterinary thermometer is made of the following components in parts by weight: 430 parts of quartz sand, 15 parts of limestone, 13 parts of feldspar, 4 parts of soda ash, 3 parts of boric acid and 63 parts of modified filler.

[0024] Further, the preparation of the modified filler comprises the following steps:

[0025] (1) Put sodium lauryl sulfate and sodium dioctyl succinate sulfonate in the reaction kettle at a weight ratio of 1:0.7, then add 95% ethanol to the reaction kettle, stir continuously, and then slowly drop Add 8 drops of 1g / mLd cerium chloride solution, and after continuing to stir for 25min, add steel fiber and silicate with a weight ratio of 1:3.4 in the reactor, and continue stirring for 40min to obtain material A for subsequent use;

[0026] (2) Add modifying liquid to the material A obtained in step (1), then place material A and modifying liquid together in a micro-jet homogenizer, and perform high-pressure micro-jet ...

Embodiment 2

[0036] A glass used for a new type of veterinary thermometer is made of the following components in parts by weight: 470 parts of quartz sand, 18 parts of limestone, 15 parts of feldspar, 6 parts of soda ash, 4 parts of boric acid and 66 parts of modified filler.

[0037] Further, the preparation of the modified filler comprises the following steps:

[0038] (1) Put sodium lauryl sulfate and sodium dioctyl succinate sulfonate in the reaction kettle at a weight ratio of 1:0.8, then add 95% ethanol to the reaction kettle, stir continuously, and then slowly drop Add 14 drops of 1g / mLd cerium chloride solution, after stirring for 30min, add steel fiber and silicate with a weight ratio of 1:3.6 in the reactor, and continue stirring for 43min to obtain material A for subsequent use;

[0039] (2) Add modifying liquid to the material A obtained in step (1), then place material A and modifying liquid together in a micro-jet homogenizer, and perform high-pressure micro-jet treatment for...

Embodiment 3

[0049] A glass used for a new type of veterinary thermometer is made of the following components in parts by weight: 510 parts of quartz sand, 21 parts of limestone, 17 parts of feldspar, 8 parts of soda ash, 5 parts of boric acid and 69 parts of modified filler.

[0050] Further, the preparation of the modified filler comprises the following steps:

[0051] (1) Put sodium lauryl sulfate and sodium dioctyl succinate sulfonate in a reaction kettle at a weight ratio of 1:0.9, then add 95% ethanol to the reaction kettle, stir continuously, and then slowly drop Add 20 drops of cerium chloride solution of 1g / mLd, after continuous stirring for 35min, add steel fiber and silicate with a weight ratio of 1: 3.8 in the reactor, continue stirring to obtain material A for subsequent use after 46min;

[0052] (2) Add modifying liquid to the material A obtained in step (1), and then place material A and modifying liquid together in a micro-jet homogenizer for high-pressure micro-jet treatme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides glass of a novel thermometer for livestock, and belongs to the technical field of glass processing treatment. The glass is prepared from, by weight, 430-510 parts of quartz sand, 15-21 parts of limestone, 13-17 parts of feldspar, 4-8 parts of sodium carbonate, 3-5 part of boric acid and 63-69 parts of modified filler. The finally prepared glass has the advantages that the comprehensive performance is high, the toughness is good, the molding is easy, the glass is not fragile, the compression resistance is high, the corrosion resistance is very good, the security coefficient of the thermometer can be improved when the glass is used for the novel thermometer for the livestock, the service life of the thermometer is prolonged, and the market promotion value is very high.

Description

technical field [0001] The invention belongs to the technical field of glass processing, and in particular relates to a glass used for a novel veterinary thermometer. Background technique [0002] Glass is formed by melting silica and other chemicals together. The earliest glass makers in the world were the ancient Egyptians. The emergence and use of glass has a history of more than 4,000 years in human life. From the remains of Mesopotamia and ancient Egypt 4,000 years ago, small glass beads have been unearthed. Glass is also indispensable in the lives of modern people, such as car windshields, smartphone screen glass, and building window glass. Although the performance of glass has been improved with the development of technology, most of the existing glasses still have shortcomings such as poor impact resistance and poor anti-corrosion performance, which need further improvement. [0003] Veterinary thermometers are different from those used by the human body. There ar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C6/08C03C1/02G01K5/04
CPCC03C1/00C03C1/026G01K5/04
Inventor 董子强
Owner 董子强
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com