A method for preparing the inner lining of a non-ringing pellet rotary kiln

A rotary kiln and pelletizing technology, applied in rotary drum furnace, process efficiency improvement, furnace and other directions, can solve the problems of difficult cleaning, hidden dangers, time-consuming and labor-intensive, etc.

Active Publication Date: 2020-10-27
SHANDONG LUMING HIGH TEMPERATURE MATERIAL TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Domestic ironmaking mostly uses pellets as raw materials, and iron ore powder needs to be pelletized into pellets and then roasted in a rotary kiln before being used. Due to the high content of impurities in iron ore powder and rotary kiln fuel, such as SiO 2 , CaO, Na 2 O, Fe 2 o 3 etc., often produce low-melt phase with the pellet lining refractory material at high temperature, and thus adhere to the surface of the rotary kiln lining refractory material to form a ring. As the ring becomes thicker and thicker, production will be affected, and the kiln needs to be stopped for ring cleaning. , because a large amount of iron ore powder is contained in the ring formation process, the ring is heavy, high in strength, difficult to clean, time-consuming and laborious, and has potential safety hazards. Therefore, there is an urgent need for a ring-resistant pellet rotary kiln lining refractory material to solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing the inner lining of a non-ringing pellet rotary kiln

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] The present invention will be further described in detail below in conjunction with specific embodiments.

[0039] A method for preparing the inner lining of a non-ringed pellet rotary kiln according to the present invention comprises the following steps:

[0040] (1) Weigh and prepare raw materials;

[0041] (2) Mix the prepared raw materials evenly, add water accounting for 3-6wt% of the total weight of the raw materials, and stir evenly in an environment with a normal temperature of 5-30 degrees Celsius;

[0042] (3) pour the mixed material mixed with water into the model to obtain the billet;

[0043] (4) Bake the blank at low temperature until it is shaped;

[0044] Wherein, the raw material described in the step (1) comprises the following components according to the parts by mass:

[0045] 10-20wt% of ferro-titanium industrial by-product particles with a particle size of 8-5mm;

[0046] 10-20wt% of ferro-titanium industrial by-product particles with a particl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method for a pellet rotary kiln lining without ring formation, belonging to the field of refractory materials. The preparation method is characterized by comprising the following steps: weighing of raw materials, mixing, water addition and stirring, pouring molding, and low-temperature firing until shaping is completed. The preparation method provided by theinvention fully utilizes titanium-iron alloy industrial by-products as raw materials, solves the problem of treatment of industrial solid wastes, realizes waste reutilization, and prepares a high-performance rotary kiln lining at the same time. The rotary kiln lining prepared by using the preparation method provided by the invention has the characteristics of good wear resistance and no ring formation, so the trouble of clearing rings in the process of application is solved, and production efficiency is improved.

Description

technical field [0001] The invention belongs to the field of preparation technology of refractory materials, and relates to a preparation method of anti-ringing pellet ore rotary kiln lining refractory materials. Background technique [0002] Domestic ironmaking mostly uses pellets as raw materials, and iron ore powder needs to be pelletized into pellets and then roasted in a rotary kiln before being used. Due to the high content of impurities in iron ore powder and rotary kiln fuel, such as SiO 2 , CaO, Na 2 O, Fe 2 o 3 etc., often produce low-melt phase with the pellet lining refractory material at high temperature, and thus adhere to the surface of the rotary kiln lining refractory material to form a ring. As the ring becomes thicker and thicker, production will be affected, and the kiln needs to be stopped for ring cleaning. , because a large amount of iron ore powder is contained in the ring formation process, the ring is heavy, high in strength, difficult to clean, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/101C22B1/216
CPCC04B35/1015C04B2235/3201C04B2235/3208C04B2235/3272C04B2235/447C04B2235/602C04B2235/96C22B1/216Y02P10/20
Inventor 傅修文王秀李畅周刚德
Owner SHANDONG LUMING HIGH TEMPERATURE MATERIAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products