Material for adjusting trace elements for aluminum of external coating solvent and preparation method thereof

A technology of trace elements and solvents, applied in the field of aluminum trace element adjustment materials coated with solvents and its preparation, can solve the problems of excessive melting point difference, troublesome preparation, environmental pollution, etc., and reduce pollution, reduce preparation difficulty, and preparation difficulty low effect

Inactive Publication Date: 2018-10-09
CANGZHOU DONGZHONG SPECIAL ALLOY MFG CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As we all know, aluminum and aluminum alloys are widely used in civil, construction and aerospace. With the continuous development of aluminum processing and aluminum alloy industry, the research and development of aluminum alloy is listed as a key development technology. In the production process of aluminum alloy, it is necessary to add other metals to adjust the trace element content of aluminum alloy. When the existing method is used to adjust the trace element content of aluminum alloy, the intermediate metal or metal additive is generally used to complete the aluminum alloy in the smelting process. alloying, but in the preparation of master alloys, there is a problem that the difference in melting point is too large, the preparation is more troublesome, and when using metal additives to adjust the content of trace elements in aluminum alloys, the temperature required for molten metal additives is higher than that of aluminum. temperature, it is easy to cause a large burning loss of aluminum metal, which reduces its yield. At the same time, a large amount of release agent needs to be added in the production process of metal additives, which will produce more black in the process of melting and casting. smoke, polluting the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] Below in conjunction with the examples, the specific implementation of the present invention will be further described in detail. The following examples are used to illustrate the present invention, but are not intended to limit the scope of the present invention.

[0022] The solvent-coated microelement adjustment material for aluminum of the present invention is made by mixing special solvents, adhesives, pure titanium chips, manganese flakes and copper wires and drying them.

[0023] The solvent-coated aluminum trace element adjustment material of the present invention, the special solvent is formed by mixing magnesium oxide, hexachloroethane and aluminum fluoride, and its mixing ratio is:

[0024] Magnesium Oxide 20%;

[0025] Hexachloroethane 25%;

[0026] Aluminum fluoride 55%.

[0027] In the solvent-coated aluminum trace element adjustment material of the present invention, the binder is an aqueous solution of polyvinyl alcohol.

[0028] The preparation meth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of aluminum alloy production, and particularly relates to a material for adjusting trace elements for aluminum of an external coating solvent and a preparation method thereof. The material and the preparation method thereof have the advantages that the preparation difficulty can be lowered, in addition, the pollution to the environment can be reduced, and intermediate metal and metal additives can be replaced; and the material is prepared by mixing and then drying a special solvent, an adhesive, pure titanium scraps, manganese sheets and copper wires.

Description

technical field [0001] The invention relates to the technical field of aluminum alloy production, in particular to a solvent-coated trace element adjustment material for aluminum and a preparation method thereof. Background technique [0002] As we all know, aluminum and aluminum alloys are widely used in civil, construction and aerospace. With the continuous development of aluminum processing and aluminum alloy industry, the research and development of aluminum alloy is listed as a key development technology. In the production process of aluminum alloy, it is necessary to add other metals to adjust the trace element content of aluminum alloy. When the existing method is used to adjust the trace element content of aluminum alloy, the intermediate metal or metal additive is generally used to complete the aluminum alloy in the smelting process. alloying, but in the preparation of master alloys, there is a problem that the difference in melting point is too large, the preparati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C1/02C22C21/00
Inventor 张忠华张忠凯王磊
Owner CANGZHOU DONGZHONG SPECIAL ALLOY MFG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products