Fireproof composition for preparing fireproof glass and preparation method thereof

A technology for fireproof glass and composition, applied in the field of fireproof composition and preparation thereof, fireproof composition for fireproof glass and preparation thereof, can solve the problems of low adhesion of fireproof liquid, poor anti-aging performance, affecting fireproof performance and the like, To achieve the effect of improving adhesion, good fire resistance and improving efficiency

Active Publication Date: 2018-10-19
新福兴玻璃工业集团有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the fireproof glass prepared by this method improves the fireproof performance of the glass to a certain extent, the adhesion of the fireproof liquid is low, which makes the compatibility between the fireproof liquid layer and the glass poor, and often occurs during long-term use. The problems of anti-detachment and anti-aging properties of glass affect the fireproof performance. With the continuous development of the construction industry, the utilization rate of fireproof glass is increasing. It is required that the fireproof liquid can ensure that the glass still has the fire protection under long-term use conditions. good fire performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fireproof composition for preparing fireproof glass and preparation method thereof
  • Fireproof composition for preparing fireproof glass and preparation method thereof
  • Fireproof composition for preparing fireproof glass and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] 1. Prepare raw materials according to the following weight ratio (g)

[0041]

[0042]

[0043] 2. Pour the raw materials potassium nitrate, cesium nitrate, Swiss seven-eight, methacrylic acid, acetone, and table salt into a plastic container filled with water in sequence, and use an electric stirrer to stir for mixing. The stirring rate is 120rpm (usually 60-120rpm); stirring time is 1.5h;

[0044] 3. Stir and mix the mixed solution for 1.5 hours, and place it at a temperature of 25°C to allow it to fully blend with each other, and leave it to react for 48 hours to obtain the fireproof composition of the present invention.

Embodiment 2

[0046] 1. Prepare raw materials according to the following weight ratio (g)

[0047]

[0048] 2. Pour the raw materials potassium nitrate, cesium nitrate, Swiss seven-eight, methacrylic acid, acetone, and salt into a plastic container filled with water in sequence, and use an electric stirrer to stir for mixing treatment, wherein the stirring rate is 100rpm (usually 60-120rpm); Stirring time is 2h;

[0049] 3. Stir and mix the mixed solution for 2 hours, and place it under the temperature condition of 25° C. to fully fuse with each other to generate oxidation and reduction reactions. After standing for 50 hours, the fireproof composition of the present invention is obtained.

Embodiment 3

[0051] 1. Prepare raw materials according to the following weight ratio (g)

[0052]

[0053]

[0054] 2. Pour the raw materials potassium nitrate, cesium nitrate, Swiss seven-eight, methacrylic acid, acetone, and table salt into a plastic container filled with water in sequence, and use an electric stirrer to stir for mixing. The stirring rate is 60rpm (usually 60-120rpm); Stirring time is 2h;

[0055] 3. Stir and mix the mixed solution for 2 hours, and place it under the temperature condition of 25° C. to fully fuse with each other to generate oxidation and reduction reactions. After standing for 60 hours, the fireproof composition of the present invention is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface stressaaaaaaaaaa
thicknessaaaaaaaaaa
service temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses fireproof composition for preparing fireproof glass and a preparation method thereof. The fireproof composition disclosed by the invention is prepared from the raw materials ofmethylacrylic acid, a photoinitiator 1173, acetone, cesium nitrate, potassium nitrate and sodium chloride. A preparation method of a fireproof solution disclosed by the invention is simple, and the fireproof glass prepared from the fireproof solution disclosed by the invention has the advantages of good high temperature resistance, high fire resistance, strong impact resistance and an excellent mechanical property.

Description

technical field [0001] The invention relates to a fireproof composition and a preparation method thereof, in particular to a fireproof composition for fireproof glass and a preparation method thereof, belonging to the field of fireproof glass production. Background technique [0002] Fire-resistant glass is a special glass that can maintain its integrity in the prescribed fire-resistant test. Its role in fire prevention is mainly to control the spread of fire or to isolate smoke. It is a measure-type fireproof material. Performance is evaluated. It is a special glass that has been processed and treated by a special process and can maintain its integrity and heat insulation in the specified fire resistance test. The original glass of fireproof glass can be made of float flat glass, toughened glass, and the composite fireproof glass can also be made of single piece of fireproof glass. [0003] There are five main types of fireproof glass, which are laminated composite firepr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C21/00
CPCC03C21/001C03C21/002
Inventor 田永刚陈玉平陈世烜
Owner 新福兴玻璃工业集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com