Production process of 6-series aluminum alloy ultra-thin round tube extrusion profile

A technology of aluminum alloy profiles and extruded profiles, which is applied in the field of aluminum alloy production, can solve the problems that the aging system cannot meet the size and mechanical performance requirements of aluminum alloy ultra-thin round tubes, and can compensate for the low elongation and small degree of deformation after breaking , The effect of slow work hardening speed

Active Publication Date: 2018-11-09
CHINA ZHONGWANG
View PDF8 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, in order to solve the problem that the existing quenching method and aging system cannot meet the size and mechanical performance requirements of aluminum alloy ultra-thin round tubes, the present invention provides a production process for 6-series aluminum alloy ultra-thin round tube extrusion profiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process of 6-series aluminum alloy ultra-thin round tube extrusion profile
  • Production process of 6-series aluminum alloy ultra-thin round tube extrusion profile
  • Production process of 6-series aluminum alloy ultra-thin round tube extrusion profile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A production process of a 6-series aluminum alloy ultra-thin round tube extruded profile, comprising the following steps:

[0028] A. Calculate the amount of each aluminum alloy raw material and prepare the aluminum alloy raw material according to the ratio. The mass percentage ratio of each element of the 6 series aluminum alloy raw material is as follows:

[0029]

[0030] Add the prepared aluminum alloy raw materials into the melting furnace and mix them evenly to melt them into liquid aluminum alloys, then melt and cast the liquid aluminum alloys into aluminum alloy ingots. Semi-continuous casting method of filtering and casting, the temperature of the melting furnace is controlled at 750°C, and refining is carried out with refining agent;

[0031] B. The aluminum alloy ingot obtained in step A is subjected to homogenization treatment, the temperature of the homogenization treatment is 450°C, and the holding time is 20h;

[0032] C. Place the aluminum alloy ingo...

Embodiment 2

[0037] The difference between embodiment 2 and embodiment 1 is that in step A, the mass percentage ratio of each element of the 6 series aluminum alloy raw material is as follows:

[0038]

Embodiment 3

[0040] The difference between Example 3 and Example 1 is that the temperature of the homogenization treatment in step B is 500° C., and the holding time is 10 h.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of aluminum alloy production, and relates to a production process of a 6-series aluminum alloy ultra-thin round tube extrusion profile, aluminum alloy rawmaterials comprise 1.35-1.45% of Si, 0.21% of Fe, 0.05 % of Cu, 0.44 to 0.48% of Mn, 0.50 to 0.55% of Mg, 0.09% of Cr, 0.05% of Zn, 0.02% of Ti, <= 0.05% of other single impurities, <=0.15% of total impurities, and balance of Al, an aluminum alloy ingot prepared by the formula is subjected to extrusion, on-line water mist quenching treatment, stretching and straightening, and artificial aging, andthe aging system for the artificial aging is 145+ / -5DEG C *11h, existing quenching method and aging system are changed, the size and the mechanical properties of a finally prepared aluminum alloy ultra-thin round tube can meet the requirements of production preparation, the aluminum alloy tube is thin in wall, and the elongation after fracture is greatly improved.

Description

technical field [0001] The invention belongs to the technical field of aluminum alloy production, and relates to a production process of a 6-series aluminum alloy ultra-thin round tube extrusion profile. Background technique [0002] The so-called aluminum alloy is to add an appropriate amount of other elements to industrial pure aluminum to improve the nature of aluminum to meet various needs in industry and life. Due to the small specific gravity, high specific strength and good comprehensive performance of aluminum alloy, it is widely used in aviation industry, automobile manufacturing industry, power instrument, tool and civil utensil manufacturing, etc. [0003] In the research and development and production process of aluminum alloy, it is necessary to analyze the chemical composition in aluminum alloy, so as to achieve the purpose of strictly controlling the content of each chemical composition, thereby avoiding the loss of control of the composition before the furnac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C1/02C22C21/02C22F1/043C22F1/02B21C23/02
CPCB21C23/02C22C1/026C22C21/02C22F1/02C22F1/043
Inventor 李佳宁周通刘生辉滕飞赵釜玉
Owner CHINA ZHONGWANG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com