Functional layer coating for projection screen, projection screen and manufacturing method thereof

A functional layer and screen technology, applied in the field of projection, can solve the problems of low contrast, low resolution, narrow viewing angle, etc., achieve the effect of blocking water vapor, simple production method, and improving contrast

Active Publication Date: 2020-12-11
张家港宝视特影视器材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing projection screens still have problems such as low brightness, low contrast, low resolution, and narrow viewing angles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Functional layer coating for projection screen, projection screen and manufacturing method thereof
  • Functional layer coating for projection screen, projection screen and manufacturing method thereof
  • Functional layer coating for projection screen, projection screen and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A method for making a projection screen, comprising the following steps:

[0039] (1) Provide a base layer, the material of the base layer is PET, and the thickness of the base layer is 1mm;

[0040] (2) Coating a glass fiber layer of 0.3mm on one side of the base layer, depositing a protective layer on one side of the glass fiber layer, the material of the protective layer is a composite layer composed of silicon nitride and silicon carbide, and the thickness is 0.5mm;

[0041] (3) Add 18 parts of precious metal nanoparticles and 15 parts of ceramic powder into 55 parts of water-based styrene-acrylic emulsion, raise the temperature to 75°C, oscillate ultrasonically for 15-30min, set the temperature to 50°C, add 5 parts of plasticizer, 4 1 part of stiffening agent and 2 parts of flame retardant, put into a disperser and stir at a speed of 500 rpm for 10-20 minutes to obtain a functional layer coating, which is coated on one side of the protective layer to form a functio...

Embodiment 2

[0043] A method for making a projection screen, comprising the following steps:

[0044] (1) Provide a base layer, the material of the base layer is PVC, and the thickness of the base layer is 1mm;

[0045] (2) Coating a glass fiber layer of 0.3 mm on one side of the base layer, depositing a protective layer on one side of the glass fiber layer, the material of the protective layer is aluminum oxide, and the thickness is 0.3 mm;

[0046] (3) Add 12 parts of precious metal nanoparticles and 10 parts of ceramic powder into 50 parts of water-based styrene-acrylic emulsion, raise the temperature to 85°C, ultrasonically oscillate for 15-30min, set the temperature to 60°C, add 4 parts of plasticizer, 3 1 part of stiffening agent and 4 parts of flame retardant, put into a disperser and stir at a speed of 500 rpm for 10-20 minutes to obtain a functional layer coating, which is coated on one side of the protective layer to form a functional layer , the thickness of the functional laye...

Embodiment 3

[0048] A method for making a projection screen, comprising the following steps:

[0049] (1) Provide a base layer, the material of the base layer is PVC, and the thickness of the base layer is 1mm;

[0050] (2) Coating a glass fiber layer of 0.3mm on one side of the base layer, depositing a protective layer on one side of the glass fiber layer, the material of the protective layer is a combined layer of silicon oxide and silicon carbide, and the thickness is 0.6mm;

[0051] (3) Add 20 parts of precious metal nanoparticles and 16 parts of ceramic powder into 53 parts of water-based styrene-acrylic emulsion, raise the temperature to 85°C, oscillate ultrasonically for 15-30min, set the temperature to 55°C, add 3 parts of plasticizer, 3 1 part of stiffening agent and 5 parts of flame retardant, put into a disperser and stir at a speed of 500 rpm for 10-20 minutes to obtain a functional layer coating, which is coated on one side of the protective layer to form a functional layer ,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a functional layer coating for a projection screen. The coating is prepared from the following components in parts by weight: 50-55 parts of aqueous styrene-acrylic emulsion, 12-20 parts of noble metal nanoparticles, 10-18 parts of ceramic powder, 3-6 parts of a plasticizer and 2-5 parts of a stiffening agent. The projection screen comprises a base layer as well as a glassfiber layer, a protective layer and a functional layer which are arranged on one side of the base layer sequentially. The projection screen has high optical efficiency, high screen brightness, 1.04 brightness gain and wide viewing angle range. Besides, the projection screen is provided with the protective layer for blocking water vapor, and can be prevented from damage caused by moisture.

Description

technical field [0001] The application belongs to the projection field, and in particular relates to a functional layer coating for a projection screen, a projection screen and a manufacturing method thereof. Background technique [0002] The projection screen is one of the most commonly used products in the peripheral equipment of the projector. When watching movies in the home theater or presenting materials in meetings and large-scale events, the projector is often used to project images onto a projection screen to make the image to be presented Completely and clearly presented on the white projection screen. Existing projection screens have problems such as unclear projected content, uneven brightness of projected content, and low brightness gain, which cannot satisfy the audience's desire for intuitive quality effects. [0003] After the light projected by the projector passes through the projection screen, due to the influence of the diffusion angle, the observer perc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D125/14C09D7/61G03B21/60
CPCC08K2003/0806C08K2003/0831C08K2003/085C08K2201/011C09D125/14C09D7/61G03B21/60C08K3/08C08K3/00
Inventor 姜国梁沈瑜沈姣姜茂德陈浩
Owner 张家港宝视特影视器材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap