A kind of volcanic rock composition plate, profile and manufacturing method

A technology of volcanic rock and composition, which is applied in the field of construction and home decoration, can solve the problems of insufficient plate performance, rough manufacturing method, single raw material variety, etc., and achieve the effect of excellent performance, low cost and excellent performance

Active Publication Date: 2020-01-31
FUSONG COUNTY HEPING FURNITURE CO LTD
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0016] Existing plate making methods, the method and the prepared materials have their own imperfections, such as the single type of raw materials, rough manufacturing methods, insufficient plate performance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A volcanic rock composite plate is made of the following raw materials in parts by weight: 100 parts by weight of volcanic rock, 10 parts of graphene, 2 parts of potassium permanganate, 30 parts of urea-formaldehyde resin adhesive, 1 part of phosphogypsum, 1 part of straw, and 0.1 parts of medicinal residue.

[0041] It includes the following steps:

[0042] 1) Mix graphene and potassium permanganate, add appropriate amount of water, wet ball mill for 1 hour, dry at room temperature for 1 hour, record as product A, and set aside;

[0043] 2) directly pulverize the straw and medicinal dregs by ball milling for 1 hour, record it as product B, and set aside;

[0044] 3) Mix volcanic rock and phosphogypsum, wet ball mill for 2 hours, add product A obtained in step 1) and product B obtained in step 2), and ball mill for 2 hours;

[0045] 4) Mix the product obtained in step 3) with the urea-formaldehyde resin adhesive evenly, compress and mold at a pressure of 3MPa, for 1h, ...

Embodiment 2

[0047] A volcanic rock composition board, made of the following raw materials in parts by weight: volcanic rock 110, graphene 15, potassium permanganate 5, urea-formaldehyde resin adhesive 50, phosphogypsum 2, straw 2, and medicinal residue 0.2.

[0048] It includes the following steps:

[0049] 1) Mix graphene and potassium permanganate, add appropriate amount of water, wet ball mill for 2 hours, dry at room temperature for 3 hours, record as product A, and set aside;

[0050] 2) directly pulverize the straw and medicinal dregs by ball milling for 2 hours, record it as product B, and set aside;

[0051] 3) Mix volcanic rock and phosphogypsum, wet ball mill for 3 hours, add product A obtained in step 1) and product B obtained in step 2), and ball mill for 3 hours;

[0052] 4) Mix the product obtained in step 3) with a urea-formaldehyde resin adhesive evenly, compress and mold at a pressure of 5 MPa, for 2 hours, and ripen for 3 days to make a board.

Embodiment 3

[0054] A volcanic rock composition board, made of the following raw materials in parts by weight: volcanic rock 104, graphene 12, potassium permanganate 3, urea-formaldehyde resin adhesive 35, phosphogypsum 1, straw 1, and medicinal residue 0.15.

[0055] It includes the following steps:

[0056] 1) Mix graphene and potassium permanganate, add appropriate amount of water, wet ball mill for 1.2 hours, dry at room temperature for 1.3 hours, record as product A, and set aside;

[0057] 2) directly pulverize the straw and medicinal dregs by ball milling for 1.2 hours, record it as product B, and set aside;

[0058] 3) Mix volcanic rock and phosphogypsum, wet ball mill for 2.3 hours, add product A obtained in step 1) and product B obtained in step 2), and ball mill for 2.3 hours;

[0059] 4) Mix the product obtained in step 3) with a urea-formaldehyde resin adhesive evenly, compress and mold at a pressure of 3.5 MPa, for 1.2 hours, and ripen for 1.3 days to make a board.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
densityaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to View More

Abstract

The invention relates to a volcanic composite board and a sectional material. The volcanic composite board is prepared from the following raw materials in parts by weight: 100 to 110 parts of volcanic, 10 to 15 parts of graphene, 2 to 5 parts of potassium permanganate, 30 to 50 parts of a urea-formaldehyde resin adhesive, 1 to 2 parts of phosphogypsum, 1 to 2 parts of straws and 0.1 to 0.2 part ofherb residue. The volcanic is used as a basic raw material, graphene is added, and industrial wastes and forestry and agricultural wastes are sufficiently utilized, so that the obtained product is light in weight and excellent in performance.

Description

technical field [0001] The invention relates to the field of construction and home improvement, namely a volcanic rock composition plate, profile and production method. Background technique [0002] With the gradual enhancement of my country's economic strength and the continuous improvement of the level of science and technology, the government has paid more and more attention to and recognized the use of advanced energy-saving technologies and energy-saving materials in the field of construction to save energy. In the existing technology, due to the lack of resources, the prices of organic plates and profiles in construction and home decoration are gradually rising, and they will not be able to meet market demand in the future. At present, in building decoration, the materials for indoor pavement or dado decoration are generally made of wood, stone or porcelain. [0003] CN201610246103.5 discloses a plate and profile made of volcanic rock composition, which is made of raw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/12
CPCC04B26/127C04B2111/40C04B2201/20C04B2201/50C04B14/14C04B14/024C04B18/0445C04B18/24C04B22/08
Inventor 孙和平
Owner FUSONG COUNTY HEPING FURNITURE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com