Heat non-combustible tobacco sheet by papermaking method, coating liquid thereof, coat method and preparation method thereof

A heat-not-burn, tobacco sheet technology, applied in the directions of tobacco, tobacco preparation, application, etc., can solve the problems of lack of large-scale production, large surface adhesion of the sheet, deviation of processing performance, etc., and is conducive to cutting or rolling. Good handling, good machinability, reduced surface adhesion and friction

Active Publication Date: 2018-11-27
SHANGHAI TOBACCO GRP CO LTD +1
View PDF11 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among the common heat-not-burn tobacco products in the market, some use the thick slurry method sheet, which has the disadvantages of strong surface adhesion, less tobacco aroma, mainly flavoring outside the smoke, and deviation in processing performance; some use the Dry-process flakes, the R&D platform has low output of small products, does not have the capacity for large-scale production, and the smoke volume after being made into cigarettes is relatively small

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A preparation method of heat-not-burn tobacco sheet by papermaking method, the steps are as follows:

[0049] (1) Mix 50g of tobacco raw material with 50g of bleached coniferous wood pulp, add 35g of 200 mesh heavy calcium carbonate, and then add 1000g of hot water at 60°C for extraction, use a single-screw squeezer to achieve solid-liquid separation, and squeeze dryness 25%, to obtain tobacco extract and pulp mass;

[0050] (2) diluting the pulp mass obtained in step (1), mechanically beating the pulp, and copying and molding to obtain the tobacco sheet base;

[0051] (3) concentrating the tobacco extract obtained in step (1) to a concentration of 25% tobacco concentrate at a temperature of 70° C. and a vacuum of 40 kPa after purification;

[0052] (4) Add glycerol, propylene glycol, 1250 mesh light calcium carbonate and potassium bicarbonate to the tobacco concentrate obtained in step (3), and form a tobacco sheet coating solution after uniform stirring for 10 minute...

Embodiment 2

[0057] A preparation method of heat-not-burn tobacco sheet by papermaking method, the steps are as follows:

[0058] (1) Mix 82g of tobacco raw material with 18g of bleached coniferous wood pulp, add an additional 15g of 200 mesh heavy calcium carbonate, and then add 400g of hot water at 70°C for extraction, use a single-screw squeezer to achieve solid-liquid separation, and squeeze dryness 33%, to obtain tobacco extract and pulp mass;

[0059] (2) diluting the pulp mass obtained in step (1), mechanically beating the pulp, and copying and molding to obtain the tobacco sheet base;

[0060] (3) concentrating the tobacco extract obtained in step (1) to a concentration of 40% tobacco concentrate at a temperature of 60° C. and a vacuum of 55 kPa after purification;

[0061] (4) Add glycerol, 1250 mesh wollastonite and potassium citrate to the tobacco concentrate obtained in step (3), and form a tobacco sheet coating solution after uniform stirring for 10 minutes, wherein 50g of gl...

Embodiment 3

[0066] A preparation method of heat-not-burn tobacco sheet by papermaking method, the steps are as follows:

[0067] (1) Mix 82g of tobacco raw material with 18g of bleached coniferous wood pulp, add 15g of 200 mesh diatomite, and then add 600g of hot water at 70°C for extraction. Use a single-screw squeezer to achieve solid-liquid separation, and the squeeze dryness is 32%, to obtain tobacco extract and pulp mass;

[0068] (2) diluting the pulp mass obtained in step (1), mechanically beating the pulp, and copying and molding to obtain the tobacco sheet base;

[0069] (3) concentrating the tobacco extract obtained in step (1) to a concentration of 40% tobacco concentrate at a temperature of 65° C. and a vacuum of 60 kPa after purification;

[0070] (4) Add glycerol, R2 type titanium dioxide and potassium citrate in the tobacco concentrate that step (3) obtains, form tobacco sheet coating liquid after uniform stirring 12min, wherein add 40g glycerine in every 60g tobacco conce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A method for heat non-combustible tobacco sheet and coating liquid thereof by pap making method includes such steps as concentrating liquid of tobacco, smoke agent, viscosity reduce agent and combustion promoter, concentrating liquid of tobacco 20-90 g and smoke agent 10-80 g per 100 g of concentrated liquid of tobacco and smoke agent, coating liquid of tobacco 20-90 g and smoke agent 10-80 g per100 g of concentrated liquid of tobacco and smoke agent, coating liquid of tobacco 10-80 g per 100 g of concentrated liquid of tobacco and smoke agent, coating liquid of tobacco 10-80 g per 100 g of non-combustible liquid, coating liquid of tobacco 10-80 g per 100 g of non-combustible liquid, coating liquid of non-combustible liquid, coating liquid of non-combustible liquid and coating liquid of non-combustible tobacco. 1 to 15 g of viscosity reduce and 1 to 8 g of combustion promoter per 100 g of tobacco concentrate and smoke agent. By means of the coating liquid of the invention, the heatednon-combustible tobacco sheet obtained by the coating method endows the papermaking tobacco sheet with a high proportion of glycerol, and has low surface adhesion and friction.

Description

technical field [0001] The invention belongs to the field of novel heat-not-burn tobacco products, and in particular relates to a paper-making heat-not-burn tobacco sheet and its coating solution, coating method and preparation method. Background technique [0002] The world cigarette market is facing the third revolution after the birth of the cigarette machine and the advent of the filter tip. As a new type of tobacco product, the new heat-not-burn cigarette is gradually becoming the product pursued by the new generation of smokers, and its market share is gradually increasing. Improvement, rapid development momentum, significant reduction in harmful chemical components and biological toxicity of smoke, and easier acceptance by younger smokers. Therefore, the research on new tobacco products and their heating devices has gradually become the key work of various tobacco industries, among which the research on tobacco products is the most important. [0003] Papermaking rec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A24B3/14
CPCA24B3/14
Inventor 严新龙薛洪龙张克娟李新生宋成剑李德贵
Owner SHANGHAI TOBACCO GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap