Biological epoxy asphalt as well as preparation method and application thereof

A kind of epoxy asphalt, biological technology, applied in the direction of building structure, building components, building insulation materials, etc., can solve the problems such as poor effect, achieve excellent high and low temperature and anti-aging characteristics, reduce precipitation and oxidation, and is conducive to popularization and use Effect

Active Publication Date: 2018-11-27
SOUTHEAST UNIV
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved in the present invention is to provide a kind of biological epoxy asphalt, to solve the problems such as poor effect existing in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Biological epoxy asphalt as well as preparation method and application thereof
  • Biological epoxy asphalt as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Example 1: Weigh 100 parts of epoxidized soybean oil, add 20 parts of phenyl glycidyl ether, start stirring, gradually heat up to 160° C., react for 2 hours and cool to room temperature to obtain component A of the bio-epoxy material.

Embodiment 2

[0032] Example 2: Weigh 100 parts of epoxidized soybean oil, add 20 parts of benzyl glycidyl ether, start stirring, gradually heat up to 160 ° C, react for 2 hours and cool to room temperature to obtain component A of the bio-epoxy material.

Embodiment 3

[0033] Example 3: Weigh 100 parts of epoxidized soybean oil, add 30 parts of benzyl glycidyl ether, start stirring, gradually heat up to 160° C., react for 2 hours and cool to room temperature to obtain component A of the bio-epoxy material.

[0034] The preparation method of bio-epoxy asphalt B component is as follows:

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses biological epoxy asphalt. The biological epoxy asphalt contains a component A, a component B and a component C, wherein the component A contains epoxidized soybean oil and a diluent, the component B contains a curing agent, an accelerant and a defoaming agent, and the component C contains asphalt; and the mass ratio of the component A to the component C is (105-126) :45, and the mass ratio of the component A to the component B is 100 : (57-520). Compared with the prior art, the biological epoxy asphalt can be used for replacing traditional petroleum asphalt; by utilizing the materials of epoxidized soybean oil, a biological curing agent and the like, the cost is remarkably lowered, and meanwhile, the thermoplastic property of a traditional asphalt material can be effectively improved, so that the biological epoxy asphalt has excellent high-low-temperature performance and anti-aging property and can be widely applied to the pavements of roads, tunnels and the like and the pavement of bridge surfaces. The invention discloses a preparation method of the biological epoxy asphalt.

Description

technical field [0001] The invention belongs to the field of construction, and in particular relates to a biological epoxy asphalt and its preparation method and application. Background technique [0002] Epoxy asphalt is a three-dimensional continuous phase thermosetting material formed by an irreversible chemical crosslinking and curing reaction of epoxy resin, curing agent, and petroleum asphalt. As the temperature rises, epoxy asphalt will not soften like traditional asphalt, and has good aging resistance and chemical corrosion resistance. The fatigue performance of epoxy asphalt concrete is three orders of magnitude greater than that of Superpave polymer modified asphalt concrete, which can be easily It is suitable for heavy load, large traffic volume and wide-area temperature, which greatly improves road performance. On the other hand, as an alternative product of traditional petroleum asphalt, bio-asphalt can be made from a variety of biomass materials, such as wheat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L91/00C04B26/26
CPCC04B26/26C08L95/00C04B2201/50C08L2201/08C08L91/00C04B14/02
Inventor 罗桑魏小皓田佳昊陆庆全迅闵剑勇钟科杨旭王建伟殷俊梅晨悦刘诗城黄浩
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com