Foamed concrete and preparation method thereof

A technology of foamed concrete and chemical foaming agent, which is applied in the field of building concrete, can solve the problems of poor thermal insulation performance of foamed concrete, achieve excellent mechanical properties and thermal insulation performance, reduce drying shrinkage, and improve flexural resistance performance effect

Inactive Publication Date: 2018-12-07
苏州郎旭志远科技有限公司
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art, the present invention provides a foamed concrete and its preparation method, which solves the problem that the thermal insulation performance of foamed concrete is not as good as that of organic foam thermal insulation materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0026] Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0027] The invention provides a technical solution: a foamed concrete and a preparation method thereof, which are composed of airgel powder, foamed concrete and fibers, the airgel powder is composed of an internal hydrophobic layer and a surface hydrophilic layer, and the surface is hydrophilic The thickness of the water layer is 0.1-100 μm, and the fiber mat is one or more of glass fiber mat, basalt fiber mat, alumina fiber mat, carbon fiber mat, and polyvinyl chloride fiber mat.

[0028] A kind of foam concrete and preparation method thereof, comprises the following steps:

[0029] first step:

[0030] Airgel powder modification;

[0031] Step two:

[0032] The airgel powder is dry mixed with the gelling material, and then wet mixed with water;

[0033] t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses foamed concrete and a preparation method thereof. The foamed concrete contains aerogel powder, foamed concrete and fibers, wherein the aerogel powder contains an internal hydrophobic layer and a surface hydrophilic layer, and the thickness of the surface hydrophilic layer is 0.1-100 microns; and a fiber felt is one or more of a glass fiber felt, a basalt fiber felt, an aluminum oxide fiber felt, a carbon fiber felt and a polyvinyl chloride fiber felt. According to the preparation method, the fibers are compounded with the foamed concrete, the fibers are uniformly distributed in the foamed concrete, and the foamed concrete still remains a nano-porous structure; and compared with existing foamed concrete in the market, the foamed concrete has relatively excellent mechanical property and heat insulation property, the fracture resistance and pressure resistance of the foamed concrete can be remarkably improved, the foamed concrete can be endowed with certain flexibility, and the drying shrinkage value of the foamed concrete can be decreased.

Description

technical field [0001] The invention relates to the technical field of building concrete, in particular to foamed concrete and a preparation method thereof. Background technique [0002] Commonly used wall insulation materials include expanded polystyrene, expanded polyurethane, rock wool, insulating mortar, expanded glass, and traditional expanded concrete. Expanded polystyrene and expanded polyurethane have excellent heat insulation performance, but they are flammable in case of fire and produce suffocating smoke, which seriously threatens the safety of the owner; rock wool has excellent heat insulation performance, but it fails in water, and the construction is difficult; insulation mortar Good fire resistance, but relatively high thermal conductivity; foamed glass is prone to slag, and the cost is high, which affects its engineering application. [0003] Compared with existing thermal insulation materials, foamed concrete belongs to Class A thermal insulation materials,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/06C04B28/32C04B28/14C04B28/10C04B28/26C04B26/06C04B26/14C04B26/16C04B26/08C04B26/32C04B38/02C04B20/12C04B14/06
CPCC04B28/04C04B20/12C04B26/06C04B26/08C04B26/14C04B26/16C04B26/32C04B28/06C04B28/065C04B28/10C04B28/14C04B28/26C04B28/32C04B14/064C04B2103/0057C04B24/383C04B2103/302C04B22/147C04B22/04C04B14/4656C04B38/02C04B20/1051C04B20/1022
Inventor 任旭任策
Owner 苏州郎旭志远科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products