Corrosion and oxidation resistant jewelry 10K green gold and processing process thereof

A processing technology and oxidation-resistant technology, applied in the field of gold alloys, can solve the problems of fading, corrosion, discoloration, etc., and achieve the effect of low production cost, reduced equipment requirements, and low price

Inactive Publication Date: 2018-12-07
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current green K gold often has corrosion spots on the surface after being used for 6 months, as well as fading and fading.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A corrosion-resistant and oxidation-resistant 10K green gold for jewelry and a processing technology thereof. In terms of weight percentage, the composition of the alloy is Li: 1.0wt.%, Mn: 2.0wt.%, Fe: 4.0wt.%, Cd: 8.0wt.%, Zn: 6.0wt.%, In: 15.0wt.% , Au: 40.0wt.%, the balance is tin. The above-mentioned 10K green gold for corrosion-resistant and oxidation-resistant jewelry and its processing technology include the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a graphite crucible; Protected by argon gas to avoid serious burning of alloy elements due to large air flow; heat preservation at 1200 degrees for 10 minutes during smelting, and electromagnetic stirring by high-frequency induction furnace; after stirring evenly, heat preservation at 1200 degrees for 1 minute and cast out of the furnace; gold alloy casting adopts The steel mold with a diameter of 50-100mm is cooled by water cooling. The obtained ...

Embodiment 2

[0019] A corrosion-resistant and oxidation-resistant 10K green gold for jewelry and a processing technology thereof. In terms of weight percentage, the composition of the alloy is Li: 1.4wt.%, Mn: 4.0wt.%, Fe: 6.0wt.%, Cd: 12.0wt.%, Zn: 8.0wt.%, In: 20.0wt.% , Au: 42.0wt.%, the balance is tin. The above-mentioned 10K green gold for corrosion-resistant and oxidation-resistant jewelry and its processing technology include the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a graphite crucible; Protected by argon gas to avoid serious burning of alloy elements due to large air flow; heat preservation at 1200 degrees for 10 minutes during smelting, and electromagnetic stirring by high-frequency induction furnace; after stirring evenly, heat preservation at 1200 degrees for 1 minute and cast out of the furnace; gold alloy casting adopts The steel mold with a diameter of 50-100mm is cooled by water cooling. The obtained...

Embodiment 3

[0022] A corrosion-resistant and oxidation-resistant 10K green gold for jewelry and a processing technology thereof. In terms of weight percentage, the composition of the alloy is Li: 1.2wt.%, Mn: 3.0wt.%, Fe: 5.0wt.%, Cd: 9.0wt.%, Zn: 7.0wt.%, In: 18.0wt.% , Au: 41.0wt.%, the balance is tin. The above-mentioned 10K green gold for corrosion-resistant and oxidation-resistant jewelry and its processing technology include the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a graphite crucible; Protected by argon gas to avoid serious burning of alloy elements due to large air flow; heat preservation at 1200 degrees for 10 minutes during smelting, and electromagnetic stirring by high-frequency induction furnace; after stirring evenly, heat preservation at 1200 degrees for 1 minute and cast out of the furnace; gold alloy casting adopts The steel mold with a diameter of 50-100mm is cooled by water cooling. The obtained ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses corrosion and oxidation resistant jewelry 10K green gold and a processing process for the corrosion and oxidation resistant jewelry 10K green gold. In percentage by weight, thealloy comprises the ingredients of 1.0-1.4% of Li, 2.0-4.0% of Mn, 4.0-6.0% of Fe, 8.0-12.0% of Cd, 6.0-8.0% of Zn, 15.0-20.0% of In, 40.0-42.0% of Au and the balance tin. By means of the corrosion and oxidation resistant jewelry 10K green gold and the processing process for the corrosion and oxidation resistant jewelry 10K green gold, the problems that present green K gold is seriously insufficient in corrosion resistance and generates corrosion spots after being used for 6 months are solved, the corrosion and oxidation resistant jewelry 10K green gold effectively breaks through the bottleneck of development in the field of jewelry, and prediction can be performed, implementation and industrialization of the corrosion and oxidation resistant jewelry 10K green gold will obtain fruitful economic results and social benefits.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a gold alloy. Background technique [0002] Gold is a symbol of nobility and wealth. Gold jewelry itself has infinite beauty, can play the role of decoration and enhancement, and enhance the charm and confidence of the wearer. With the development of China's economy, the domestic gold and jewelry market has gradually prospered. From the initial dominance of the world by gold jewelry, to the addition of diamond and platinum jewelry in the 1990s, the domestic gold jewelry market has basically formed a three-point pattern. Traditional gold products are increasingly unable to meet the increasing consumer demand, and gold deep processing has become the only way for many companies to capture the market. [0003] When other elements are added to gold to form a gold alloy, the resulting alloy jewelry is called K gold in the market. When gold is fused with other metals, K gold of differ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C30/04C22C30/06C22C1/02C22F1/14
CPCC22C30/04C22C1/02C22C5/02C22C30/06C22F1/14
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap