Preparation method of plastic with antibacterial function

A plastic and functional technology, which is applied in the field of plastic preparation with antibacterial function, can solve the problems of inconspicuous germ effect and poor antibacterial effect, and achieve the effect of improved antibacterial property, strong impact strength and improved antibacterial property

Inactive Publication Date: 2018-12-21
HEFEI WANZHIJING DOORS & WINDOWS CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing Chinese patent literature (publication number: CN103627197B) discloses an antibacterial thermoplastic composition and a preparation method thereof. The composition includes the following components blended: thermoplastic resin: 100 parts by weight; antibacterial agent 0.3 to 3 parts by weight parts; wherein the antibacterial agent is antibacterial glass powder, including the following components by weight percentage: P2O5 30-40wt%; Na2O or K2O 6-18wt%, ZnO 50-60wt%; Ag2O 0-0.09wt%; The average particle size of the antibacterial glass powder is 0.05-100um. The plastic uses oxides as antibacterial materials. The properties of the ox...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of plastic with antibacterial function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of plastic preparation method with antibacterial function of the present embodiment, comprises the following steps:

[0028] Step 1: Mix polypropylene resin, modified polyester fiber, and water hyacinth fiber composite polycarbonate, and add them to the reaction kettle. The reaction temperature is 145°C, the stirring speed is 115r / min, and the stirring time is 15min. Then Then add expanded chlorite powder, continue to stir for 35 minutes, then add epoxy silane coupling agent KH-560 and tert-butylhydroquinone in turn, increase the stirring speed to 155r / min, and stir for 35 minutes to obtain mixture A;

[0029] In step 2, the mixture A, tetra-n-butyl titanate and polyvinyl alcohol obtained in step 1 are sent to a twin-screw extruder for extrusion, the extrusion temperature is 155°C, and extrusion cooling is formed to obtain the present invention. Antimicrobial plastic.

[0030] The preparation method of the modified polyester fiber of the present embodiment is: ...

Embodiment 2

[0039] A kind of plastic preparation method with antibacterial function of the present embodiment, comprises the following steps:

[0040] Step 1: Mix polypropylene resin, modified polyester fiber, and water hyacinth fiber composite polycarbonate, and add them to the reaction kettle. The reaction temperature is 155°C, the stirring speed is 125r / min, and the stirring time is 25min. Then Then add expanded chlorite powder, continue stirring for 45 minutes, then add epoxy silane coupling agent KH-560 and tert-butylhydroquinone in sequence, increase the stirring speed to 175r / min, and stir for 45 minutes to obtain mixture A;

[0041] Step 2. The mixture A, tetra-n-butyl titanate and polyvinyl alcohol obtained in step 1 are sent to a twin-screw extruder for extrusion. The extrusion temperature is 165°C. Extrusion is cooled and formed to obtain the present invention. Antimicrobial plastic.

[0042]The preparation method of the modified polyester fiber of the present embodiment is: ...

Embodiment 3

[0051] A kind of plastic preparation method with antibacterial function of the present embodiment, comprises the following steps:

[0052] Step 1: Mix polypropylene resin, modified polyester fiber, and water hyacinth fiber composite polycarbonate, and add them to the reaction kettle. The reaction temperature is 150°C, the stirring speed is 120r / min, and the stirring time is 20min. Then Then add expanded chlorite powder, continue stirring for 40 minutes, then add epoxy silane coupling agent KH-560 and tert-butylhydroquinone in sequence, increase the stirring speed to 160r / min, and stir for 40 minutes to obtain mixture A;

[0053] Step 2, the mixture A, tetra-n-butyl titanate, and polyvinyl alcohol obtained in step 1 are sent to a twin-screw extruder for extrusion, the extrusion temperature is 160 ° C, extrusion cooling is formed, and the present invention has Antimicrobial plastic.

[0054] The preparation method of the modified polyester fiber of the present embodiment is:

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of plastic with an antibacterial function. The method comprises the following steps that 1, polypropylene resin, modified polyester fibers and eichhornia crassipes fiber composite polycarbonate are mixed, and are added into a reaction kettle, a reaction temperature is 145-155 DEG C, a stirring rotating speed is 115-125 r/min, stirring time is 15-25 min,and then swelling chlorite powder is added. The invention aims to provide the preparation method of the plastic with the antibacterial function; the antibacterial function of the plastic is greatly improved compared with that in the prior art, and the plastic has a high use value and good application prospects.

Description

technical field [0001] The invention relates to the technical field of plastic preparation, in particular to a method for preparing plastic with antibacterial function. Background technique [0002] With the continuous improvement of people's living standards, people's requirements for plastics are becoming more and more stringent, and antibacterial plastics are also rising. Plastics that inhibit or kill bacteria, algae, and even viruses keep themselves clean by inhibiting the reproduction of microorganisms. [0003] The existing Chinese patent literature (publication number: CN103627197B) discloses an antibacterial thermoplastic composition and a preparation method thereof. The composition includes the following components blended: thermoplastic resin: 100 parts by weight; antibacterial agent 0.3 to 3 parts by weight wherein the antibacterial agent is antibacterial glass powder, including the following components by weight percentage: P2O5 30-40wt%; Na2O or K2O 6-18wt%, Zn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L67/00C08L69/00C08L5/08C08K13/02C08K3/38C08K3/22C08K3/34
CPCC08K2003/0806C08K2003/2296C08K2003/387C08K2201/011C08L23/12C08L2205/16C08L67/00C08L69/00C08L5/08C08K13/06C08K9/12C08K3/08C08K3/38C08K3/22C08K3/346
Inventor 武娟
Owner HEFEI WANZHIJING DOORS & WINDOWS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap