Bamboo dyer fiber spunlaced non-woven soft towel base fabric and preparing method

A Bamboo Deer fiber and non-woven technology is applied in the field of Bamboo Deer fiber spunlace non-woven soft towel base fabric and preparation field, which can solve the problem of poor net-forming effect of pure polyester fiber, high quality resistance of polyester fiber, and shrinkage and deformation of fabric. Large and other problems, to achieve the effect of good hygroscopicity, soft hand feel, and less surface fluff

Inactive Publication Date: 2018-12-21
ZHONGYUAN ENGINEERING COLLEGE
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the wet breaking strength is small, and the shrinkage deformation of the fabric made of pure viscose fiber is large
The strength of viscose fiber is lower than that of cotton fiber, it is not washable, its elongation at break is higher than that of cotton fiber, it has poor wear resistance, it is easy to deform under small load, it has p...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A preparation method of bamboo dale fiber spunlace nonwoven soft towel base cloth, the steps are as follows:

[0046] Utilizing the above technological process, equipment and technical measures, etc., the spunlaced nonwoven base fabric of bamboo dale fiber has been developed, wherein, it is made of the raw materials with the following weight ratio: the weight content of bamboo dale fiber The weight content of jade fiber accounts for 10%, the weight content of antibacterial viscose fiber accounts for 5%, the weight content of viscose fiber accounts for 45%, the weight content of antibacterial polyester fiber accounts for 5%, and the weight content of polyester fiber accounts for 25%, the performance index of the spunlace nonwoven soft towel base fabric is: the actual weight is 45.08g / m 2 , average thickness 0.37mm; longitudinal strength 41.5N, transverse strength 46.2N, longitudinal and transverse strength ratio 0.90:1; longitudinal elongation at break 25.54%, transverse...

Embodiment 2

[0048] A preparation method of bamboo dale fiber spunlace nonwoven soft towel base cloth, the steps are as follows:

[0049] Utilizing the above technological process, equipment and technical measures, etc., the spunlaced nonwoven base fabric of bamboo dale fiber has been developed, wherein, it is made of the raw materials with the following weight ratio: the weight content of bamboo dale fiber The weight content of jade fiber accounts for 5%, the weight content of antibacterial viscose fiber accounts for 25%, the weight content of viscose fiber accounts for 30%, and the weight content of polyester fiber accounts for 25%. The performance index of the cloth is: the actual weight is 50.0g / m 2 , average thickness 0.30~0.49mm; longitudinal strength 37.5N, transverse strength 42.4N, ratio of longitudinal and transverse strength 0.88:1; longitudinal elongation at break 24.63%, transverse elongation at break 38.4%, ratio of longitudinal and transverse elongation at break 0.64 :1; lo...

Embodiment 3

[0051] A preparation method of bamboo dale fiber spunlace nonwoven soft towel base cloth, the steps are as follows:

[0052] Utilizing the above technological process, equipment and technical measures, etc., the spunlaced nonwoven base fabric of bamboo dale fiber has been developed, wherein, it is made of the raw materials with the following weight ratio: the weight content of bamboo dale fiber The weight content of antibacterial viscose fiber accounts for 25%, the weight content of viscose fiber accounts for 40%, the weight content of antibacterial polyester fiber accounts for 5%, and the weight content of polyester fiber accounts for 15%. The performance index of the base cloth is: the actual weight is 50.1g / m 2 , average thickness 0.31mm; longitudinal strength 33.25N, transverse strength 40.12N, ratio of longitudinal and transverse strength 0.83:1; longitudinal elongation at break 24.73%, transverse elongation at break 37.8%, ratio of longitudinal and transverse elongation ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
The average thicknessaaaaaaaaaa
Longitudinal strengthaaaaaaaaaa
Lateral forceaaaaaaaaaa
Login to view more

Abstract

The invention provides a bamboo dyer fiber spunlaced non-woven soft towel base fabric and a preparing method. The soft towel base fabric comprises, by weight, 5-20% of bamboo dyer fiber, 0-50% of jadefiber, 0-70% of viscose, 0-70% of polyester fiber, 0-70% of antibacterial viscose and 0-70% of antibacterial polyester fiber. The bamboo dyer fiber spunlaced non-woven soft towel base fabric has theadvantage of being soft in hand feel, high in water absorbing capacity, moisture absorbing capacity, breathability and moisture permeability, good in appearance, few in surface flock, free of fiber tow and the like; the base fabric can soften skin cuticle, expand pores, promote sweat gland secretion, accelerate metabolism, care the pores and tighten skin and has a quite good skin cleaning and caring effect; meanwhile, wrinkles on the skin can be prevented, the water conservation of the skin can be promoted, the skin is better moistened and smoothened, and it is ensured that the skin is rosy and rich in color and luster.

Description

technical field [0001] The invention relates to the field of health-care spunlace cloth for medical textiles, in particular to a spunlace nonwoven soft towel base cloth of bamboo dyer fiber and a preparation method thereof. Background technique [0002] In recent years, with the gradual improvement of people's material life quality and health care awareness, disposable spunlace nonwoven wet wipes and soft wipes that cleanse, moisturize, facilitate, clean and disinfect have become necessities in people's daily life. Its uses are increasingly functional, diversified, diverse, health-care and convenient, etc., and the market demand is increasing. Various functional wet wipes and soft towels are popular among people. Antibacterial fibers, etc. The wet wipes and soft wipes developed by the developed spunlace nonwovens not only have the functions of cleaning, moisturizing, moisturizing, antibacterial, disinfection, sanitation, and reliability, but also have no lint, no qualitative...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/492D04H1/4382
CPCD04H1/4382D04H1/492D10B2201/24D10B2331/04D10B2401/13
Inventor 赵博
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap