Fluorine-containing polymer auxiliary master batch with effect of eliminating melt fracture

A melt fracture, polymer technology, applied in the field of processing aids, can solve the problems of not mentioning surface defects, reducing the amount of fluoroelastomer used, difficult to disperse, etc., to achieve good surface finish, improve fluidity, and improve shark skin Effect

Inactive Publication Date: 2019-01-04
QUANGANG PETROCHEM RES INST OF FUJIAN NORMAL UNIV
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Chinese patent CN102399407A discloses a preparation method of a modified fluorine-containing processing aid. A modified fluorine-containing processing aid is obtained by polymerizing a modified fluoroelastomer with a polymer; the modified fluorine-containing processing aid Effectively increase the bonding time between fluoroelastomers and metals, reduce the amount of fluoroelastomers used, increase the compatibility of fluoroelastomers and polymers, and improve the processing performance of resins, but there is no Mention that this modification aid improves surface defects during polymer extrusion processing
[0006] In view of the UHMWPE / PE alloy pipe extrusion process application of fluoropolymer additive masterbatch to eliminate surface defects, the present invention has developed a fluoropolymer additive masterbatch, and by adding the masterbatch to In UHMWPE / PE alloy, the extrusion process was initially explored
In addition, the form of fluorine-containing polymer additives is powder, and powder additives are directly added to granular polyethylene materials, which has problems such as difficulty in dispersion and dust pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A fluoropolymer additive masterbatch with the effect of eliminating melt fracture, the following method is used:

[0028] 1. A fluorine-containing polymer additive masterbatch with the effect of eliminating melt fracture, characterized in that: according to the weight percentage formula:

[0029] HDPE98

[0030] Vinylidene fluoride-hexafluoropropylene copolymer 2.

[0031] 2. A method for preparing a fluorine-containing polymer additive masterbatch with the effect of eliminating melt fracture, comprising the steps of:

[0032] A. Drying: Dry vinylidene fluoride-hexafluoropropylene copolymer and HDPE in a drying oven for 8 h;

[0033] B. Weighing: weigh the dried vinylidene fluoride-hexafluoropropylene copolymer and HDPE according to the weight percentage ratio;

[0034] C. Blending: each component weighed is placed in a high-speed kneader and mixed at a high speed for 5 min, and the speed of the high-speed mixer is 2500 rpm;

[0035] D. Extrusion granulation: Put th...

Embodiment 2

[0037] A fluoropolymer additive masterbatch with the effect of eliminating melt fracture, the following method is used:

[0038] 1. A fluorine-containing polymer additive masterbatch with the effect of eliminating melt fracture, characterized in that: according to the weight percentage formula:

[0039] LLDPE 98

[0040] Vinylidene fluoride-hexafluoropropylene copolymer 2.

[0041] 2. A method for preparing a fluorine-containing polymer additive masterbatch with the effect of eliminating melt fracture, comprising the steps of:

[0042] A. Drying: Dry vinylidene fluoride-hexafluoropropylene copolymer and LLDPE in a drying oven for 8 h;

[0043] B. Weighing: weigh the dried vinylidene fluoride-hexafluoropropylene copolymer and LLDPE according to the weight percentage ratio;

[0044]C. Blending: each component weighed is placed in a high-speed kneader and mixed at a high speed for 5 min, and the rotating speed of the high-speed mixer is 2500rpm;

[0045] D. Extrusion granulat...

Embodiment 3

[0047] A fluoropolymer additive masterbatch with the effect of eliminating melt fracture, the following method is used:

[0048] 1. A fluorine-containing polymer additive masterbatch with the effect of eliminating melt fracture, characterized in that: according to the weight percentage formula:

[0049] LDPE98

[0050] Vinylidene fluoride-hexafluoropropylene copolymer 2.

[0051] 2. A method for preparing a fluorine-containing polymer additive masterbatch with the effect of eliminating melt fracture, comprising the steps of:

[0052] A Drying: Dry the vinylidene fluoride-hexafluoropropylene copolymer and LDPE in a drying oven for 8 h;

[0053] B. Weighing: weigh the dried vinylidene fluoride-hexafluoropropylene copolymer and LDPE according to the weight percentage ratio;

[0054] C. Blending: each component weighed is placed in a high-speed kneader and mixed at a high speed for 5 min, and the rotating speed of the high-speed mixer is 2500 rpm;

[0055] D. Extrusion granula...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses fluorine-containing polymer auxiliary master batch with an effect of eliminating melt fracture. By using the fluorine-containing polymer auxiliary master batch to improve the flowability of UHMWPE / PE alloy, the 'sharkskin' phenomenon in alloy extrusion is reduced. According to the technical scheme, the fluorine-containing polymer auxiliary master batch is prepared by usingfluorine-containing polymer auxiliaries as the additives and using different types of polyethylene materials as the matrix resin. The fluorine-containing polymer auxiliary master batch is prepared by,by mass percentage, 95-99% of polyethylene resin and 1-5% of fluorine-containing polymer auxiliaries. A preparation method of the fluorine-containing polymer auxiliary master batch includes the stepsof firstly, drying; secondly, weighing materials; thirdly, mixing; fourthly, performing extrusion granulation. The prepared fluorine-containing polymer auxiliary master batch is good in surface smoothness, capable of improving the 'sharkskin' phenomenon of the UHMWPE / PE alloy, capable of increasing productivity and lowering energy consumption and beneficial to the forming of UHMWPE / PE alloy pipes.

Description

technical field [0001] The invention relates to a processing aid, in particular to a fluorine-containing polymer processing aid masterbatch with the effect of eliminating melt fracture and a preparation method thereof. Background technique [0002] In recent years, phenomena such as "shark skin" melt flow instability and melt cyclic rupture have become one of the most important problems that have to be solved in thermoplastic polymer processing. Especially for UHMWPE / PE alloys, melt fracture not only limits the efficiency of extrusion processing, product dimensional stability and surface gloss, but also seriously restricts the development of processing economy. Therefore, efficient processing and molding of polymers depends on effectively solving melt fracture problems such as "shark skin". In order to solve this problem, many polymer additives came into being. Polymer Processing Additives (PPA) improved from fluoroelastomers and fluoroplastics is a new type of processing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L27/16C08L27/18C08J3/22
CPCC08J3/226C08J2323/06C08J2423/06C08J2423/08C08J2427/16C08J2427/18
Inventor 陈庆华成惠斌钱庆荣肖荔人黄宝铨薛珲罗永晋曾令兴刘欣萍
Owner QUANGANG PETROCHEM RES INST OF FUJIAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products