Water-permeable film for plant protection and preparation method thereof

A technology of permeable membrane and polymer, applied in plant protection, plant protection cover, botanical equipment and methods, etc., can solve the problems of crop yield reduction, soil compaction, residual membrane and its debris increase, etc., to ensure the effect of normal growth

Inactive Publication Date: 2019-01-11
温州莲华环保科技有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the increase in the use of agricultural film and its refractory property will increase the residual film and its fragments in the soil, causing soil compaction and poor permeability, resulting in a reduction in crop production, and its difficulty in recycling leads to it being discarded in nature. environmental hazards
For crops cultivated in agricultural film greenhouses, if the transmitted sunlight is too strong, it may cause adverse effects such as burns on the crops

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present invention proposes a kind of water-permeable film for plant protection, the formula of its raw material by weight is as follows: 45 parts of low-density polyvinyl chloride, 25 parts of PVB polymer, 12 parts of carbon black type black polyester masterbatch, 7 parts of light stabilizer , 7 parts of permethrin, 3 parts of glyceryl monostearate, 3 parts of organic vanadium salt, 3 parts of antioxidant, 1 part of anti-aging agent, and 1 part of ultraviolet absorber.

[0022] The present invention also provides a preparation process of a water-permeable membrane for plant protection, comprising the following steps:

[0023] S1. Weigh low-density polyvinyl chloride, PVB polymer and carbon black type black polyester masterbatch in proportion, and place them slowly in the mixing melting machine in turn. After the addition is completed, raise the temperature in the mixing melting machine to 220 degrees Celsius, so that the above-mentioned raw materials can be smelted ...

Embodiment 2

[0029] The present invention proposes a kind of water-permeable film for plant protection, the formula of its raw material by weight is as follows: 50 parts of low-density polyvinyl chloride, 28 parts of PVB polymer, 13 parts of carbon black type black polyester masterbatch, 7.5 parts of light stabilizer , 7.5 parts of permethrin, 3.5 parts of glyceryl monostearate, 3.5 parts of organic vanadium salt, 3.5 parts of antioxidant, 1.5 parts of anti-aging agent, and 1.5 parts of ultraviolet absorber.

[0030] The present invention also provides a preparation process of a water-permeable membrane for plant protection, comprising the following steps:

[0031] S1. Weigh low-density polyvinyl chloride, PVB polymer and carbon black type black polyester masterbatch in proportion, and place them slowly in the mixing melting machine in turn. After the addition is completed, raise the temperature in the mixing melting machine to 225 degrees Celsius, so that the above-mentioned raw materials...

Embodiment 3

[0037] The present invention proposes a kind of water-permeable film for plant protection, the formula of its raw materials by weight is as follows: 55 parts of low-density polyvinyl chloride, 30 parts of PVB polymer, 14 parts of carbon black type black polyester masterbatch, 8 parts of light stabilizer , 8 parts of permethrin, 4 parts of glyceryl monostearate, 4 parts of organic vanadium salt, 4 parts of antioxidant, 2 parts of antiaging agent, and 2 parts of ultraviolet absorber.

[0038] The present invention also provides a preparation process of a water-permeable membrane for plant protection, comprising the following steps:

[0039] S1. Weigh low-density polyvinyl chloride, PVB polymer and carbon black type black polyester masterbatch in proportion, and place them slowly in the mixing melting machine in turn. After the addition is completed, raise the temperature in the mixing melting machine to 230 degrees Celsius, so that the above-mentioned raw materials can be smelte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a water-permeable film for plant protection. The water-permeable film comprises, by weight, 45-65 parts of low-density polyvinyl chloride, 25-35 parts of a PVB polymer, 12-16 parts of carbon black type black polyester masterbatch, 7-9 parts of a light stabilizer, 7-9 parts of permethrin, 3-5 parts of glyceryl monostearate, 3-5 parts of an organic vanadium salt, 3-5 parts ofan antioxidant, 1-3 parts of an anti-aging agent and 1-3 parts of a UV absorber. The invention also discloses a preparation method of the water seepage film for plant protection. The water-permeablefilm can effectively shield the crops so that the crops are prevented from being transmitted by the sunlight too strongly, and the light stabilizer can evenly distribute lights in the water-permeablefilm. The permethrin can treat pests in soil so that the growth of crops is not influenced and the normal growth of plants is guaranteed.

Description

technical field [0001] The invention relates to the technical field of preparation of water-permeable membranes, in particular to a water-permeable membrane for plant protection and a preparation process. Background technique [0002] The main component of agricultural permeable membrane is polyethylene or polypropylene, which is currently the most produced plastic product in the world. The use of agricultural film is beneficial to the growth and development of crops and increases crop yield. However, the increase in the use of agricultural film and its refractory property will increase the residual film and its fragments in the soil, causing soil compaction and poor permeability, resulting in a reduction in crop production, and its difficulty in recycling leads to it being discarded in nature. The environmental hazards are great. For crops cultivated in agricultural film greenhouses, if the transmitted sunlight is too strong, there may be adverse effects such as burns on ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L29/14C08L67/00C08K13/02C08K5/101C08K5/103C08K3/04C08J3/22A01G13/02
CPCA01G13/0275C08J3/226C08J2467/00C08K3/04C08L27/06C08L2203/16C08L2205/03C08L29/14C08L67/00C08K13/02C08K5/101C08K5/103
Inventor 薛立新林旭杰林玉生高从堦
Owner 温州莲华环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap