Polishing solution for stainless steel processing and preparation method of polishing solution

A technology of polishing liquid and stainless steel, applied in polishing compositions containing abrasives, etc., can solve the problems of high raw material cost, complicated preparation method, unsuitable for industrialized popularization and production, etc., and achieves low surface roughness, simple method and good cooling. effect of effect

Inactive Publication Date: 2019-01-11
合肥久新不锈钢厨具有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The preparation methods of the above two prior art are relatively complicated, and the c...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A polishing solution for stainless steel processing, comprising the following raw materials in parts by weight: 12 parts of sulfated castor oil, 11 parts of cocamidopropyl amine oxide, 23 parts of modified silicon dioxide, 11 parts of ethyl silicone oil, and 14 parts of abrasive , 9 parts of silica sol, 6 parts of brightener, 9 parts of compound additive, 13 parts of decaglycerol decaoleate, 9 parts of ethanol solution, 8 parts of surfactant, 5 parts of pH regulator, 9 parts of corrosion inhibitor parts and 20 parts of deionized water.

[0033] A preparation method of a polishing liquid for stainless steel processing, comprising the following preparation steps:

[0034] a. Mix the abrasive, decaglycerol decaoleate and ethanol solution into the reaction kettle, raise the temperature to 65°C, heat the reaction for 20 minutes, then cool to room temperature, then add the surfactant, and carry out ultrasonic dispersion treatment for 15 minutes to obtain a mixture ;

[0035...

Embodiment 2

[0045] A polishing liquid for stainless steel processing, comprising the following raw materials in parts by weight: 11 parts of sulfated castor oil, 11 parts of cocamidopropyl amine oxide, 22 parts of modified silicon dioxide, 11 parts of ethyl silicone oil, and 15 parts of abrasive , 11 parts of silica sol, 6 parts of brightener, 15 parts of compound additive, 13 parts of deca-polyglycerol decaoleate, 9 parts of ethanol solution, 5 parts of surfactant, 6 parts of pH regulator, 7 parts of corrosion inhibitor parts and 20 parts of deionized water.

[0046] A preparation method of a polishing liquid for stainless steel processing, comprising the following preparation steps:

[0047] a. Mix the abrasive, decaglycerol decaoleate and ethanol solution into the reaction kettle, raise the temperature to 68°C, heat the reaction for 24 minutes, then cool to room temperature, then add the surfactant, and carry out ultrasonic dispersion treatment for 18 minutes to obtain a mixture ;

...

Embodiment 3

[0058] A polishing liquid for stainless steel processing, comprising the following raw materials in parts by weight: 10 parts of sulfated castor oil, 11 parts of cocamidopropyl amine oxide, 21 parts of modified silicon dioxide, 12 parts of ethyl silicone oil, and 16 parts of abrasive , 12 parts of silica sol, 8 parts of brightener, 13 parts of compound additive, 12 parts of deca-polyglycerol decaoleate, 8 parts of ethanol solution, 6 parts of surfactant, 7 parts of pH regulator, 7 parts of corrosion inhibitor parts and 25 parts of deionized water.

[0059] A preparation method of a polishing liquid for stainless steel processing, comprising the following preparation steps:

[0060] a. Mix the abrasive, decaglycerol decaoleate and ethanol solution into the reaction kettle, raise the temperature to 65°C, heat and react for 24 minutes, then cool to room temperature, then add a surfactant, perform ultrasonic dispersion treatment for 18 minutes, and obtain a mixture ;

[0061] b....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a polishing solution for stainless steel processing and a preparation method of the polishing solution. The polishing solution is prepared from the following components: sulfated castor oil, cocamidopropyl dimethylamine oxide, modified silica, ethyl silicone oil, an abrasive, silica sol, a brightener, a compound additive, polyglyceryl-10 decaoleate, an ethanol solution, a surfactant, a pH regulator, a corrosion inhibitor and deionized water. The polishing solution prepared by the invention is simple in method, low in cost, excellent in polishing effect, high in polishingprecision and high in polishing efficiency, has excellent anti-rust and easy-to-clean effects, and is harmless to the human body and the environment and suitable for large-scale production.

Description

technical field [0001] The invention belongs to the technical field of stainless steel processing, and in particular relates to a polishing liquid for stainless steel processing and a preparation method thereof. Background technique [0002] With the improvement of people's living standards, stainless steel products are becoming more and more widely used in chemical industry, petroleum, home appliances, hardware, food, machinery manufacturing and other fields, and the requirements for stainless steel products are getting higher and higher, not only must be durable, but also To achieve the appearance of mirror, bright, delicate and pleasing effect. [0003] At present, the commonly used methods of polishing stainless steel mainly include: (1) Electrochemical polishing: Although the effect of electrochemical polishing is excellent, the energy consumption is high. For complex parts, not only special fixtures are required, but also for anodes, cathodes, and blind holes. For bli...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09G1/02
CPCC09G1/02
Inventor 辛松
Owner 合肥久新不锈钢厨具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap