Waterborne calcium stearate emulsion and preparation method thereof

A technology of water-based calcium stearate and calcium stearate, which is applied in the direction of coating, etc., can solve the problems of easy precipitation, high production cost, flocculation and stratification, etc., achieve good dispersion effect, simplify production process, and save production cost Effect

Active Publication Date: 2019-02-19
广州正浩新材料科技有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Even if the existing water-based calcium stearate emulsion is added with emulsifier and dispersant, the dispersion effect is not good, it is easy to precipitate, and flocculation and stratification will occur after long-term storage
In addition, the existing method requires high-speed stirring and grinding under heating conditions in the process of preparing aqueous calcium stearate emulsion, the production process is complicated, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The preparation of embodiment 1 aqueous calcium stearate emulsion

[0027] Composition in parts by weight of raw materials: 38 parts of calcium stearate; 15 parts of emulsifier; 0.5 part of polyoxyethylene polyoxypropanolamine ether; 0.3 part of methyl p-hydroxybenzoate; 50 parts of water;

[0028] Described emulsifying agent is prepared by following method:

[0029] (1) Thionyl chloride was added dropwise to 11-trans-octadecenoic acid, the reaction temperature was controlled at 55°C, and the reaction was stirred for 3 hours to obtain 11-trans-octadecenoic acid chloride;

[0030] (2) adding sorbitol and sinapyl alcohol to the acetone solution, then adding 11-trans-octadecenoic acid chloride, reacting at 35°C for 2 hours, washing the product to obtain the emulsifier;

[0031] The molar ratio of 11-trans-octadecenoic acid and thionyl chloride described in step (1) is 1:1.8;

[0032] In step (2), the molar ratio of sorbitol, sinapyl alcohol and 11-trans-octadecenoic acid...

Embodiment 2

[0035] The preparation of embodiment 2 aqueous calcium stearate emulsions

[0036] Composition in parts by weight of raw materials: 25 parts of calcium stearate; 10 parts of emulsifier; 0.3 part of polyoxyethylene polyoxypropanolamine ether; 0.5 part of methyl p-hydroxybenzoate; 40 parts of water;

[0037] Described emulsifying agent is prepared by following method:

[0038] (1) Thionyl chloride was added dropwise to 11-trans-octadecenoic acid, the reaction temperature was controlled at 60°C, and the reaction was stirred for 2 hours to obtain 11-trans-octadecenoic acid chloride;

[0039] (2) adding sorbitol and sinapyl alcohol to the acetone solution, then adding 11-trans-octadecenoic acid chloride, reacting at 30°C for 3 hours, washing the product to obtain the emulsifier;

[0040] The molar ratio of 11-trans-octadecenoic acid and thionyl chloride described in step (1) is 1:1.5;

[0041] In step (2), the molar ratio of sorbitol, sinapyl alcohol and 11-trans-octadecenoic aci...

Embodiment 3

[0044] The preparation of embodiment 3 aqueous calcium stearate emulsion

[0045] Composition in parts by weight of raw materials: 55 parts of calcium stearate; 15 parts of emulsifier; 0.5 part of polyoxyethylene polyoxypropanolamine ether; 0.5 part of methyl p-hydroxybenzoate; 60 parts of water;

[0046] Described emulsifying agent is prepared by following method:

[0047] (1) Thionyl chloride was added dropwise to 11-trans-octadecenoic acid, the reaction temperature was controlled at 50°C, and the reaction was stirred for 4 hours to obtain 11-trans-octadecenoic acid chloride;

[0048] (2) adding sorbitol and sinapyl alcohol to acetone solution, then adding 11-trans-octadecenoic acid chloride, reacting at 40° C. for 1.5 h, washing the product to obtain the emulsifier;

[0049] The molar ratio of 11-trans-octadecenoic acid and thionyl chloride described in step (1) is 1:2;

[0050] In step (2), the molar ratio of sorbitol, sinapyl alcohol and 11-trans-octadecenoic acid chlor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of calcium stearate and particularly discloses waterborne calcium stearate emulsion and a preparation method thereof. The waterborne calcium stearate emulsion is prepared from, by weight, 25-60 parts of calcium stearate, 10-20 parts of an emulsifying agent, 0.1-1 part of a defoaming agent, 0.1-1 part of preservatives and 40-70 parts of water. The waterborne calcium stearate emulsion is simple in production process, excellent in dispersion effect and available for long-time storage and placement.

Description

technical field [0001] The invention relates to the technical field of calcium stearate, in particular to an aqueous calcium stearate emulsion and a preparation method thereof. Background technique [0002] Calcium stearate emulsion is a product with the molecular formula Ca(C 17 h 35 COO) 2 It is a white viscous liquid and is a lubricant with excellent performance. It can be used in fields such as starch, casein or emulsion paint. Because calcium stearate is insoluble in water, it is necessary to add emulsifier and dispersant in the process of preparing aqueous calcium stearate emulsion to achieve the dispersion effect. Even if the existing water-based calcium stearate emulsion is added with an emulsifier and a dispersant, the dispersion effect is not good, and it is easy to precipitate, and the phenomenon of flocculation and stratification will occur when it is left for a long time. In addition, the existing method requires high-speed stirring and grinding under heati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/63C09D7/65
CPCC09D7/63C09D7/65
Inventor 李英
Owner 广州正浩新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com