Heavy load bearing lubricating grease and preparation method thereof

A bearing lubrication, heavy-duty technology, applied in the field of lubricating grease, can solve the problems affecting the service life of vehicle bearings and lubricating grease, poor water resistance, extreme pressure and wear resistance, poor shear stability, etc., and achieve excellent mechanical stability. and adhesion, reducing pitting and preventing wear

Inactive Publication Date: 2019-03-08
安徽中天石化股份有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] For the lubrication requirements of heavy-duty vehicle hub bearings, some different types of greases have been developed at home and abroad, mainly lithium-composite greases and urea-based greases, and a variety of extreme pressure and anti-wear agents are used in conjunction with them, but there are Poor shear stability, large oil separation, poor water resistance and extreme pressure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heavy load bearing lubricating grease and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A heavy-duty bearing lubricating grease comprises the following raw materials in parts by weight:

[0044]8 parts of octadecylamine, 4 parts of MDI (diphenylmethane, 4'-diisocyanate), 8 parts of high molecular fatty acid, 6 parts of low molecular acid, 7 parts of lithium hydroxide, 20 parts of water, 60 parts of base oil A, base 40 parts of oil B, 0.2 parts of antioxidant A, 0.6 parts of antioxidant B, 0.2 parts of antirust agent, 0.2 parts of extreme pressure and antiwear agent A, 1 part of extreme pressure and antiwear agent B, 5 parts of tackifier, stable 2 parts of agent, 6 parts of structure improver.

[0045] The high molecular weight fatty acid is 12 hydroxystearic acid.

[0046] The low molecular acid is azelaic acid.

[0047] The base oil A is deeply refined mineral oil 150BS, and the base oil B is PAO-16 synthetic oil.

[0048] The antioxidant A is zinc dialkyldithiocarbamate.

[0049] The antioxidant B is di-tert-butyl-p-cresol.

[0050] The rust inhibit...

Embodiment 2

[0066] A heavy-duty bearing lubricating grease comprises the following raw materials in parts by weight:

[0067] 10 parts of octadecylamine, 6 parts of MDI (diphenylmethane-4,4'-diisocyanate), 10 parts of high molecular fatty acid, 8 parts of low molecular acid, 8 parts of lithium hydroxide, 25 parts of water, 80 parts of base oil A , 60 parts of base oil B, 0.5 parts of antioxidant A, 0.8 parts of antioxidant B, 0.4 parts of rust inhibitor, 0.5 parts of extreme pressure and antiwear agent A, 2 parts of extreme pressure and antiwear agent B, 15 parts of tackifier , 3 parts of stabilizer, 8 parts of structure improver.

[0068] The high molecular weight fatty acid is 12 hydroxystearic acid.

[0069] The low molecular acid is azelaic acid.

[0070] The base oil A is deeply refined mineral oil 150BS, and the base oil B is PAO-16 synthetic oil.

[0071] The antioxidant A is zinc dialkyldithiocarbamate.

[0072] The antioxidant B is di-tert-butyl-p-cresol.

[0073] The rust i...

Embodiment 3

[0089] A heavy-duty bearing lubricating grease comprises the following raw materials in parts by weight:

[0090] 9 parts of octadecylamine, 5 parts of MDI (diphenylmethane-4,4'-diisocyanate), 9 parts of high molecular fatty acid, 7 parts of low molecular acid, 7.5 parts of lithium hydroxide, 23 parts of water, 70 parts of base oil A , 50 parts of base oil B, 0.4 parts of antioxidant A, 0.7 parts of antioxidant B, 0.3 parts of rust inhibitor, 0.4 parts of extreme pressure and antiwear agent A, 1.5 parts of extreme pressure and antiwear agent B, 10 parts of tackifier , 2.5 parts of stabilizer, 7 parts of structure improver.

[0091] The high molecular weight fatty acid is 12 hydroxystearic acid.

[0092] The low molecular acid is azelaic acid.

[0093] The base oil A is deeply refined mineral oil 150BS, and the base oil B is PAO-16 synthetic oil.

[0094] The antioxidant A is zinc dialkyldithiocarbamate.

[0095] The antioxidant B is di-tert-butyl-p-cresol.

[0096] The ru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses heavy load bearing lubricating grease which comprises the following raw materials in parts by weight: 8-10 parts of octadecylamine, 4-6 parts of MDI (diphenylmethane-4,4'-diisocyanate), 8-10 parts of macromolecule fatty acid, 6-8 parts of low molecular acid, 7-8 parts of lithium hydroxide, 20-25 parts of water, 60-80 parts of base oil A, 40-60 parts of base oil B, 0.2-0.5 parts of an antioxidant A, 0.6-0.8 parts of an antioxidant B, 0.2-0.4 parts of an antirust agent, 0.2-0.5 parts of an extreme pressure anti-wear agent A, 1-2 parts of an extreme pressure anti-wear agent B, 5-15 parts of a tackifier, 2-3 parts of a stabilizer and 6-8 parts of a structure improver. Except the heavy load bearing lubricating grease disclosed by the invention is excellent in high temperature resistance, lubricating property, adhesivity, pumpability, oxidation stability and heat stability, the heavy load bearing lubricating grease is more excellent in shear stability, colloid stability, water resistance and extreme pressure anti-wear property.

Description

technical field [0001] The invention relates to the field of lubricating grease, in particular to heavy-duty bearing lubricating grease and a preparation method thereof. Background technique [0002] Grease is the fifth part of the heavy-duty automobile hub bearing, and its performance directly affects the life of the hub bearing. The life of lubricating grease in heavy-duty automobile hub bearings is an extremely important performance. With the continuous development of economy and technology, "lifetime lubrication" has become the mainstream development trend of hub bearing lubrication, that is, the service life of grease is equal to or exceeds that of hub bearings. The service life of the bearing can reduce the failure rate of the hub bearing, reduce the production cost of the bearing, and improve the productivity. [0003] Heavy-duty automobile hub bearing grease is a semi-solid lubricant. To make the automobile hub bearing grease have a longer service life and better us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M169/06C10N50/10C10N30/08C10N30/06C10N30/02C10N30/10
CPCC10M169/06C10M2201/14C10M2203/1025C10M2205/026C10M2205/0285C10M2207/026C10M2207/1276C10M2207/1285C10M2207/16C10M2217/0456C10M2219/068C10M2223/041C10M2223/043C10N2030/02C10N2030/06C10N2030/08C10N2030/10C10N2050/10C10N2030/26C10N2030/68C10N2010/02C10N2010/04C10N2020/02C10N2060/14
Inventor 高晓谋高荣权何甲生张睿智
Owner 安徽中天石化股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap