A low chrome magnesia chrome brick for glass kiln

A chrome-magnesia-chrome brick and glass kiln technology, which is applied in the field of refractory materials, can solve the problems of hexavalent chromium pollution and other problems, and achieve the effects of improving corrosion resistance, high temperature resistance, and good corrosion resistance

Active Publication Date: 2021-08-31
RUITAI MATERIALS TECHNOLOGY CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problems to be solved by the present invention are: 1) Significantly reduce the amount of Cr in magnesia-chrome bricks used in glass kiln regenerators 2 o 3 content in order to alleviate the environmental pollution of hexavalent chromium in residual magnesia-chrome bricks; 2) in reducing the Cr content of magnesia-chrome brick 2 o 3 content while improving the service life of low-chrome magnesia-chrome bricks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low chrome magnesia chrome brick for glass kiln

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A low-chromium magnesia-chrome brick, expressed in mass percentage, its raw material composition is: 20% fused magnesia with a particle size of 4-2mm, 12% fused magnesia with a particle size of 2-1mm, and fused magnesia-aluminum spinel with a size of 2-1mm 10% magnesia, 26% 1-0mm magnesia chrome sand, 32% fused magnesia <0.088mm, and 3.5% binder sulfurous acid pulp waste liquid and magnesium chloride solution (the specific gravity of the binder is 1.25 ), the raw materials of the above formula are weighed, kneaded, molded, dried, and fired at 1700°C for 8 hours.

Embodiment 2

[0024] The low-chrome magnesia-chrome brick of the present invention is represented by mass percentage, and the raw materials are composed of: 18% fused magnesia with a particle size of 4-2mm, 11% fused magnesia with a particle size of 2-1mm, and fused magnesia-aluminum spinel with a size of 2-1mm 17%, 1-0mm magnesia chrome sand 23%, <0.088mm fused magnesia 31%; in addition, add binder sulfurous acid pulp waste liquid (binder specific gravity 1.35) accounting for 4% of the total mass of all the above-mentioned raw materials, and mix the above The raw materials of the formula are obtained by weighing, kneading, molding, drying, and firing at 1750°C for 7 hours.

Embodiment 3

[0026] The low-chromium magnesia-chrome brick of the present invention is represented by mass percentage, and the raw materials are composed of: 16% of fused magnesia with a particle size of 4-2mm, 10% of fused magnesia with a particle size of 2-1mm, and fused magnesia-aluminum spinel with a size of 2-1mm 16%,; 1-0mm magnesia chrome sand 23%, <0.088mm fused magnesia 35%; in addition, a binder magnesium chloride solution accounting for 4.5% of the total mass of all the above-mentioned raw materials is added (the specific gravity of the binder is 1.30), and the above formula The raw materials are weighed, kneaded, molded, dried, and fired at 1760°C for 5 hours.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-chrome magnesia-chrome brick for a glass kiln, expressed in mass percentage, 25-10% of fused magnesia with a particle size of 4-2mm; 15-10% of fused magnesia with a particle size of 2-1mm; 20-5% of fused magnesia-aluminum spinel with a particle size of 2-1mm; 30-10% of pre-synthesized magnesia-chrome sand with a particle size of 1-0mm; 40-30% of fused magnesia with a particle size of <0.088mm; The total mass of all the above-mentioned raw materials is 3-5% binder. The low-chrome magnesia-chrome brick for glass kilns of the present invention has the performance characteristics of low chromium content, high density, high strength, strong corrosion resistance and good creep resistance. The low-chromium magnesia-chrome brick of the present invention is used in the regenerator of a glass kiln, which can greatly reduce the chromium content of the refractory material, effectively alleviate the pollution of the hexavalent chromium contained in the residual brick to the environment, and at the same time prolong the service life of the kiln and improve the kiln efficiency. The operating rate of the furnace can achieve good economic and social benefits.

Description

technical field [0001] The invention belongs to the technical field of refractory materials, and in particular relates to a low-chrome magnesia-chrome brick for a glass kiln regenerator. Background technique [0002] With the rapid development of the glass industry, the total output of flat glass in my country ranks first in the world. In recent years, the glass industry is facing the challenge of resolving overcapacity and transformation and upgrading. Whether it is float glass or bottle glass, in order to further reduce costs, the technology of using petroleum coke instead of heavy oil as fuel has been widely used in the glass industry. However, the use of petroleum coke is accompanied by increased erosion and a significant shortening of kiln life. [0003] At present, the upper layer of the regenerator of the glass kiln uses magnesia bricks with an MgO content of about 97%; the magnesia bricks originally used in the upper layer of the regenerator with an MgO content of a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/047
CPCC04B35/047C04B2235/3222C04B2235/77C04B2235/96
Inventor 徐琳琳王俊涛徐如林魏瀚闫昕周严敦王杰曾袁林
Owner RUITAI MATERIALS TECHNOLOGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap