Non-curable rubber asphalt waterproof coating and preparation method thereof

A technology of asphalt waterproof coating and non-curing rubber, which is applied in the direction of asphalt coating, other rubber coatings, coatings, etc., and can solve the problem that the heat resistance, low temperature flexibility and extensibility of non-curing rubber asphalt waterproof coating are difficult to meet the quality standards at the same time, softening The problems of high cost of agent and high production cost of non-curing rubber asphalt waterproof coating are achieved, and the effects of resource saving, good adhesion and low cost are achieved.

Inactive Publication Date: 2019-03-29
CHINA PETROLEUM & CHEM CORP
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But at present, the production cost of non-curing rubber asphalt waterproof coating is too high, especially the cost of softener is particularly high, causing many small manufacturers to lower the quality standard in order to make money, and the non-curing rubber asphalt waterproof coating produced has heat resistance, low temperature flexibility and extensibility. Difficulty meeting quality standards at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-curable rubber asphalt waterproof coating and preparation method thereof
  • Non-curable rubber asphalt waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A non-curing rubber asphalt waterproof coating, comprising the following raw materials in parts by weight: 55 parts of 70# road petroleum asphalt, 15 parts of catalytic cracking oil slurry, 6 parts of SBS 1301, 10 parts of coumarone resin, 20 parts of 80 mesh waste rubber powder parts, 15 parts of fly ash, 2.5 parts of NP-10.

[0029] The preparation method comprises the following steps:

[0030] (1) Mix petroleum asphalt and softener, heat to 150°C, stir for 40 minutes at a medium speed, and the stirring speed is 2000r / min;

[0031] (2) Add styrene-butadiene block copolymer to the mixture obtained in step (1), heat to 170°C, stir at a medium speed for 60min, and the stirring speed at a medium speed is 2000r / min;

[0032] (3) Add tackifying resin, waste rubber powder, surfactant and filler to the mixture obtained in step (2) successively, cool down to 140°C, stir at high speed for 60min at a speed of 6000r / min, then cool down to room temperature have to.

Embodiment 2

[0034] A non-curing rubber asphalt waterproof coating, comprising the following raw materials in parts by weight: 50 parts of 70# road petroleum asphalt, 20 parts of catalytic cracking oil slurry, 5 parts of SBS1301, 12 parts of terpene resin, 15 parts of 60 mesh waste rubber powder, Fly ash 20 parts, MOA-91.5 parts.

[0035] The preparation method comprises the following steps:

[0036] (1) Mix petroleum asphalt and softener, heat to 155°C, stir for 30 minutes at medium speed, and the stirring speed at medium speed is 3000r / min;

[0037] (2) Add styrene-butadiene block copolymer to the mixture obtained in step (1), heat to 180°C, stir at a medium speed for 40min, and the stirring speed at a medium speed is 3000r / min;

[0038] (3) Add tackifying resin, waste rubber powder, surfactant and filler to the mixture obtained in step (2) successively, cool down to 150°C, stir at high speed for 50min at a speed of 5000r / min, then cool down to room temperature have to.

Embodiment 3

[0040] A non-curing rubber asphalt waterproof coating, comprising the following raw materials in parts by weight: 45 parts of 90# road petroleum asphalt, 16 parts of catalytic cracking oil slurry, 7 parts of SBS1301, 15 parts of C5 petroleum resin, 10 parts of 100 mesh waste rubber powder , 15 parts of fly ash, 2 parts of SG-40.

[0041] The preparation method comprises the following steps:

[0042] (1) Mix petroleum asphalt and softener, heat to 160°C, stir at a medium speed for 20 minutes, and the stirring speed at a medium speed is 2500r / min;

[0043] (2) Add styrene-butadiene block copolymer to the mixture obtained in step (1), heat to 190°C, stir at a medium speed for 30min, and the medium speed stirring speed is 2500r / min;

[0044] (3) Add tackifying resin, waste rubber powder, surfactant and filler to the mixture obtained in step (2) successively, cool down to 160°C, stir at a high speed for 60min at a speed of 5500r / min, then cool down to room temperature have to.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of building waterproof materials, and in particular, relates to a non-curable rubber asphalt waterproof coating and a preparation method thereof. The non-curable rubber asphalt waterproof coating comprises the following raw materials in parts by weight: 35-65 parts of petroleum asphalt, 5-25 parts of a softener, 2-10 parts of styrene-butadiene block copolymer, 5-20 parts of tackifying resin, 5-25 parts of waste rubber powder, 5-20 parts of a filler and 0.5-3 parts of a surfactant. Cheap catalytic cracking oil slurry is introduced into the raw materials, fly ash collected from flue gas after coal combustion is used as a filler, and the prepared non-curable rubber asphalt waterproof coating can be guaranteed to have excellent high and low temperature performance, good extensibility, difficult curing, good cohesiveness, good flexibility, strong self-healing property and low cost. The invention also provides the preparation method, wherein the preparation method has the advantages of low cost, environmental protection, convenience, safety and reliability.

Description

technical field [0001] The invention belongs to the technical field of building waterproof materials, and in particular relates to a non-curing rubber asphalt waterproof coating and a preparation method thereof. Background technique [0002] Non-curing rubber asphalt waterproof coating is a creeping waterproof coating. It is not a water-based coating, nor is it a solvent-based or reactive coating, but a solvent-free, non-film-forming one-component creeping coating. It has good bonding ability with metal, non-metal and concrete substrates, and has dual functions of waterproof and metal anticorrosion. It is suitable for municipal engineering, subway tunnels, dams, pools, road bridges, roofs, toilets, undergrounds Waterproofing and grouting plugging of other parts. Non-curing rubber asphalt waterproof coating can be used alone or combined with traditional waterproof materials. When used in combination, the waterproof reliability is higher. At present, the waterproof construct...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D153/02C09D119/00C09D7/61C09D7/65
CPCC08K2003/2241C08L2201/08C08L2205/035C08L2207/24C09D195/00C08L53/02C08L19/003C08L91/00C08L45/02C08K3/36C08K3/22C08L45/00C08L57/02
Inventor 张传明高淑美马鹏程贾丽凤许金山刘爱华毛冬梅
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap