A kind of preparation method of cubic structure cosbs thermoelectric compound

A cubic structure and compound technology, applied in the field of preparation of CoSbS-based thermoelectric materials, can solve the problems of high overall cost, high cost of Sb single substance, and inability to obtain high-symmetry cubic structure thermoelectric materials, etc., to achieve low-cost constituent elements and symmetrical crystal structure Sex controllable, high density effect

Inactive Publication Date: 2021-05-18
HENAN POLYTECHNIC UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] CoSb 3 The high symmetry is determined by its molecular structure, and its crystal system itself has high symmetry, but the cost of Sb is very high, resulting in the corresponding CoSb 3 overall high cost
However, for relatively lower-cost thermoelectric materials such as CoSbS, because its own crystal system is not cubic, it is not possible to obtain high-symmetry cubic thermoelectric materials by using the usual preparation methods.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of cubic structure cosbs thermoelectric compound
  • A kind of preparation method of cubic structure cosbs thermoelectric compound
  • A kind of preparation method of cubic structure cosbs thermoelectric compound

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] In this embodiment, the preparation method of the thermoelectric material of the present invention is described in detail by taking the preparation process of CoSbS as an example.

[0047] Such as figure 1 As shown, the method includes the following steps: 1) batching step; 2) wet ball milling step; 3) drying step; 4) pressing step; 5) sintering step.

[0048] The above five steps will be described in detail below.

[0049] 1) Ingredients step

[0050] Co, Sb, and S are used as raw materials, mixed with the molar ratio of CoSbS molecular formula, and placed in a stainless steel ball mill jar. Preferably, the raw materials are Co powder, Sb powder and S powder with a purity ≥ 99.5%; the raw materials are weighed according to the CoSbS stoichiometric ratio, and the total weight is 5g. The ball-to-material ratio can be set to 20:1.

[0051] Preferably, in order to increase the possibility of more CoSbS-based thermoelectric materials, Ni, Se, Te or Fe can be added to the ...

Embodiment 2

[0062] In this example, the thermoelectric material Ni x co 1-x SbS (x=0-0.15).

[0063] In the preparation of thermoelectric materials Ni x co 1-x In the process of SbS, the inventor adopted steps similar to those in Example 1, namely 1) batching step; 2) wet ball milling step; 3) drying step; 4) pressing step; 5) sintering step. Wherein the sintering pressure is 1-3GPa. After the sintered samples were tested by X-ray diffraction, it was found that all samples were orthogonal structures under 1GPa conditions (such as figure 2 ), the sample transforms into a cubic structure after doping 5% Ni under the condition of 2GPa (such as image 3 ), that is, Ni doping can reduce the structural transition pressure of CoSbS.

[0064] In order to characterize the properties of samples with different structures, the Ni-doped samples synthesized at 1GPa and 3GPa were cut and polished, and the resistivity, Seebeck coefficient and thermal conductivity of the samples were tested by LSR-...

Embodiment 3

[0068] In this example, the preparation of thermoelectric material Fe x co 1-x SbS (x=0-0.1).

[0069] In the preparation of thermoelectric materials Fe x co 1-x In the process of SbS, the inventor adopted steps similar to those in Example 1, namely 1) batching step; 2) wet ball milling step; 3) drying step; 4) pressing step; 5) sintering step.

[0070] In this embodiment, the sintering pressure is 2GPa. Figure 6 For the X-ray diffraction pattern of the sample, it is found that the Fe-doped CoSbS sample is still an orthorhombic structure, that is, Fe doping cannot reduce the crystal structure transition pressure of CoSbS as Ni does. Since Fe doping does not improve the symmetry of the crystal structure of CoSbS, and at the same time provides more electrons to the CoSbS compound, the resistivity of the sample increases and the thermoelectric performance decreases (the power factor of Fe-doped CoSbS at room temperature is only 5×10 -5 μWcm -1 K -2 ).

[0071] Simila...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for preparing a CoSbS thermoelectric compound with a cubic structure. The preparation method includes the following steps: Step 1) placing raw materials in a ball mill tank, the raw materials include Co powder, Sb powder and S powder; step 2) wet ball milling; step 3) drying the wet-milled product to obtain a dry powder precursor; step 4) pressing the obtained powder precursor into a block; step 5) compressing The formed block is subjected to high-pressure synthesis to obtain a cubic structure CoSbS compound, wherein, in the step (5), the high-pressure synthesis is carried out on a high-temperature and high-pressure device, and the synthesis process includes wrapping the block sample into a boron nitride insulating tube, and installing Put it into the pyrophyllite synthesis block, and carry out high-pressure synthesis, and the synthesis pressure adopted is greater than 2GPa. The method of the invention can effectively obtain the CoSbS thermoelectric compound with a cubic structure, and the process is simple and the period is short.

Description

technical field [0001] The invention belongs to the technical field of preparation of functional materials, in particular, the invention relates to the field of high-pressure synthesis technology, especially the preparation method of a CoSbS-based thermoelectric material with a cubic structure. Background technique [0002] In recent years, the traditional fossil energy represented by oil has become increasingly exhausted and its price has been rising. At the same time, the extensive use of fossil energy has led to the deterioration of the environment. Energy and environmental issues force people to pay more and more attention to new energy and energy conversion materials. Thermoelectric material is a functional material that can realize direct conversion of heat energy and electric energy. It can be used as a thermoelectric generator, so as to effectively utilize a large amount of waste heat and waste heat in industry. Thermoelectric devices do not have any mechanical mov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01G51/00C01G53/00C01B19/00
CPCC01B19/002C01G51/006C01G53/006C01P2002/72
Inventor 朱红玉宿太超胡强胡美华李尚升贺春元杜保立杨曼曼杜景阳
Owner HENAN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap