Sheet bonding material and magnetic workpiece and preparation method and application thereof

A bonding material and sheet-like technology, which is applied in the direction of film/sheet-like adhesives, magnetic objects, inductors/transformers/magnets, etc., can solve the problem of motor temperature rise, energy loss, and low service life of motor magnets And other issues

Inactive Publication Date: 2019-04-26
ZHEJIANG PANGOOD POWER TECH CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the continuous improvement and improvement of the new energy industry, the development and application of magnetic material motors has entered a new stage. Since the whole piece of magnetic material magnet steel will generate eddy current internal friction during the high-speed motion of the motor, eddy currents are prone to generate heat, which not only makes the The temperature of the motor rises, causing energy loss, and the magnet steel is easy to demagnetize after the temperature rises, causing the motor to fail to work. In order to solve the above-mentioned problems of low service life and high energy consumption of the motor magnet steel, the magnetic material magnet steel is usually divided into pieces Then glued into a whole magnetic steel
[0003] In the prior art, the magnetic steel is bonded with a mixture of glass beads and a binder after being divided into pieces, but the addition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sheet bonding material and magnetic workpiece and preparation method and application thereof
  • Sheet bonding material and magnetic workpiece and preparation method and application thereof
  • Sheet bonding material and magnetic workpiece and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-7

[0095] In the magnetic workpieces of Examples 1-7, the insulating layer of the sheet-like bonding material is glass fiber woven fabric, and the glue layer is epoxy resin glue. The difference is that the thickness and content of the insulating layer and the glue layer are different. For details, refer to the table 1:

[0096] Table 1

[0097]

[0098]

[0099] The result that utilizes the magnetic workpiece of embodiment 1-7 to test can refer to table 2:

[0100] Table 2

[0101]

Embodiment 8

[0103] In this embodiment, the structure of the magnetic workpiece is the same as in Embodiment 4, except that the thickness of the insulating layer is 0.01 mm.

[0104] The shear strength of the magnetic workpiece of this embodiment is 57.4P / MPa. When the insulation effect of the adhesive layer is tested with a digital multimeter, there is a beeping sound, which shows that the magnetic workpiece is conductive. The main reason is that the thickness of the insulating layer is not enough, and the prepared The adhesive layer is easy to be squeezed out when the workpiece is magnetic, and it is difficult to ensure that the thickness of the adhesive layer is consistent.

Embodiment 9

[0106] In this embodiment, the structure of the magnetic workpiece is the same as in Embodiment 4, except that the content of the glue layer is 60 wt%.

[0107] The shear strength of the magnetic workpiece in this embodiment is 60.4P / MPa, and the insulation effect test result is infinite / no sound. However, because the cost of the glue is relatively high, the content of the glue layer is too high, it is partially extruded during the pressure curing process, and the thickness of the adhesive layer is thick, the consistency of the magnetic properties of the product becomes poor, resulting in a relatively large increase in cost.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a sheet bonding material and a magnetic workpiece and a preparation method and application thereof, and relates to the field of magnetic material bonding. The sheet bonding material comprises an insulating layer and glue layers disposed on the two opposite surfaces of the insulating layer. The inventor finds that the sheet bonding material has a simple structure, a uniform thickness, easy control of the thickness of the sheet bonding material, no bubbles and excellent bonding and insulating effects.

Description

technical field [0001] The invention relates to the field of magnetic material bonding, in particular to a sheet-shaped bonding material, a magnetic workpiece, a preparation method and an application thereof. Background technique [0002] With the continuous improvement and improvement of the new energy industry, the development and application of magnetic material motors has entered a new stage. Since the whole piece of magnetic material magnet steel will generate eddy current internal friction during the high-speed motion of the motor, eddy currents are prone to generate heat, which not only makes the The temperature of the motor rises, causing energy loss, and the magnet steel is easy to demagnetize after the temperature rises, causing the motor to fail to work. In order to solve the above-mentioned problems of low service life and high energy consumption of the motor magnet steel, the magnetic material magnet steel is usually divided into pieces And then glued into a who...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01F7/02H01F41/02C09J7/21
CPCC09J7/21C09J2301/124C09J2301/312C09J2400/10C09J2400/123C09J2400/143C09J2400/263C09J2423/046C09J2461/00C09J2463/00C09J2467/006C09J2477/006C09J2479/08H01F7/0215H01F41/0253
Inventor 严建新王智博胡佳俊
Owner ZHEJIANG PANGOOD POWER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap