A kind of preparation technology of anti-pilling modal fabric

A preparation process and anti-pilling technology, applied in fabric surface trimming, dyeing, textile and other directions, can solve problems such as prone to fluffing, pilling, and unsatisfactory comfort of modal fabrics, so as to reduce yarn fluffing and improve reliability The effect of weaving and convenient follow-up operation

Active Publication Date: 2021-08-17
广东绮瑞制衣实业有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the problem that the comfort of existing modal fabrics is not ideal and the traditional modal fabrics are prone to fluffing and pilling in the process of preparation and use, and proposes a preparation process for anti-pilling modal fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The preparation technology of a kind of anti-pilling modal fabric that the present invention proposes comprises the following steps:

[0026] S1. Spinning: Cleaning, carding, and drawing of modal fibers, and then proceed to the roving process with a roving weight of 5.5m / 10m, a front roller of 181r / min, a traction multiple of the rear area of ​​1.18, and a twist coefficient of 85. , and then the yarn obtained in the roving process is twisted in a 2mm circular tube with a twist coefficient of 255. After twisting, the front roller is 189r / min, the traction multiple of the rear area is 1.26 times, and the twist coefficient is 400. The spun yarn process obtains the modal fiber yarn; in the described cleaning process, the speed of the carding needle beater is 440r / min, and the blade protruding height is 1.5mm; in the described carding process, the doffer speed is 18r / min, and the licker-in speed is 760r / min, cylinder speed 320r / min; In the described drawing process, the comb...

Embodiment 2

[0035]The preparation technology of a kind of anti-pilling modal fabric that the present invention proposes comprises the following steps:

[0036] S1. Spinning: Cleaning, carding, and drawing of modal fibers, and then proceed to the roving process with a roving weight of 5.5m / 10m, a front roller of 181r / min, a traction multiple of the rear area of ​​1.18, and a twist coefficient of 85. , and then the yarn obtained in the roving process is twisted in a 2mm circular tube with a twist coefficient of 255. After twisting, the front roller is 189r / min, the traction multiple of the rear area is 1.26 times, and the twist coefficient is 400. The spun yarn process obtains the modal fiber yarn; in the described cleaning process, the speed of the carding needle beater is 440r / min, and the blade protruding height is 2.5mm; in the described carding process, the doffer speed is 18r / min, and the licker-in speed is 760r / min, cylinder speed 320r / min; In the described drawing process, the combi...

Embodiment 3

[0045] The preparation technology of a kind of anti-pilling modal fabric that the present invention proposes comprises the following steps:

[0046] S1. Spinning: Cleaning, carding, and drawing of modal fibers, and then proceed to the roving process with a roving weight of 5.5m / 10m, a front roller of 181r / min, a traction multiple of the rear area of ​​1.18, and a twist coefficient of 85. , and then the yarn obtained in the roving process is twisted in a 3mm circular tube with a twist coefficient of 255. After twisting, the front roller is 189r / min, the traction multiple of the rear area is 1.26 times, and the twist coefficient is 400. In the spinning process, modal fiber yarn is obtained; in the cleaning process, the speed of the carding needle beater is 450r / min, and the blade extension height is 2mm; in the carding process, the doffer speed is 18r / min, and the licker-in speed is 760r / min, cylinder speed 320r / min; In the described drawing process, the combined root number is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation process of an anti-pilling modal fabric, comprising the following steps: S1, spinning: cleaning, carding, drawing, roving, twisting, and spun modal fiber to obtain modal fiber yarn; S2 , warping; S3, sizing: sizing includes the following raw materials: phosphate starch, polyvinyl alcohol 205, sodium bis(2-ethylhexyl) sulfosuccinate, sodium tripolyphosphate and emulsified wax; S4, reeding ; S5, weaving; S6, printing and dyeing: carry out singeing treatment to the modal fabric, the modal fabric after singeing is carried out pre-treatment in the treatment liquid first, carries out rolling after the pre-treatment, then transfers to the dyeing slurry, at 80~ Dye at 90°C for 1 to 2 hours, then soap and hot wash, and cool to room temperature to obtain the anti-pilling modal fabric. The modal fabric prepared by the preparation process proposed by the invention has the characteristics of being soft, not prone to pilling and fluffing, and has high comfort.

Description

technical field [0001] The invention relates to the technical field of textile materials, in particular to a preparation process of an anti-pilling modal fabric. Background technique [0002] Dyer fiber is a kind of cellulose fiber, which belongs to cellulose fiber like rayon cotton, and is a pure man-made fiber. It is made of wood pulp from European shrubs and then processed through a special spinning process. It has good hygroscopicity and weavability, and can be interwoven with other fiber yarns to weave a variety of fabrics. Fabric has broad application prospects in the field of clothing, and is mostly used in the production of underwear. However, fabrics made of modal fibers also have certain disadvantages, such as strong drape and easy fit, which makes the comfort of existing modal fabrics unsatisfactory, and modal fabrics are prone to fuzzing and pilling during preparation and use. . Based on the deficiencies in the prior art, the present invention proposes a prepa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/11D06M15/333D06M13/256D06M11/71D06M13/02D06P1/44D06P3/60D06P1/48D06P1/613D06P1/52D06P1/673D06P1/653D03D15/225D06C9/00D06B3/04D06M101/06
Inventor 唐以锦唐以昌
Owner 广东绮瑞制衣实业有限公司