Medium-temperature repairing rubber material, preparation method thereof and application thereof in a propellant

A rubber material, medium temperature technology, applied in the field of ablation-resistant materials, can solve problems affecting the quality and reliability of engine products, achieve good mechanical properties, good bonding strength, and short vulcanization time

Active Publication Date: 2019-05-07
HUBEI INST OF AEROSPACE CHEMOTECH
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These defects may appear in intermediate products of engine manufacturing (such as composite engine metal-insulation layer molded heads) or in the in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medium-temperature repairing rubber material, preparation method thereof and application thereof in a propellant
  • Medium-temperature repairing rubber material, preparation method thereof and application thereof in a propellant
  • Medium-temperature repairing rubber material, preparation method thereof and application thereof in a propellant

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0045] Example 1

[0046] The composition and formula of the medium temperature repair rubber material are shown in Table 3;

[0047] Table 3 Example 1 Composition and formula of medium temperature repair rubber material

[0048] Serial number

[0049] (1) Material preparation: prepare materials according to the ratio of Example 1 in Table 3;

[0050] (2) Mixing: According to EPDM thin pass 3 times → aramid fiber

[0051] PA→ZnO→SiO 2 →LPO→APP→RD→vulcanizing agent→thin pass 6 times→vulcanization accelerator→thin pass out sheet to refine the middle temperature repair rubber material;

[0052] When preparing rubber compounds, it is necessary to avoid mixing accelerators and vulcanizing agents together and direct contact, in order to prevent the rapid decomposition of hydrogen peroxide compounds. The correct method of mixing operation is to first fully and uniformly disperse the vulcanizing agent into the raw rubber, and then slowly add the vulcanization accelerator. The mixed rubber s...

Example Embodiment

[0057] Example 2

[0058] The composition and formula of medium temperature repair rubber materials are shown in Table 5;

[0059] Table 5 Example 2 Composition and formula of medium temperature repair rubber material

[0060]

[0061]

[0062] (1) Material preparation: prepare materials according to the ratio of Example 2 in Table 5;

[0063] (2) Mixing: According to EPDM thin pass 3 times → aramid fiber

[0064] PA→ZnO→SiO 2 →LPO→APP→RD→vulcanizing agent→thin pass 6 times→vulcanization accelerator→thin pass out sheet to refine EPDM insulation material.

[0065] When preparing rubber compounds, it is necessary to avoid mixing accelerators and vulcanizing agents and direct contact, in order to prevent the rapid decomposition of hydrogen peroxide compounds. The correct method of mixing operation is to first fully and uniformly disperse the vulcanizing agent into the raw rubber, and then slowly add the vulcanization accelerator. The mixed rubber should be stored at low temperature before...

Example Embodiment

[0070] Example 3

[0071] The composition and formula of medium temperature repair rubber materials are shown in Table 7;

[0072] Table 7 Example 3 Composition and formula of medium temperature repair rubber material

[0073] Serial number

[0074] (1) Material preparation: prepare materials according to the ratio of Example 3 in Table 1;

[0075] (2) Mixing: According to EPDM thin pass 3 times → aramid fiber

[0076] PA→ZnO→SiO 2 →LPO→APP→RD→vulcanizing agent→thin pass 6 times→vulcanization accelerator→thin pass out sheet to refine EPDM insulation material.

[0077] When preparing rubber compounds, it is necessary to avoid mixing accelerators and vulcanizing agents together and direct contact, in order to prevent the rapid decomposition of hydrogen peroxide compounds. The correct method of mixing operation is to first fully and uniformly disperse the vulcanizing agent into the raw rubber, and then slowly add the vulcanization accelerator. The mixed rubber should be stored at low t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Wire ablation rateaaaaaaaaaa
Adhesive strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a medium-temperature repairing rubber material, a preparation method thereof and an application thereof in a propellant, belonging to the technical field of ablation-resistantmaterials, in particular to a medium-temperature repairing thermal insulating layer material for a high-energy propellant, a thermal insulating layer capable of rapidly vulcanizing at a medium temperature, and a preparation method thereof. The vulcanization system of the invention adopts a vulcanization system of peroxide and accelerator, the thermal insulating material is difficult to absorb nitrate ester, does not affect the ablation performance of the thermal insulating layer, does not affect the interface adhesion performance of the high-energy propellant, and has good adaptability with the interface of the high-energy propellant.

Description

technical field [0001] The invention relates to a medium-temperature repairing rubber material and its preparation method and application in propellants, belonging to the technical field of ablation-resistant materials, in particular to a medium-temperature repairing insulation layer material for high-energy propellants, which can be used at medium temperatures Heat insulating layer capable of rapid vulcanization and method for making same. Background technique [0002] EPDM thermal insulation material is mainly based on EPDM rubber mixed with additives such as flame retardants, fibers and inorganic fillers. It has low density, aging resistance, ablation resistance, good thermal insulation performance and excellent mechanical properties. It has become the main research and development direction of thermal insulation materials in solid rocket motors. In recent years, it has been successfully applied in the new generation of solid intercontinental missiles, medium-range surfac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/16C08L77/00C08K13/02C08K5/14C08K3/22C08K3/36B29C35/02
Inventor 周俊王明超吴磊陈德宏陈雯陈馨任雯君何永祝凌玲
Owner HUBEI INST OF AEROSPACE CHEMOTECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap