Environment-friendly transparent zinc-based heat stabilizer for PVC and preparation process thereof
A zinc-based heat and stabilizer technology, applied in the field of material chemistry, can solve problems such as poor environmental protection, poor transparency, and high toxicity, and achieve the effects of inhibiting initial discoloration, solving poor transparency, and ensuring low haze.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0018] Example 1:
[0019] Weigh 90 parts of stearic acid, 10 parts of zinc oxide, 0.1 part of hydrogen peroxide, 0.4 part of a mixture of ammonia and potassium hydroxide in any ratio, put the weighed stearic acid into the reaction kettle, heat and stir to 90°C, slowly add zinc oxide , Add hydrogen peroxide to react for 80 minutes, add a mixture of ammonia water and potassium hydroxide in any ratio, cool down after the reaction material is clear and transparent, cool the material after discharging, and crush to obtain powdered transparent zinc stearate after tableting.
[0020] Weigh 15 parts of zinc stearate, 10 parts of hydrotalcite, 5 parts of fumed silica, 2 parts of 6-amino-1,3-dimethyluracil, tris(2-hydroxyethyl) iso 5 parts of cyanurate, 2 parts of glycerol monostearate, 2 parts of pentaerythritol monostearate, 3 parts of phosphite, 1 part of antioxidant, 1 part of external lubricant, 0.5 part of β-diketone, Add the weighed zinc stearate, hydrotalcite, and fumed silica into...
Example Embodiment
[0022] Example 2
[0023] Weigh 110 parts of stearic acid, 20 parts of zinc oxide, 0.5 part of hydrogen peroxide, 0.6 part of a mixture of ammonia and potassium hydroxide in any ratio, put the weighed stearic acid into the reactor, heat and stir to 140°C, slowly add zinc oxide , Add hydrogen peroxide to react for 100 minutes, add a mixture of ammonia water and potassium hydroxide in any proportion, cool down after the reaction material is clear and transparent, discharge the material and cool, pulverize after tabletting to obtain powdered transparent zinc stearate.
[0024] Weigh 35 parts of zinc stearate, 32 parts of hydrotalcite, 15 parts of fumed silica, 8 parts of 6-amino-1,3-dimethyluracil, tris(2-hydroxyethyl) iso 20 parts of cyanurate, 8 parts of glyceryl monostearate, 8 parts of pentaerythritol monostearate, 15 parts of phosphites, 5 parts of antioxidants, 5 parts of external lubricants, 5 parts of β-diketones, Add the weighed zinc stearate, hydrotalcite, and fumed silica ...
Example Embodiment
[0026] Example 3
[0027] Weigh 100 parts of stearic acid, 15 parts of zinc oxide, 0.2 part of hydrogen peroxide, 0.5 part of a mixture of ammonia and potassium hydroxide in any ratio, put the weighed stearic acid into the reactor, heat and stir to 110°C, slowly add zinc oxide , Add hydrogen peroxide to react for 90 minutes, add a mixture of ammonia water and potassium hydroxide in any proportion, cool down after the reaction material is clear and transparent, cool the material after discharging, and crush to obtain powdered transparent zinc stearate after tableting.
[0028] Weigh 25 parts of zinc stearate, 25 parts of hydrotalcite, 10 parts of fumed silica, 6 parts of 6-amino-1,3-dimethyluracil, tris(2-hydroxyethyl) iso 12 parts of cyanurate, 4 parts of glyceryl monostearate, 4 parts of pentaerythritol monostearate, 6 parts of phosphite, 3 parts of antioxidants, 3 parts of external lubricants, 2 parts of β-diketones, Add the weighed zinc stearate, hydrotalcite, and fumed silica ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap