Preparation method of environment-friendly light-color anti-ultraviolet polyester fabric

An anti-ultraviolet and environmentally friendly technology, applied in dyeing method, rayon manufacturing, single-component polyester rayon, etc., can solve the problem that anti-ultraviolet performance needs to be improved, and achieve good anti-ultraviolet performance and anti-ultraviolet effect. , the effect of improving bonding strength

Inactive Publication Date: 2019-05-17
杭州新尚科技咨询有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The fiber has good wearing performance and flame retardant performance, but the effect of anti-ultraviolet performance needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method of an environment-friendly light-colored anti-ultraviolet polyester fabric is carried out according to the following steps:

[0029] A, the raw vermiculite is ground to powder, and the raw vermiculite powder of the micron scale is screened out;

[0030] B. Dry the raw vermiculite powder at 55°C for 14 hours to remove the moisture on the surface of the raw vermiculite powder;

[0031] C. Add the raw vermiculite powder into the polyester chips, heat and stir, and control the process of heating from room temperature to 205°C for 4-8 hours;

[0032] D. Continue heating to 315°C and keep it warm for 30 minutes to obtain molten modified polyester;

[0033] E. The modified polyester chips are spun at high speed on a spinning machine to make nascent fibers. The specific process conditions are: spinning temperature 335°C, spinning speed 1380m / min;

[0034] F, the as-spun fiber is adopted parallel drawing machine to carry out shaping, obtains polyester fibe...

Embodiment 2

[0043] A preparation method of an environment-friendly light-colored anti-ultraviolet polyester fabric is carried out according to the following steps:

[0044] A, the raw vermiculite is ground to powder, and the raw vermiculite powder of the micron scale is screened out;

[0045] B. Dry the raw vermiculite powder at 60°C for 12 hours to remove the moisture on the surface of the raw vermiculite powder;

[0046] C. Add the raw vermiculite powder into the polyester chips, heat and stir, and control the process of heating from room temperature to 210°C for 4 hours;

[0047] D. Continue heating to 310°C and keep it warm for 40 minutes to obtain molten modified polyester;

[0048] E. The modified polyester chips are spun at high speed on a spinning machine to make nascent fibers. The specific process conditions are: spinning temperature 320°C, spinning speed 1450m / min;

[0049] F, the as-spun fiber is adopted parallel drawing machine to carry out shaping, obtains polyester fiber,...

Embodiment 3

[0058] A preparation method of an environment-friendly light-colored anti-ultraviolet polyester fabric is carried out according to the following steps:

[0059] A, the raw vermiculite is ground to powder, and the raw vermiculite powder of the micron scale is screened out;

[0060] B. Dry the raw vermiculite powder at 50°C for 16 hours to remove the moisture on the surface of the raw vermiculite powder;

[0061] C. Add the raw vermiculite powder into the polyester chips, heat and stir, and control the process of heating from room temperature to 200°C for 8 hours;

[0062] D. Continue heating to 320°C and keep it warm for 25 minutes to obtain molten modified polyester;

[0063] E. The modified polyester chips are spun at high speed on a spinning machine to make nascent fibers. The specific process conditions are: spinning temperature 350°C, spinning speed 1300m / min;

[0064] F, the as-spun fiber is adopted parallel drawing machine to carry out shaping, obtains polyester fiber,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of environment-friendly light-color anti-ultraviolet polyester fabric. The method comprises the following steps: grinding raw vermiculite into powder, and screening out micro raw vermiculite powder; heating and drying the raw vermiculite powder; adding the raw vermiculite powder to a polyester chip, and performing heating and stirring; performing heatingcontinuously and keeping the temperature to obtain molten modified polyester; spinning the modified polyester chip on a spinning machine at high speed to prepare nascent fiber; setting the nascent fiber by a parallel drafting machine to obtain polyester fiber; spinning the polyester fiber into polyester fabric with a conventional method; dyeing the polyester fabric to obtain a finished polyesterfabric product. By use of the special performance and structure of vermiculite and the special fiber preparation method, the polyester fabric with good ultraviolet resistance is obtained, and naturalplant fibers are adopted for dyeing in the following dyeing process, and the preparation method is more environmentally friendly than traditional anti-ultraviolet polyester fabric preparation methods.

Description

technical field [0001] The invention relates to the field of functional clothing fabrics, in particular to a preparation method of an environment-friendly light-color anti-ultraviolet polyester fabric. Background technique [0002] As the most widely used chemical fiber, polyester fiber has good fiber-forming and mechanical properties, high strength, good light resistance, heat resistance and acid and alkali resistance, good processability and spinnability, and can be purely spun or blended and interweave. Polyester fabrics are washable, wear-resistant, non-ironing and wrinkle-resistant, and are widely used in clothing, home textiles, decoration and product applications. However, polyester fiber also has disadvantages such as poor hygroscopicity, non-sweat-absorbing fabric, stuffy feeling when worn, poor anti-static ability, and easy to be stained with dust, which greatly restricts the application and development of polyester fiber. In order to improve the wearing comfort ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/10D06P1/34D06P3/52
Inventor 芦美玲
Owner 杭州新尚科技咨询有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap