High-hardness and anti-dazzle hardening layer coating liquid and hardening film

A technology of hardened layer and coating liquid, applied in the direction of coating, etc., can solve the problem that the hardened film cannot have both high hardness and anti-glare properties, and achieve the effects of reducing gloss, satisfying scratches, and reducing specular reflection

Inactive Publication Date: 2019-05-28
NINGBO EXCITON TECH
View PDF5 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that the existing hardened film cannot have both high hardness and anti-glare properties, the present invention provides a high-hardness, anti-glare hardened layer coating solution and a hardened film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-hardness and anti-dazzle hardening layer coating liquid and hardening film
  • High-hardness and anti-dazzle hardening layer coating liquid and hardening film
  • High-hardness and anti-dazzle hardening layer coating liquid and hardening film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] The invention provides a hardened layer coating solution, which comprises 40% acrylate prepolymer, 30% acrylate monomer, 27.8% silicon dioxide, 2% photoinitiator, 0.25% Auxiliary, said percentage content is weight percentage content.

[0077] The preparation method of the hardening solution provided in this embodiment includes:

[0078] 20% ten-functional urethane acrylic resin oligomer, 20% hexa-functional urethane acrylic resin oligomer, 30% hexa-functional acrylate monomer, 27.8% silica particles, 2% photoinitiator, 0.2% leveling agent. Disperse the main resin in an organic solvent to form a hardening solution with a solid content of 50%. Among them, the ten-functional urethane acrylic resin oligomer, the hexa-functional urethane acrylic resin oligomer, and the hexa-functional acrylate monomer are all provided by Meiyuan Special Chemical Co., Ltd., and the photoinitiator is 184, silicon dioxide, which is provided by BASF. It is provided by Fuji Silicon Chemical Co...

Embodiment 2

[0083] The preparation method of the hardening solution provided in this embodiment includes:

[0084] 35% ten-functional urethane acrylic resin oligomer, 18.6% hexa-functional urethane acrylic resin oligomer, 28% hexa-functional acrylate monomer, 15% silica particles, 3% photoinitiator, 0.4% leveling agent. Disperse the main resin in an organic solvent to form a hardening solution with a solid content of 45%. Among them, the ten-functional urethane acrylic resin oligomer, the hexa-functional urethane acrylic resin oligomer, and the hexa-functional acrylate monomer were all provided by Meiyuan, the photoinitiator was 184 provided by BASF, the silica was provided by Fuji Silicon Chemical, and the fluid The leveling agent is provided by BYK, and the organic solvent is ethyl acetate.

[0085] Coatings were applied on 188 μm PET substrates.

[0086] The thickness of the formed hardened layer was 20 μm.

[0087] The performance test results of the prepared cured film are shown ...

Embodiment 3

[0089] The preparation method of the hardening solution provided in this embodiment includes:

[0090] 10% ten-functional urethane acrylic resin oligomer, 40% hexa-functional urethane acrylic resin oligomer, 26.9% hexa-functional acrylate monomer, 20% silica particles, 3% photoinitiator, 0.1% leveling agent. Disperse the main resin in an organic solvent to form a hardening solution with a solid content of 60%. Among them, the ten-functional urethane acrylic resin oligomer, the hexa-functional urethane acrylic resin oligomer, and the hexa-functional acrylate monomer were all provided by Meiyuan, the photoinitiator was 184 provided by BASF, the silica was provided by Fuji Silicon Chemical, and the fluid The leveling agent is provided by BYK, and the organic solvent is ethyl acetate.

[0091] Coatings were applied on 125 μm PET substrates.

[0092] The thickness of the formed hardened layer was 21 μm.

[0093] The performance test results of the prepared cured film are shown ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of a hardening film, in particular to high-hardness and anti-dazzle hardening layer coating liquid and a hardening film. In order to solve the problems that the existing hardening film cannot realize high hardness or anti-dazzle performance at the same time, the invention provides the high-hardness and anti-dazzle hardening layer coating liquid and thehardening film. The hardening layer coating liquid contains 40 to 80 percent of acrylic ester prepolymers, 10 to 30 percent of acrylic ester monomers, 7 to 30 percent of silicon dioxide, 2 to 6 percent of photoinitiators and 0.1 to 0.5 percent of auxiliary agents in percentage by weight. The hardening layer coating liquid provided by the invention forms a hardening layer after the curing; high hardness and anti-dazzle performance are realized. The hardening film provided by the invention has high hardness and anti-dazzle protection effects.

Description

technical field [0001] The invention relates to the technical field of hardened film, in particular to a high-hardness, anti-glare hardened layer coating liquid and a hardened film. Background technique [0002] Among the many properties of LCD optical protective film, anti-glare function has become one of the most important requirements. "Glare" is the impact on vision due to the improper distribution of brightness or contrast in the field of view. The light reflected by the surrounding light source on the screen surface has a certain impact on the brightness and contrast of the image, which is called "glare" phenomenon . In particular, low-brightness displays such as LCDs are more difficult to recognize when operating under high-brightness light. Watching such screens for a long time is very harmful to the naked eye. The methods for realizing the anti-glare function of the screen include: (1) mechanically grinding the surface of the film or selectively corroding it with ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/02C09D7/61C08J7/06C08L67/02
Inventor 唐海江汪诚简伟任缪锴夏寅薛永富张彦李刚
Owner NINGBO EXCITON TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com