A rubber water seal and washing machine technology, applied in the field of rubber processing, can solve the problems of poor sealing and low pressure change, and achieve the effects of promoting tight bonding, improving compatibility, and improving market promotion and application value.

Inactive Publication Date: 2019-06-21
刘辉
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Through the preparation of synthetic rubber, rubber molding, vulcanization and post-treatment processes, a rubber with good wear resistance, low pressure change, high hardness, high strength, good tensile properties, low temperature resistance, water resistance a...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A washing machine rubber water seal material, consisting of the following components by weight:

[0031] 60 parts of natural rubber, 25 parts of methyl vinyl silicone rubber, 23 parts of fluororubber TP, 16 parts of thermoplastic elastomer, 13 parts of modified composite filler, 5 parts of karaya gum, 1 part of sulfur, 3 parts of light calcium; The preparation method of the modified composite filler is as follows: Put the montmorillonite in a microwave oven for microwave activation treatment, take it out after 6 minutes of microwave activation treatment; will step The montmorillonite after the medium microwave treatment was immersed in a hydrochloric acid solution with a mass fraction of 20%, and was continuously stirred for 30 minutes, and then filtered out for later use; will step The filtered montmorillonite was placed in a freezer and frozen at -50°C for 30 minutes; will step The montmorillonite and ceramic micropowder after the intermediate treatment ar...

Embodiment 2

[0051] A washing machine rubber water seal material, consisting of the following components by weight:

[0052] 65 parts of natural rubber, 28 parts of methyl vinyl silicone rubber, 25 parts of fluororubber TP, 18 parts of thermoplastic elastomer, 14 parts of modified composite filler, 6 parts of karaya gum, 1.5 parts of sulfur, 3.5 parts of light calcium; The preparation method of the modified composite filler is as follows: Put the montmorillonite in a microwave oven for microwave activation treatment, take it out after 8 minutes of microwave activation treatment; will step The montmorillonite after the medium microwave treatment was immersed in a hydrochloric acid solution with a mass fraction of 25%, and was continuously stirred for 35 minutes and then filtered out for later use; will step The montmorillonite filtered out of the medium was placed in a freezer and frozen at a temperature of -40°C for 35 minutes; will step The montmorillonite and ceramic micropow...

Embodiment 3

[0072] A washing machine rubber water seal material, consisting of the following components by weight:

[0073] 70 parts of natural rubber, 31 parts of methyl vinyl silicone rubber, 27 parts of fluororubber TP, 20 parts of thermoplastic elastomer, 15 parts of modified composite filler, 7 parts of karaya gum, 2 parts of sulfur, 4 parts of light calcium; The preparation method of the modified composite filler is as follows: Put the montmorillonite in a microwave oven for microwave activation treatment, take it out after 10 minutes of microwave activation treatment; will step The montmorillonite after the medium microwave treatment was immersed in a hydrochloric acid solution with a mass fraction of 30%, and was continuously stirred for 40 minutes and then filtered out for later use; will step The montmorillonite filtered out was placed in a freezer and frozen at -30°C for 40 minutes; will step The montmorillonite and ceramic micropowder after the intermediate treatme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rubber water sealing material of a washing machine. The rubber water sealing material comprises the following components: natural rubber, methyl vinyl silicone rubber, fluororubber TP, a thermoplastic elastomer, a modified composite filler, karaya gum, sulphur and calcium carbonate. According to the prepared rubber water sealing material, the modification is carried out,so that the compatibility of inorganic components and high polymer compounds can be improved, the modified composite filler and the substrate raw material components can be closely combined, as a result, the tensile strength and the elongation at break of the rubber water sealing material can be improved; the permanent compression set value is reduced; the comprehensive performances are extremelyoutstanding; and the rubber water sealing material is high in market popularization and application value.

Description

technical field [0001] The invention belongs to the technical field of rubber processing, and in particular relates to a rubber water sealing material for a washing machine. Background technique [0002] The performance of the washing machine is good or bad. In addition to the materials and structure of the washing machine meeting the requirements of the working medium, the choice of sealing material is also very important. The reasonable choice of sealing material is to ensure its normal and orderly operation and reduce maintenance and repair costs. key. With the development of industrial technology and increasingly complex and diverse requirements, sealing materials have also developed rapidly, with more and more types and continuous improvement in physical and chemical properties; however, the comprehensive performance of existing washing machine sealing materials cannot reach Some production requirements, short service life. [0003] "A Washing Machine Rubber Water Sea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L7/00C08L83/07C08L27/12C08K13/06C08K9/00C08K3/34C08K9/02C08K3/00
Inventor 刘辉
Owner 刘辉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap