A kind of regeneration method of deactivated catalyst

A deactivated catalyst, catalyst technology, applied in the direction of catalyst regeneration/reactivation, chemical instruments and methods, physical/chemical process catalysts, etc.

Active Publication Date: 2021-10-08
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For the deactivated catalyst caused by carbon deposition, its activity can be restored by regeneration, but for the deactivated catalyst caused by metal deposition pollution, it cannot be regenerated to restore its activity, so it can only be discarded.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of regeneration method of deactivated catalyst
  • A kind of regeneration method of deactivated catalyst
  • A kind of regeneration method of deactivated catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Take a deactivated hydrotreating catalyst with a carbon deposition of 6.5%, and its active metal components are Mo and Ni, and perform carbon burning regeneration treatment in an oxygen-containing atmosphere. At a heating rate of 3°C / min, the temperature was raised to 200°C, kept at a constant temperature for 10 hours, and then continued to rise to 330°C, kept at a constant temperature for 8 hours. The obtained sample had a carbon content of 1.5% and a sulfur content of 1.8%. The obtained sample was named C-1.

[0027] Take a deactivated hydrotreating catalyst with a carbon deposition of 8.2%, and its active metal components are Mo, Ni, and Co, and use different conditions to perform carbon regeneration treatment in an oxygen-containing atmosphere. At a heating rate of 3°C / min, the temperature was raised to 200°C, kept at a constant temperature for 10 hours, and then continued to rise to 320°C, kept at a constant temperature for 10 hours. The obtained sample had a carbo...

Embodiment 2

[0029] Take 61g of tetrakis hydroxymethyl phosphorus sulfate aqueous solution (solution concentration is 75wt%), spray catalyst C-1, after aging for 3 hours, treat at 100°C for 3 hours, take 14g of DMDS and 9ml of hydrazine hydrate and spray it, Heat treatment at a low temperature of 100°C for 3 hours. That is, the desired catalyst C-3 is obtained.

Embodiment 3

[0031] Take 55g of tetrahydroxyethylphosphorus sulfate, dilute it with water to form a 70ml solution, spray the catalyst C-2 with the solution, and after aging for 3 hours, heat treat at 80°C for 3 hours, take 12g of carbon disulfide and 9ml of hydrazine hydrate solution and spray , heat treatment at 100°C for 3 hours. That is, the desired catalyst C-4 is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a method for regenerating a deactivated catalyst. The regeneration method includes the following contents: (1) contacting the hydrogenation catalyst to be regenerated with an oxygen-containing gas to carry out charcoal treatment to obtain a catalyst A; (2) combining the catalyst A with an oxygen-containing gas. The organic compound solution is contacted and subjected to heat treatment to obtain catalyst B; (3) organic sulfide and hydrazine hydrate are introduced into catalyst B, and then heat treatment is performed to obtain a regenerated catalyst. The regeneration method can improve the activity of the regenerated catalyst.

Description

technical field [0001] The invention relates to a catalyst treatment method, in particular to a regeneration method of a deactivated catalyst. Background technique [0002] Hydroprocessing is a very important process for converting crude oil into high-value products, and its core is a hydroprocessing catalyst. The activity of the catalyst is provided by the sulfide state of the metal. The activity of the catalyst will gradually decrease during use, that is, the catalyst is deactivated. In summary, the reasons are generally divided into coking deactivation (causing catalyst pore blockage), poisoning deactivation (causing catalyst acid center poisoning) and sintering deactivation (causing catalyst crystal phase changes), etc. The main reasons for the deactivation of industrial hydrogenation catalysts are coke formation and metal blockage, migration or aggregation of active metal components, changes in phase composition, reduction in the number of active centers, sintering of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J38/02B01J38/10B01J38/12B01J38/52B01J38/66C10G45/04
Inventor 徐黎明高玉兰葛海龙孟兆会佟佳
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com