A kind of composite filter material and its preparation method and performance testing method

A composite filter material and performance technology, used in separation methods, chemical instruments and methods, filtration and separation, etc., can solve the problems of large particle size, difficult and high-efficiency filtration, etc., to enhance adsorption performance, reduce piezoresistance, and increase fiber spacing. Effect

Active Publication Date: 2021-08-03
UNIV OF SCI & TECH BEIJING
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Filter materials such as glass fiber, quartz fiber, cellulose fiber and electret fiber, which are commonly used for particulate matter filtration, cannot absorb and remove gases because they do not contain micropores (<2nm) or mesopores (2-50nm); Adsorbents such as activated carbon, molecular sieve, alumina, and mesoporous materials are difficult to efficiently filter particulate matter due to their large particle size and spherical columnar shape

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of composite filter material and its preparation method and performance testing method
  • A kind of composite filter material and its preparation method and performance testing method
  • A kind of composite filter material and its preparation method and performance testing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0138] refer to figure 1 , the present embodiment proposes that the preparation process of the composite filter material containing nanofibers is:

[0139] Fix the load base on the rollers and start the rollers;

[0140] Fill the dimethylformamide solution of polyacrylonitrile into the electrospinning solution cavity, spray it to the roller, and generate nanofibers on the loading base;

[0141] Put the adsorbent solution into the electrospray solution chamber, spray to the roller, and load the adsorbent on the load base until the adsorbent solution is sprayed completely;

[0142] Stop the roller, let it dry, and curve the fiber cloth on the roller to finally obtain the composite filter material containing nanofibers.

[0143] The rotating speed of the roller is 10r / min.

[0144] The mass fraction of polyacrylonitrile in the dimethylformamide solution of polyacrylonitrile is 10%.

[0145] The adsorbent solution is obtained by dissolving the adsorbent in an isopropanol solut...

Embodiment 2

[0168] The preparation method of the composite filter material without nanofibers of the present embodiment is basically the same as that of Example 1, the only difference is:

[0169] The adsorbent used is ZSM-5 molecular sieve.

[0170] Spray 40mg and 10mg of ZSM-5 powdered molecular sieves onto the fiber substrate, respectively, to prepare adsorbents with loading masses per unit area of ​​0.80 and 0.20mg / cm 2 The loading ratios of samples No. 1 and No. 2 are 85% and 75%, respectively.

[0171] According to the performance test method of a composite filter material described in Example 1, the performance tests were performed on sample No. 1 and sample No. 2 respectively.

[0172] The test conditions are:

[0173] The gas to be measured is ozone, and the ozone concentration is 600ppb.

[0174] Experimental results such as Figure 9 The comparison chart of the ozone removal efficiency of the two composite filter materials with different adsorbent loading mass is shown, fro...

Embodiment 3

[0176] According to the performance testing method of a kind of composite filter material of implementation case 1, the loading mass per unit area of ​​the adsorbent containing and not containing nanofibers is 0.40 mg / cm 2 (80% load rate,) performance test of the composite filter material, the test conditions are:

[0177] The particle size range of the particle to be measured is 0-300nm.

[0178] Experimental results such as Figure 10 The ozone removal efficiency comparison chart of the two composite filter materials with and without nanofibers is shown. From this figure, it can be obtained that the particulate matter efficiency curve of the composite filter material with nanofibers is above the efficiency curve of the composite filter material without nanofibers , indicating that nanofibers contribute to the removal of particulate matter.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of composite filter material materials, and in particular relates to a composite filter material and a preparation method and performance testing method thereof. The chemical bed method is used to disperse, and the polymer is sprayed by electrospinning to form nanofibers, and a series of methods are carried out on a coarsely supported substrate. The test method of the composite filter material is that the ozone generation unit and the particle generation unit generate ozone and nano-particles, respectively, and flow through the filter paper holder with composite filter material and the filter paper holder without composite filter material under the impetus of airflow. The particle size and concentration of the particulate matter are detected to obtain the efficiency curve of the composite filter material for removing ozone and particulate matter, and then the adsorption performance of the composite filter material is obtained.

Description

technical field [0001] The invention belongs to the field of composite filter materials, in particular to a composite filter material and its preparation method and performance testing method, including the preparation methods of various composite filter materials, and a performance test method for synchronous removal of gas and particulate matter is designed to determine its performance to test. Background technique [0002] At present, the air passenger flow is increasing year by year, and the environmental quality in the cabin is receiving more and more attention. The main pollutants in the cabin are particulate matter, microorganisms and ozone. Ozone-induced surface and gas reactions can lead to secondary emissions of particulate matter and volatile organic compounds (VOCs), which can be more harmful than ozone itself. Therefore, it is necessary to remove PM and ozone in the environment. [0003] Generally, the removal of nanoparticles in the cabin mainly depends on t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D39/14B01D46/00B01D46/54G01N15/08
CPCB01D39/14B01D46/0036B01D46/546B01D2239/025B01D2239/0407B01D2239/10G01N15/08G01N2015/084G01N2015/0866
Inventor 李子宜金成赞包丹琪裴有康刘应书
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com