A kind of alloy material for bearing rolling body and preparation method thereof

A technology of alloy materials and rolling elements, which is applied in metal processing equipment, transportation and packaging, etc., can solve the problems of radial size, large vibration and noise, and high price, and achieve the effect of improving strength, enhancing hardness, and increasing hardness

Active Publication Date: 2020-08-28
NINGBO DAER MACHINERY TECH CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the rolling bearing has been standardized and serialized, but compared with the sliding bearing, its radial size, vibration and noise are larger, and the price is also higher.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of alloy material for bearing rolling body and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] A method for preparing an alloy material for a bearing rolling body, comprising the following steps:

[0040] Step S1. Mix the metal powders of the base material, add a lubricant, and place them in a cleaned ball mill tank (made of stainless steel). The ball mill tank is evacuated and filled with argon inert gas to prevent the powder from grinding during the ball milling process. Adhesive oxidation, ball milling the mixed powder, ball milling at 250r / min for 2 hours, the ball milling medium is alumina balls, the ball diameters are 10mm, 6mm and 3mm, and the ball-to-material ratio is 10:1;

[0041] Step S2, after the above-mentioned mixed powder is cooled to room temperature, add modified graphene oxide, and continue ball milling at 250r / min for 2h under the protection of argon (divided into two steps of ball milling, which can prevent graphene from being easily wrapped in the composite material) The surface of the metal particles makes it difficult for the metal particl...

Embodiment 1

[0048] An alloy material for a bearing rolling body, made of the following raw materials in parts by weight: 80 parts of base material, 9 parts of lubricant, and 6 parts of modified graphene oxide;

[0049] The alloy material is made by the following steps:

[0050] Step S1. Mix the metal powders of the base material, add lubricant, and place them in a cleaned ball mill tank. The ball mill tank is evacuated and filled with argon inert gas to prevent the powder from bonding and oxidation during the ball milling process. The mixed powder is ball milled for 2 hours at 250r / min, the ball milling medium is alumina balls, the ball diameters are 10mm, 6mm and 3mm, and the ball-to-material ratio is 10:1;

[0051] Step S2, after the above-mentioned mixed powder is cooled to room temperature, then add modified graphene oxide, and continue ball milling at 250r / min for 2h under the protection of argon;

[0052] Step S3, the mixed powder after ball milling is sintered under the sintering ...

Embodiment 2

[0055] An alloy material for a bearing rolling body, made of the following raw materials in parts by weight: 90 parts of a base material, 10 parts of a lubricant, and 6.5 parts of modified graphene oxide;

[0056] The alloy material is made by the following steps:

[0057] Step S1. Mix the metal powders of the base material, add lubricant, and place them in a cleaned ball mill tank. The ball mill tank is evacuated and filled with argon inert gas to prevent the powder from bonding and oxidation during the ball milling process. The mixed powder is ball milled for 2 hours at 250r / min, the ball milling medium is alumina balls, the ball diameters are 10mm, 6mm and 3mm, and the ball-to-material ratio is 10:1;

[0058] Step S2, after the above-mentioned mixed powder is cooled to room temperature, then add modified graphene oxide, and continue ball milling at 250r / min for 2h under the protection of argon;

[0059] Step S3, the mixed powder after ball milling is sintered under the sin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses an alloy material for a bearing rolling body, which is made of the following raw materials in parts by weight: 80-100 parts of base material, 9-11 parts of lubricant, 6-7 parts of modified graphene oxide, and the base material includes Ti powder, Al powder, Cr powder, Nb powder, Al 2 o 3 powder; the invention also discloses the preparation method of the alloy material, including two steps of ball milling and plasma sintering. The present invention adopts Ti powder, Al powder, Cr powder, Nb powder, Al 2 o 3 The powder is used as the matrix material of the alloy, and lubricant and modified graphene oxide are added, and the alloy material is prepared by two-step ball milling method and plasma sintering method. The addition of stretched lamellar graphene oxide can improve the hardness and strength of the alloy material And other mechanical properties, the synergistic effect of the lubricant and the graphene lubricating film can improve the self-lubricating effect of the alloy material, and the alloy material can be made into a bearing rolling body with excellent comprehensive performance.

Description

technical field [0001] The invention belongs to the technical field of bearing rolling body preparation, and in particular relates to an alloy material for a bearing rolling body and a preparation method thereof. Background technique [0002] Bearing is an important part of contemporary mechanical equipment. Its main function is to support the mechanical rotating body, reduce the friction coefficient during its movement, and ensure its rotation accuracy. According to the different friction properties of moving elements, bearings can be divided into two categories: rolling bearings and sliding bearings. Among them, the rolling bearing has been standardized and serialized, but compared with the sliding bearing, its radial dimension, vibration and noise are larger, and the price is also higher. Rolling bearings are generally composed of four parts: outer ring, inner ring, rolling body and cage. As a part of the bearing structure, the rolling body plays a very significant role...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/05C22C14/00C22C1/10B22F1/00B22F3/105B22F9/04
CPCC22C1/05C22C14/00B22F9/04B22F3/105B22F2009/043B22F1/10
Inventor 刘正龙
Owner NINGBO DAER MACHINERY TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com