Medical cermet material and preparation method thereof

A cermet and metal matrix technology, which is applied in the field of medical cermet materials and its preparation, can solve the problem of uneven distribution of metal and ceramic phases in wear-resistant composite materials, insufficient mixing of metal and ceramic particles, and wear-resistant composite materials. Poor abrasiveness and other problems to achieve the effect of low processing efficiency, good contact and high compressive strength

Inactive Publication Date: 2019-08-20
CHANGSHA QIUDIANBING INFORMATION TECH CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Cermet is a composite material made of metal and ceramics as raw materials. It has the advantages of both metals and ceramics, overcomes the brittleness of ceramics and makes up for the shortcomings of metals in terms of high strength, high hardness, high temperature resistance, and wear resistance. , has received widespread attention and research, and is widely used. However, some existing cermet materials, especially in medicine, cannot fully mix

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Medical cermet material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1, a medical metal ceramic material and a preparation method thereof, comprising the following components in parts by mass: 58 parts of metal matrix, 22 parts of ceramic particles, 4 parts of kaolin, and 1 part of binder.

[0029] ingredient Metal matrix Ceramic particles Kaolin Binding agent Proportion / part 582241

[0030] A method for preparing medical cermet materials includes the following steps:

[0031] S1: Weigh the raw materials of each component as required and conduct mixing treatment;

[0032] S2, turn on the ball mill, perform dry ball milling on the metal substrate, and ball mill to obtain small materials;

[0033] S3: After mixing the ceramic particles, the binder and the small materials uniformly, the material is trapped at 30°C, and the trapping time is 16 hours. After the trapping is completed, the mixture is evenly mixed to obtain pellets;

[0034] S4: Put the pellets into the mold and put into the drying furnace to obtain a dry compact;

[0035] S5: ...

Example Embodiment

[0045] Example 2, a medical cermet material and a preparation method thereof, comprising the following components in parts by mass: 60 parts of metal matrix, 24 parts of ceramic particles, 6 parts of kaolin, and 2 parts of binder.

[0046] ingredient Metal matrix Ceramic particles Kaolin Binding agent Proportion / part 602462

[0047] S1, weigh the raw materials of each component as required and perform mixing treatment;

[0048] S2, turn on the ball mill, perform dry ball milling on the metal substrate, and ball mill to obtain small materials;

[0049] S3: After mixing the ceramic particles, the binder and the small materials uniformly, the material is trapped at 38°C, and the trapping time is 28 hours. After the trapping is completed, the mixture is evenly mixed to obtain pellets;

[0050] S4: Put the pellets into the mold and put into the drying furnace to obtain a dry compact;

[0051] S5: Put the dry billet in step S3 into the hot pressing furnace, increase the temperature in the...

Example Embodiment

[0061] Example 3, a medical metal ceramic material and a preparation method thereof, includes the following components in parts by mass: 63 parts of metal matrix, 26 parts of ceramic particles, 8 parts of kaolin, and 3 parts of binder.

[0062] ingredient Metal matrix Ceramic particles Kaolin Binding agent Proportion / part 632683

[0063] A method for preparing medical cermet materials includes the following steps:

[0064] S1, weigh the raw materials of each component as required and perform mixing treatment;

[0065] S2, turn on the ball mill, perform dry ball milling on the metal substrate, and ball mill to obtain small materials;

[0066] S3: After mixing the ceramic particles, the binder and the small materials uniformly, the material is trapped at 42° C. The trapping time is 48 hours. After the trapping is completed, the mixture is evenly mixed to obtain the pellets;

[0067] S4: Put the pellets into the mold and put into the drying furnace to obtain a dry compact;

[0068] S5. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a medical cermet material. The medical cermet material comprises following components by weight part: metal matrixes of 58-64 parts, ceramic particles of 22-26 parts, kaolin of4-8 parts and binding agents of 1-3 parts. The medical cermet material has the beneficial effects that a ball mill is used to break up metal into small material before processing by arranging the ball mill, metal particles and ceramic particles are enabled to contact well and distribute evenly by adopting a mode of decreasing the particle diameter of the metal matrixes, and therefore the preparedmedical cermet material is enabled to have performance of high pressure strength and high breaking strength, and secondly, the preparation process of the cermet material is clear, specific operationof all steps is detailed, the flow path of the preparation process is clear, the problem that low processing efficiency is caused by undefined description of a traditional processing method is solved,and processing equipment used for preparing the medical cermet material are simple, convenient to use, and capable of greatly reducing production cost.

Description

technical field [0001] The invention discloses a medical cermet material and a preparation method thereof, belonging to the technical field of composite materials. Background technique [0002] Cermet is a composite material made of metal and ceramics as raw materials. It has the advantages of both metals and ceramics, overcomes the brittleness of ceramics and makes up for the shortcomings of metals in terms of high strength, high hardness, high temperature resistance, and wear resistance. , has received widespread attention and research, and is widely used. However, some existing cermet materials, especially in medicine, cannot fully mix the metal and ceramic particles during sintering, resulting in wear-resistant composite materials. The uneven distribution of the ceramic phase leads to poor wear resistance of the composite material, and it is easy to reduce the fracture degree of the appliance when the medical appliance is manufactured in the later stage. Therefore, how t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F1/00B22F9/04B22F3/14
CPCB22F9/04B22F3/14B22F2009/043B22F1/10
Inventor 不公告发明人
Owner CHANGSHA QIUDIANBING INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap